Decontamination finishing agent used for polyester fiber, and preparation method thereof

A polyester fiber and finishing agent technology, applied in fiber processing, fiber types, textiles and papermaking, etc., can solve the problems of unwashable textiles, poor decontamination performance of polyester fibers, and difficulty in removing dirt, etc. The effect of easy decontamination, improved fluffy and soft feeling, and excellent washability

Active Publication Date: 2013-09-25
DUPLUS CHEM OF ZHANGJIAGANG CITY
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, polyester fiber has poor decontamination performance
In commonly used laundry methods, such as washing in conventional domestic washing machines or hand washing with bars, it is often very difficult to remove soils from textile materials and, given the removal of unwanted substances from textiles, residues Soil in the water often redeposits on the textile material before the wash cycle is complete, making the textile impossible to wash

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decontamination finishing agent used for polyester fiber, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1) Weigh 800 grams of polyethylene glycol, 150 grams of ethylene glycol, 180 grams of dimethyl terephthalate, 800 grams of polyamide, and 10 grams of magnesium acetate;

[0016] 2) Put the above materials into the reaction kettle, raise the temperature to 140°C and keep it for 190 minutes, continue to raise the temperature to 220°C and keep it for 70 minutes, then carry out the polymerization reaction at a vacuum degree of -0.08MP and a temperature of 230°C to generate a number average molecular weight of 5000~ 6000 block copolymer of polyester polyether polyamide, after cooling down to 190°C, discharge;

[0017] 3) Mix the block copolymer of polyester polyether polyamide, glycerin and water into a solution according to the mass ratio of 1:3:96.

Embodiment 2

[0019] l) Weigh 900 grams of polyethylene glycol, 140 grams of ethylene glycol, 170 grams of dimethyl terephthalate, 700 grams of polyamide, and 7 grams of zinc acetate;

[0020] 2) Put the above materials into the reactor, raise the temperature to 150°C and keep it for 160 minutes, continue to raise the temperature to 210°C and keep it for 60 minutes, then carry out the polymerization reaction at a vacuum degree of -0.08MP and a temperature of 240°C to generate a number average molecular weight of 8000~ 9000 polyester polyether polyamide block copolymer, after cooling down to 200 ℃, discharge;

[0021] 3) Mix the block copolymer of polyester polyether polyamide, ethylene glycol, and water into a solution in a mass ratio of 2:3:95.

Embodiment 3

[0023] l) Weigh 700 grams of polyethylene glycol, 160 grams of ethylene glycol, 190 grams of dimethyl terephthalate, 900 grams of polyamide, and 8 grams of calcium acetate;

[0024] 2) Put the above materials into the reaction kettle, raise the temperature to 180°C and keep it for 180 minutes, continue to raise the temperature to 210°C and keep it for 60 minutes, then carry out the polymerization reaction at a vacuum degree of -0.09MP and a temperature of 280°C to generate a number average molecular weight of 14000~ 15000 block copolymer of polyester polyether polyamide, after cooling down to 200 ℃, discharge;

[0025] 3) Mix the block copolymer of polyester polyether polyamide, fluorine-containing resin, and water into a solution according to the mass ratio of 3:3:94.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a decontamination finishing agent used for polyester fiber, and a preparation method thereof. The finishing agent comprises, by weight, 1-5% of a polyester-polyether-polyamide block copolymer, 2-5% of glycerol or ethylene glycol or fluorine resin, and balance of water. The polyester-polyether-polyamide block copolymer is prepared from the raw materials of, by weight: 60-160 parts of polyethylene glycol, 13-40 parts of glycol, 14-26 parts of dimethyl terephthalate, 15-100 parts of polyamide, and 0.2-1 parts of metal acetate as a catalyst. With the in-bath crease-resisting agent provided by the invention, the polyester fiber is provided with good decontamination performance. Also, fluffy and soft texture, antistatic property, hydrophilic smoothness, and the like of polyester fiber can be improved. The decontamination finishing agent has excellent washing resistance, and does not fail after at least 30 times of washing.

Description

technical field [0001] The invention relates to a decontamination finishing agent for polyester fibers and a preparation method thereof. Background technique [0002] As we all know, polyester fiber has poor decontamination performance. In commonly used laundry methods, such as washing in conventional domestic washing machines or hand washing with bars, it is often very difficult to remove soils from textile materials and, given the removal of unwanted substances from textiles, residues Dirt in the water often redeposits on the textile material before the wash cycle is complete, making the textile impossible to wash. Therefore, it is very necessary to modify the polyester fiber before leaving the factory to make it have good decontamination performance. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a stain-removing finishing agent for polyester fibers. [0004] Another technical problem to be solved by the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/148D06M15/256D06M15/59C08G69/44D06M101/32
Inventor 陈金辉吴玉春方玉琦李芳
Owner DUPLUS CHEM OF ZHANGJIAGANG CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com