Non-oriented electrical steel plate with high magnetic induction and low iron loss, and manufacturing method thereof

A technology for an oriented electrical steel sheet and a manufacturing method, which is applied to the non-oriented electrical steel sheet with high magnetic induction and low iron loss and its manufacturing field, can solve the problems that the capacity of the cold rolling mill cannot meet the design requirements, the production cost is increased, etc., and the surface condition is good. , low cost, high magnetic induction effect

Inactive Publication Date: 2013-11-13
BAOSHAN IRON & STEEL CO LTD
View PDF7 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The same disadvantage is that the addition of Sn and Cu will cause a substantial increase in production costs, and high-temperature coiling, high-temperature final rolling and other means are required for assistance, special slab heating and rolling equipment are required, and the content of impurity elements such as S and N The control is very strict, all requirements are less than 0.0015%
[0009] The paper written by Hunady and Cernik reports that the silicon equivalent in the steel is strictly controlled to improve the phase transformation effect of the hot rolling and finishing rolling process, and then the favorable texture of the finished steel plate is controlled by the method of cold rolling and large reduction, and the reduction rate is as high as 91. %, the capacity of ordinary cold rolling mills is far from meeting the design requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-oriented electrical steel plate with high magnetic induction and low iron loss, and manufacturing method thereof
  • Non-oriented electrical steel plate with high magnetic induction and low iron loss, and manufacturing method thereof
  • Non-oriented electrical steel plate with high magnetic induction and low iron loss, and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The technical solution of the present invention will be further described in detail below in conjunction with specific embodiments.

[0046] Embodiments of the manufacture of high magnetic induction and low iron loss non-oriented electrical steel sheets of the present invention are as follows:

[0047] Molten iron and steel scrap are smelted in a 300-ton converter according to the chemical composition ratio shown in Table 1, and slag stoppers and moving slides are used to stop slag. Then, RH refining is used for decarburization, deoxidation, and alloying. After RH refining and decarburization, complete deoxidation is performed, and the Si, Mn, and Al contents in the steel are adjusted. After the molten steel is continuously cast, a billet with a thickness of 170 mm to 250 mm and a width of 800 mm to 1400 mm is obtained. After the above smelting process, the cast slabs are subjected to hot rolling, pickling, cold rolling and annealing processes in sequence. During hot r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a non-oriented electrical steel plate with high magnetic induction and low iron loss, and a manufacturing method thereof, wherein the weight percentage of the chemical components of the steel plate is as follows: less than or equal to 0.004 % of C, 0.1-1.6% of Si, 0.02-1.0% of Mn, less than or equal to 0.003% of S, 0.1-0.6% of Al, less than or equal to 0.003% of N and less than or equal to 0.0015% of Ti, wherein Si+Al is between 0.2-2.0%, and Mn, Si and Al satisfies the following formula: Mn=K2*Si+K3*Al+a, k2=0.08-0.11, k3=0.17-0.38; a is a constant and the balance is Fe and unavoidable impurities. The non-oriented electrical steel plate with high magnetic induction and low iron loss has 1.70-1.78T of magnetic induction B50 and 3.59-5.5W / kg of iron loss P15 / 50, has good surface state and is relatively low in manufacture cost without intermediate normalizing or batch annealing, has high magnetic induction, low iron loss and no corrugated defect, and has a magnetic induction B50 0.02T higher and an iron loss P15 / 50 0.2W / kg lower than those of a normal non-oriented electrical steel plate with same license number.

Description

technical field [0001] The present invention relates to a non-oriented electrical steel sheet and a manufacturing method thereof, in particular to a non-oriented electrical steel sheet with good surface condition, low cost, high magnetic induction and low iron loss without normalization or intermediate annealing in a bell-type furnace, and a manufacturing method thereof. The magnetic induction B50 of the non-oriented electrical steel sheet is 0.02T higher than that of the conventional non-oriented electrical steel sheet of the same brand, and the iron loss P15 / 50 is 0.2W / kg lower. Background technique [0002] In recent years, high-efficiency EI iron cores, motors, small transformers and other electrical equipment have become more and more popular. One of the very important reasons is that it can meet the needs of environmental protection, energy saving and effective reduction of carbon dioxide emissions. At the same time, with the continuous improvement of the comprehensiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C21D8/12
Inventor 金冰忠张峰王波陈晓徐琪刘海王子涛
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products