Shell fabric manufacturing technology for improving stripping strength of high-denier gluing shell fabric

A technology for peeling strength and laminating fabrics, which is applied in the field of fabric manufacturing technology, can solve the problems of reducing the hand feeling and waterproof and moisture-permeable effect, changing the style and appearance of fabrics, and insufficient flatness of the fabric surface, so as to ensure the hand-feel, waterproof and moisture-permeable, Improve the peel strength and save the effect of calendering process

Active Publication Date: 2013-10-23
TRYD TEXTILE FIBER TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-denier laminated fabrics have been unable to achieve good lamination fastness in transfer lamination. Because the fibers of the fabric are relatively thick and the surface of the fabric is not flat enough, if glue is applied directly, the fastness after lamination will not be good. , so it is generally necessary to carry out calendering treatment before this, so that the fabric can be flattened before continuing to fit. After calendering treatment, the style and appearance of the fabric may be changed
In addition, in order to improve the fastness of high-denier laminated fabrics, it is necessary to increase the amount of glue applied, which improves the fastness of laminated fabrics, but reduces the hand feeling and waterproof and moisture-permeable effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shell fabric manufacturing technology for improving stripping strength of high-denier gluing shell fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A fabric manufacturing process for improving the peel strength of high-denier laminated fabrics, the high-denier fabric is a fabric above 300D, and the fabric manufacturing process includes:

[0024] A. Glue compounding, the top glue raw materials and bottom glue raw materials are mixed and configured into top glue and bottom glue respectively, wherein the ratio of each component of the bottom glue includes: 100 parts by weight of polyurethane resin, 20 parts by weight of bottom glue solvent, 1 part by weight of Bridging agent, 5 parts by weight of one-component moisture-reactive adhesive, the appearance is a transparent mist viscous body, the solid content is 70-80%; the primer solvent is toluene, dimethylformamide, butanone One of them, the bridging agent is selected from isocyanate. The configuration process of the primer is as follows:

[0025] 1). Add the primer solvent into the empty bucket, and turn on the agitator to control the speed at 400rpm;

[0026] 2). ...

Embodiment 2

[0034] A fabric manufacturing process for improving the peel strength of high-denier laminated fabrics, the high-denier fabric is a fabric above 300D, and the fabric manufacturing process includes:

[0035] A. Glue compounding, the top glue raw materials and bottom glue raw materials are mixed and configured into top glue and bottom glue respectively, wherein the ratio of each component of the bottom glue includes: 100 parts by weight of polyurethane resin, 60 parts by weight of bottom glue solvent, 7 parts by weight of Bridging agent, 15 parts by weight of one-component moisture-reactive adhesive, 3 parts by weight of bridging accelerator, the appearance is a transparent mist viscous body, and the solid content is 70-80%; the primer solvent is toluene, Any two of methyl formamide and methyl ethyl ketone, and the bridging agent is selected from isocyanate. The configuration process of the primer is as follows:

[0036] 1). Add the primer solvent into the empty bucket, and tu...

Embodiment 3

[0045] A fabric manufacturing process for improving the peel strength of high-denier laminated fabrics, the high-denier fabric is a fabric above 300D, and the fabric manufacturing process includes:

[0046] A. Glue compounding, the top glue raw materials and bottom glue raw materials are mixed and configured into top glue and bottom glue respectively, wherein the ratio of each component of the bottom glue includes: 100 parts by weight of polyurethane resin, 40 parts by weight of bottom glue solvent, 5 parts by weight of Bridging agent, 10 parts by weight of one-component moisture-reactive adhesive, 2 parts by weight of bridging accelerator, the appearance is a transparent micro-mist viscous body, and the solid content is 70-80%; the primer solvent is toluene, two The three of methyl formamide and methyl ethyl ketone are mixed, the ratio of each component is 5:10:5 by weight, and the bridging agent is selected from isocyanate. The configuration process of the primer is as foll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a shell fabric manufacturing technology for improving stripping strength of a high-denier gluing shell fabric. The manufacturing technology comprises the following steps of: A, preparing glue, wherein a mono-component moist reaction type adhesion agent is added to a primer; B, coating surface glue on release paper and drying in a step baking oven at 90 / 100 / 110 / 120 DEG C to form a surface glue layer, wherein the total thickness of the surface glue layer together with the release paper is 0.25mm-0.3 mm after drying; C, coating the primer on the surface of the surface glue layer and semi-drying, wherein the total thickness of the primer, the surface glue layer and the release paper is 0.3mm-0.35 mm after semi-drying; D, unreeling a shell fabric layer and the release paper at the same speed, and gluing the shell fabric layer and the primer at the pressure of 4-6 kg / cm<2> to form a semi-finished product which is then reeled; and E, stripping the release paper after the semi-finished product is mature. According to the manufacturing technology, the stripping strength of the high-denier gluing shell fabric can be improved, good handfeel and good waterproof and moisture permeable effects can be ensured, a calendering process is omitted, and the style and appearance of the shell fabric are ensured.

Description

technical field [0001] The invention relates to a fabric manufacturing process, in particular to a fabric manufacturing process for improving the peeling strength of high denier laminated fabrics. Background technique [0002] High-denier laminated fabrics have been unable to achieve good lamination fastness in transfer lamination. Because the fibers of the fabric are relatively thick and the surface of the fabric is not flat enough, if glue is applied directly, the fastness after lamination will not be good. , so it is generally necessary to carry out calendering treatment before this, so that the fabric can be flattened before continuing to fit. After calendering treatment, the style and appearance of the fabric may be changed. In addition, in order to improve the fastness of high-denier laminated fabrics, it is necessary to increase the amount of glue applied. Although this improves the fastness of the laminated fabrics, it reduces the hand feeling and waterproof and mois...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/02B32B37/12B32B37/26B32B38/16
Inventor 李肇魁李健徐广刘介正陈雅
Owner TRYD TEXTILE FIBER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com