Microemulsion semisynthetic copper wiredrawing liquid composition and preparation method thereof

A copper wire drawing liquid, semi-synthetic technology, used in lubricating compositions, petroleum industry and other directions, can solve the problems of oil product evaporation and smoke, on-site environment deterioration, slow heat dissipation of lubricating oil, etc., to achieve fast heat transfer speed, cooling Good effect, small temperature rise effect

Inactive Publication Date: 2013-10-16
安徽富华电子集团有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat dissipation of the lubricating oil is slow, which will damage the mold and affect the product quality. At the same time, the high temperature can easily ignite the oil or cause the oil to evaporate and smoke, resulting in the deterioration of the site environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A microemulsion semi-synthetic copper wire drawing liquid composition is made from the following raw materials (kg) in parts by weight:

[0015] Soybean oil 20, di-tert-butyl p-cresol 2, potassium triborate 3, benzotriazole 2, sodium butylnaphthalene sulfonate 2, film-forming aid 3, alkenyl succinic acid 1, silane coupling agent KH-550 4. Water 120;

[0016] The film-forming aid is made of the following raw materials in parts by weight (kg): benzoquinone 0.2, styrene 8, tert-butyl hydroperoxide 0.1, itaconate 3, silane coupling agent KH550 2, 1- Hydroxyethyl-2-oleyl imidazoline 3;

[0017] The preparation method is: mix styrene and itaconate, stir, add tert-butyl hydroperoxide and benzoquinone, stir and react for 45-60 minutes, then add 1-hydroxyethyl-2-oleyl imidazoline, Stir the reaction, the reaction temperature is 70-80°C, after 30-40 minutes of reaction, add the silane coupling agent KH550, and stir the reaction for 1-2 hours; that is.

[0018] Preparation of wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a microemulsion semisynthetic copper wiredrawing liquid composition and a preparation method thereof. The composition is prepared from the following raw materials by weight parts: 20-25 parts of soybean oil, 1-2 parts of di-t-butyl-p-cresol, 3-4 parts of tri potassium borate, 1-2 parts of benzotriazole, 2-3 parts of sodium butyl naphthalene sulfonate, 2-3 parts of a film forming auxiliary agent, 1-2 parts of alkenyl succinic acid, 3-4 parts of a silane coupling agent KH-5503, and 100-120 parts of water. According to the invention, the soybean oil is used as a lubricating component, thereby being environmental friendly and reducing harm of a wire drawing environment on worker's health; the silane coupling agent KH-5503 is used, thereby improving a film forming effect of the wiredrawing liquid, increasing a wiredrawing speed, facilitating corrosion inhibition components to form films, and prolonging an anti-corrosion time.

Description

technical field [0001] The invention relates to the technical field of copper wire drawing, and relates to a microemulsion semi-synthetic copper drawing liquid composition and a preparation method thereof. Background technique [0002] Copper wire (wire) is the main transmission wire for power transmission in the power industry. It is usually made by drawing process, that is, a metal wire with a large diameter such as steel wire passes through the hole of the mold, and is drawn under the action of external force to reduce the cross-sectional area to form the required diameter. of wire. [0003] In the existing wire drawing process, lubricating oil is mostly used as the wire drawing medium. The surface of the drawn wire is round, delicate, smooth, transparent, free of debris, the broken wire rate is reduced, and the product quality is greatly improved. However, the lubricating oil dissipates heat slowly, damages the mold, and affects product quality. At the same time, the hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10N40/24C10N30/12C10N30/06
Inventor 陈金桃谢士强唐传恩吴忠章龚平赵贵勇
Owner 安徽富华电子集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com