A kind of low surface treatment high-performance anti-rust primer for mechanical equipment and its preparation method

A low surface treatment, anti-rust primer technology, applied in the direction of anti-corrosion coatings, coatings, epoxy resin coatings, etc., can solve the problems of poor corrosion resistance, low coating efficiency, high processing requirements, etc., to achieve enhanced wettability and Permeability, improvement of construction performance, super adhesion effect

Active Publication Date: 2016-07-06
洛阳双瑞防腐工程技术有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the coating can solve the current high requirements for the surface treatment of the substrate for the primer of my country's mechanical equipment (it is easy to cause the coating to fall off due to poor sandblasting or shot blasting), low coating efficiency, high coating cost and poor corrosion resistance. pending issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low surface treatment high-performance anti-rust primer for mechanical equipment and its preparation method
  • A kind of low surface treatment high-performance anti-rust primer for mechanical equipment and its preparation method
  • A kind of low surface treatment high-performance anti-rust primer for mechanical equipment and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The quality composition of the low surface treatment high performance antirust primer for mechanical equipment is shown in Table 1:

[0023] Table one: the quality composition of each component of embodiment 1

[0024]

[0025] The mass ratio of component A: component B = 5:1.

[0026] Embodiment 1 coating technical index is as shown in table two:

[0027] Table two: embodiment 1 coating technical index

[0028]

Embodiment 2

[0030] The quality composition of the low surface treatment high performance antirust primer for mechanical equipment is shown in Table 3:

[0031] Table three: the quality composition of each component of embodiment 2

[0032]

[0033] The mass ratio of component A: component B = 5.4:1.

[0034] Embodiment 2 coating technical index is as shown in table four:

[0035] Table four: embodiment 2 coating technical index

[0036]

Embodiment 3

[0038] The quality composition of the low surface treatment high performance antirust primer for mechanical equipment is shown in Table 5:

[0039] Table five: the quality composition of each component of embodiment 3

[0040]

[0041] The mass ratio of component A: component B is 6:1.

[0042] Embodiment 3 coating technical index is as shown in table six:

[0043] Table six: embodiment 3 coating technical index

[0044]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance rust inhibiting primer for low surface treatment of mechanical equipment. The high-performance rust inhibiting primer is composed of a component A and a component B, wherein the component A comprises the following components in parts by mass: 50.0-57.0 parts of bisphenol A epoxy resin, 2.0-6.0 parts of modified resin, 1.0-3.0 parts of reactive toughening agent, 1.2-2.0 parts of penetrating agent, 9.0-11.0 parts of organic solvent, 2.0-5.0 parts of gradient alcohol solvent, 0.2-0.5 part of defoaming agent, 0.3-1.5 parts of wetting dispersant, 24.0-55.0 parts of rust inhibiting filler, 1.0-3.0 parts of rust converting agent and 0.1-0.3 part of substrate wetting agent; the component B comprises the following components in parts by mass: 13.0-14.0 parts of cardanol modified Mannich amide curing agent, 0.3-1.0 part of adhesive force promoter and 5.0-9.0 parts of organic solvent; and the mass ratio of the component A to the component B is 5:1 to 6:1. The primer has excellent adhesive force and favorable curing and film forming properties when coated on a wet substrate with the rust layer thickness of less than 80mum, so that the requirement for low surface treatment of the mechanical equipment is met.

Description

technical field [0001] The invention belongs to the technical field of mechanical equipment coatings, and in particular relates to a low-surface-treatment high-performance antirust primer for mechanical equipment and a preparation method thereof. Background technique [0002] The commonly used surface treatment methods for mechanical equipment are: manual derusting, sand blasting, shot blasting and chemical derusting, among which sandblasting and shot blasting are the most common methods. The biggest advantage of this rust removal method is high efficiency, low price, good effect, and more suitable for processing large components. At present, domestic mechanical equipment has a high self-made rate, a wide variety, complex shapes, weird structures, many dead ends, and large size differences. , the requirements for sand blasting and shot blasting are high, and the sand blasting and rust removal standards cannot be fully met, and it is prone to incomplete rust removal, insuffic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/02C09D7/12C09D5/08
Inventor 卫小星陈华山苏松峰董翔
Owner 洛阳双瑞防腐工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products