A kind of high-strength, high-toughness glass fiber reinforced PA/ABS composite material and preparation method thereof

A technology of composite materials and high toughness, applied in the field of composite materials, can solve the problems of reduced strength, tensile strength and bending performance, and achieve the effects of improving fluidity, improving slipperiness and good dispersion

Inactive Publication Date: 2015-12-09
SHANGHAI SUNNY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Patent Document Publication No. CN102051046A discloses a PA / ABS composite material and its preparation method, which can greatly improve the toughness of the material, but its strength, especially the tensile strength and bending properties, are reduced
[0003] Regarding the high-strength, high-toughness glass fiber reinforced PA / ABS composite material of the present invention, there is no report yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength, high-toughness glass fiber reinforced PA/ABS composite material and preparation method thereof
  • A kind of high-strength, high-toughness glass fiber reinforced PA/ABS composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～ Embodiment 4

[0023] Embodiment 1~Example 4 and Comparative Example 1~Comparative Example 4

[0024] The polyamide is PA6, the glass fiber is alkali-free glass fiber whose surface has been treated with silane coupling agent, the antioxidant is hindered phenolic antioxidant, the lubricating and dispersing agent is silicone, and the compatibilizer is maleic anhydride, methyl Glycidyl acrylate bifunctional co-grafted polyolefin elastomer. Each raw material was weighed according to the weight percentage shown in Table 1.

[0025] The weight percent (wt%) of each raw material in the table 1 embodiment 1~embodiment 4 and comparative example 1~comparative example 4

[0026]

[0027] Except for the glass fiber, put other raw materials into a high-efficiency mixer and mix for 5 minutes, and then discharge; the obtained premix is ​​extruded and granulated by a twin-screw extruder, and the glass fiber is fed sideways during the extrusion process. The feed port is added, the processing temperatur...

Embodiment 5

[0033] The glass fiber is alkali-free glass fiber whose surface has been treated with silane coupling agent, the antioxidant is hindered phenolic antioxidant, the lubricating and dispersing agent is silicone, the compatibilizer is maleic anhydride, glycidyl methacrylate bis Functional group co-grafted polyolefin elastomer. Take each raw material according to the following weight percentages:

[0034] Polyamide 62.5%, ABS 22%, compatibilizer 5%, glass fiber 10%, antioxidant 0.2%, lubricating dispersant 0.3%.

[0035] Except for glass fiber, put other raw materials into a high-efficiency mixer and mix for 4 minutes, and then discharge; the obtained premix is ​​extruded and granulated by a twin-screw extruder, and the glass fiber is fed sideways during the extrusion process. The feed port is added, the processing temperature is 210-235°C, divided into nine sections, one section is 210°C, the second section is 215°C, the third section is 220°C, the fourth section is 225°C, the fi...

Embodiment 6

[0037] The polyamide is PA6, the glass fiber is alkali-free glass fiber whose surface has been treated with silane coupling agent, the antioxidant is hindered phenolic antioxidant, the lubricating and dispersing agent is silicone, and the compatibilizer is maleic anhydride, methyl Glycidyl acrylate bifunctional co-grafted polyolefin elastomer. Take each raw material according to the following weight percentages:

[0038] Polyamide 39.5%, ABS 22%, compatibilizer 8%, glass fiber 30%, antioxidant 0.3%, lubricating dispersant 0.2%.

[0039] Except for the glass fiber, put other raw materials into the high-efficiency mixer and mix for 3 minutes, and then discharge; the obtained premix is ​​extruded and granulated by a twin-screw extruder, and the glass fiber is fed sideways during the extrusion process. The feed port is added, the processing temperature is 210-235°C, divided into nine sections, one section is 210°C, the second section is 215°C, the third section is 220°C, the four...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength, high-toughness glass fiber reinforced PA / ABS composite material. The composite material is prepared from the following raw material components in weight percent: polyamide 10%-65%, ABS? 10%~50%, compatibilizer 5%~15%, glass fiber 10%~40%, antioxidant 0.1%~1%, lubricating dispersant 0.1%~1%. The invention also discloses a preparation method of the glass fiber reinforced PA / ABS composite material with high strength and high toughness. The glass fiber reinforced PA / ABS composite material of the present invention has the advantages of high strength, high toughness, stable quality, and excellent comprehensive mechanical properties, and can be widely used in products in the fields of automotive interior and exterior parts, electronic appliances, and the like.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a high-strength, high-toughness glass fiber reinforced PA / ABS composite material and a preparation method thereof. Background technique [0002] Polyamide (referred to as PA), commonly known as nylon, has been widely used in automobiles, electronics, machinery and other fields because of its good strength, wear resistance, oil resistance and wide temperature range. However, with the rapid development of the electronics, electrical and automotive industries in recent years, the demand for high-strength, high-toughness engineering plastics is increasing. The commonly used polyamide engineering plastics have high water absorption, poor dimensional stability, low temperature and dry impact strength. The low disadvantages gradually fail to meet the performance requirements of many automotive and electrical parts. The blending modification of polyamide with acrylonitrile-b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08L55/02C08L51/06C08L83/04C08K13/04C08K7/14B29C47/92B29C48/92
CPCB29B7/90B29B9/14B29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 金幸杨涛孟成铭郭建鹏
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap