Method for preparing spheroidal high-sulfur-capacity magnetic iron oxide desulfurizing agent and product thereof

A magnetic iron oxide and desulfurizer technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of difficult molding of desulfurizer products, poor diffusion performance, low mechanical strength, etc., to save preparation costs and high production efficiency , Anti-mud performance improvement effect

Active Publication Date: 2013-10-23
BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is that the high sulfur capacity desulfurizer in the prior art has poor water resistance and poor diffusion performance if the binder content is high, and the desulfurizer product is difficult to form if the binder content is low, The problem of low mechanical strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing spheroidal high-sulfur-capacity magnetic iron oxide desulfurizing agent and product thereof
  • Method for preparing spheroidal high-sulfur-capacity magnetic iron oxide desulfurizing agent and product thereof
  • Method for preparing spheroidal high-sulfur-capacity magnetic iron oxide desulfurizing agent and product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Put 20kg of yellow rice as ball nuts into the granulator and roll them, spray a small amount of water solution of celadon powder to wet the ball ball surface, and then add magnetic iron oxide Fe 21.333 o 32 Began to form a ball, and the scallop powder accounts for 5% of the total mass of the safflower powder aqueous solution; then, depending on the size of the ball and the degree of surface dryness, alternately add the scallop powder aqueous solution and magnetic iron oxide Fe to the granulator 21.333 o 32 , adding magnetic iron oxide Fe 321.333 o 32 The amount increases from small to small, and the surface of the ball is completely covered by magnetic iron oxide Fe 21.333 o 32 When covering, it is necessary to spray the binder aqueous solution, and when the surface of the ball is wetted by the binder aqueous solution, it is necessary to add magnetic iron oxide Fe 21.333 o 32 , a total of 179kg of magnetic iron oxide Fe was added in this step 21.333 o 32 And...

Embodiment 2

[0035] (1) Put 0.2kg millet as ball nut into the granulator to roll, spray a small amount of sodium carboxymethyl cellulose CMC aqueous solution to wet the ball ball surface, and then add magnetic iron oxide Fe 21.333 o 32 Begin to form a ball, the organic binder CMC accounts for 3% of the total mass of the CMC aqueous solution; then, depending on the size of the ball and the degree of surface dryness, alternately add the CMC aqueous solution and the magnetic iron oxide Fe to the granulator 21.333 o 32 , adding magnetic iron oxide Fe 21.333 o 32 The amount increases from small to small, and the surface of the ball is completely covered by magnetic iron oxide Fe 21.333 o 32 When covering, it is necessary to spray the binder aqueous solution, and when the surface of the ball is wetted by the binder aqueous solution, it is necessary to add magnetic iron oxide Fe 21.333 o 32 , a total of 198kg of magnetic iron oxide Fe was added in this step 21.333 o 32 And 60kg of CMC aqu...

Embodiment 3

[0039] (1) Put 1.56kg of yellow rice as ball nuts into the granulator and roll them, spray a small amount of water solution of celadon powder to moisten the ball ball surface, and then add magnetic iron oxide Fe 21.333 o 32 Began to form a ball, and the scallop powder accounts for 10% of the total mass of the safflower powder aqueous solution; then, depending on the size of the ball and the degree of surface dryness, alternately add the scallop powder aqueous solution and magnetic iron oxide Fe to the granulator 21.333 o 32 , adding magnetic iron oxide Fe 21.333 o 32 The amount increases from small to small, and the surface of the ball is completely covered by magnetic iron oxide Fe 21.333 o 32 When covering, it is necessary to spray the binder aqueous solution, and when the surface of the ball is wetted by the binder aqueous solution, it is necessary to add magnetic iron oxide Fe 21.333 o 32 , a total of 192.44kg magnetic iron oxide Fe was added in this step 21.333 o ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a spheroidal high-sulfur-capacity magnetic iron oxide desulfurizing agent. The method comprises the following steps of: placing a female ball into rolling equipment, wetting the surface of the female ball through utilizing an organic binding agent water solution, alternately adding magnetic iron oxide Fe21.333O32 and the organic binding agent water solution, gradually forming a ball, so as to obtain spheroidal high-sulfur-capacity magnetic iron oxide Fe21.333O32 small balls with different diameters; naturally airing or drying the obtained small balls after shaping. According to the desulfurizing agent prepared by using the method: the female ball accounts for 0.1%-10% of the total mass of the desulfurizing agent, the magnetic iron oxide Fe21.333O32 accounts for87%-99% of the total mass of the desulfurizing agent, and an organic binding agent accounts for 0.5%-3% of the total mass of the desulfurizing agent. The preparation method provided by the invention has the advantages that the problems that the high-sulfur-capacity desulfurizing agent in the prior art is high in binding agent content, poor in water tolerance and poor in diffusion capability are solved, the prepared binding agent content is low, the water tolerance is good, and the diffusion ability is good.

Description

technical field [0001] The invention relates to a method for preparing a desulfurizing agent and a product thereof. Specifically, it is a method for preparing a spherical high-sulfur-capacity magnetic iron oxide desulfurizer and its product. Background technique [0002] As we all know, sewage treatment, papermaking, petroleum processing, chemical fertilizer manufacturing, chemical fiber manufacturing and some chemical raw material manufacturing industries discharge a large amount of hydrogen sulfide, which not only causes environmental pollution, but also easily leads to catalyst poisoning and deactivation, so reducing hydrogen sulfide in industrial production The amount of emissions has become one of the major problems that need to be solved in today's world industrial production. [0003] At present, in order to effectively reduce the impact of hydrogen sulfide on industrial production and the environment, a variety of hydrogen sulfide desulfurizers have been introduced ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/30B01J20/06
Inventor 刘振义付文敬
Owner BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products