Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ceramic comb

A technology for special ceramics and combs, applied in hair combs, clothing, hairdressing equipment, etc., can solve the problems of short service life of combs, easy mildew and deterioration of wood, easy to break combs, etc., to reduce the production process, reduce difficulty, and smooth combing. Effect

Inactive Publication Date: 2014-01-01
陈锐群
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wood comb is light and easy to carry, but the wood is easy to mildew and deteriorate, the service life is short, and it is not easy to clean, and now it is called for the protection of forest resources. The value of each tree is far greater than the value of its felled wood, so a new material was developed Making combs is very in line with the requirements of the times
[0004] 201210506755.X discloses a ceramic comb, which is composed of a comb body and teeth, and is formed at one time by a high-temperature firing method. However, the ceramics used in this patent are general brittle ceramics, and there is no modification of the ceramics. Due to the Brittle, the comb is easy to break during use, and the service life of the comb is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The comb body and teeth of a ceramic comb are made of special ceramic materials, and consist of the following components by weight:

[0017] 3 parts of barium carbonate, 0.01 part of copper oxide, 0.005 part of cobalt oxide, 5 parts of zinc oxide, 1 part of boric acid, 20 parts of calcite, 5 parts of kaolin, 3 parts of alumina, 35 parts of quartz, 3 parts of potassium nitrate, 3 parts of soda ash, 0.5 parts of antimony trioxide.

[0018] A kind of preparation method of ceramic comb comprises the steps:

[0019] Weigh 3 parts of barium carbonate, 0.01 part of copper oxide, 0.005 part of cobalt oxide, 5 parts of zinc oxide, 1 part of boric acid, 20 parts of calcite, 5 parts of kaolin, 3 parts of alumina, 35 parts of quartz, 3 parts of potassium nitrate, 3 parts of soda ash 1 part, 0.5 part of antimony trioxide, mixed and stirred evenly, melted at a high temperature of 1500 ° C for 2 hours, molded the molten liquid with a mold, and dried to obtain a ceramic comb.

Embodiment 2

[0021] The comb body and teeth of a ceramic comb are made of special ceramic materials, and consist of the following components by weight:

[0022] 8 parts of barium carbonate, 0.03 parts of copper oxide, 0.01 part of cobalt oxide, 10 parts of zinc oxide, 5 parts of boric acid, 35 parts of calcite, 10 parts of kaolin, 8 parts of alumina, 55 parts of quartz, 8 parts of potassium nitrate, 8 parts of soda ash, 2.0 parts of antimony trioxide.

[0023] A kind of preparation method of ceramic comb comprises the steps:

[0024] Weigh 8 parts of barium carbonate, 0.03 parts of copper oxide, 0.01 part of cobalt oxide, 10 parts of zinc oxide, 5 parts of boric acid, 35 parts of calcite, 10 parts of kaolin, 8 parts of alumina, 55 parts of quartz, 8 parts of potassium nitrate, and 8 parts of soda ash 2.0 parts of antimony trioxide, mixed and stirred evenly, melted at a high temperature of 1510 °C for 2 hours, molded the molten liquid with a mold, and dried to obtain a ceramic comb.

Embodiment 3

[0026] The comb body and teeth of a ceramic comb are made of special ceramic materials, and consist of the following components by weight:

[0027] 5 parts of barium carbonate, 0.02 parts of copper oxide, 0.007 parts of cobalt oxide, 8 parts of zinc oxide, 3 parts of boric acid, 30 parts of calcite, 8 parts of kaolin, 5 parts of alumina, 45 parts of quartz, 5 parts of potassium nitrate, 5 parts of soda ash, 1.0 parts of antimony trioxide.

[0028] A kind of preparation method of ceramic comb comprises the steps:

[0029] Weigh 5 parts of barium carbonate, 0.02 parts of copper oxide, 0.007 parts of cobalt oxide, 8 parts of zinc oxide, 3 parts of boric acid, 30 parts of calcite, 8 parts of kaolin, 5 parts of alumina, 45 parts of quartz, 5 parts of potassium nitrate, and 5 parts of soda ash 1.0 part of antimony trioxide, mixed and stirred evenly, melted at a high temperature of 1520°C for 2 hours, molded the molten liquid with a mold, and dried to obtain a ceramic comb.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ceramic comb and belongs to the technical field of ceramic production. The comb comprises a comb body and comb teeth, which are integrated, wherein the comb body and the comb teeth are both made of ceramics and integrally formed with a high-temperature firing method. The ceramic comb has the advantages of high strength, smoothness for combing and high possibility of cleaning; meanwhile, a one-step forming method is adopted, so that the manufacturing process is simplified, the difficulty is lowered, the rejection rate is reduced, and the cost is saved.

Description

technical field [0001] The invention relates to a ceramic comb, which belongs to the technical field of ceramic production. Background technique [0002] Comb, also known as comb, also known as comb in ancient times, is a tool for tidying hair. It is usually flat in shape and has many teeth. Some combs have handles and some do not. Now there are many kinds of combs, such as: mahogany combs, sandalwood combs, horn combs, etc. There are more than 300 varieties of combs in five series, including practical combs, craft combs, travel combs, high-end boutique combs, and health care combs. [0003] An important indicator for judging the performance of a comb is that its combing flow is not smooth. At present, there are many ox horn combs and sheep horn combs for sale on the market. These combs are under the banner of being smooth and rare. Small, there are not so many cows and sheep at all, let alone use the horns of cows and sheep to make combs. In addition, another most t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/653A45D24/02
Inventor 陈锐群
Owner 陈锐群
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com