Low-temperature resisting co-polypropylene modified material as well as preparation method and application thereof

A technology of copolymerized polypropylene and modified materials, which is applied in the field of low temperature resistant copolymerized polypropylene modified materials and its preparation, can solve the problems such as unchecked modified polypropylene material patents, and achieves good low temperature resistance performance, simple operation, Wide range of effects

Active Publication Date: 2013-08-21
CGN JUNER NEW MATERIALS +1
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few relevant reports on the use of modified polypropylene for plastic seals, and no relevant patents on modified polypropylene materials used for plastic seals have been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature resisting co-polypropylene modified material as well as preparation method and application thereof
  • Low-temperature resisting co-polypropylene modified material as well as preparation method and application thereof
  • Low-temperature resisting co-polypropylene modified material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Add copolymerized polypropylene, elastomer, linear low-density polyethylene, grafted polyethylene, stabilizers (including Irganox 1010 and Irganox 168) and processing aids into the high-speed mixing pot according to the amount shown in Table 6, stir and mix evenly. The mixed material is obtained, in which the source and performance of the raw materials are shown in Table 1. The mixture material is fed into the twin-screw extruder from the feeder, and the residence time of the material in the screw is 50 seconds to 120 seconds. The temperature of the twin-screw extruder from the feeding section to the head is: 180℃, 215℃ , 215℃, 215℃, 215℃, 215℃, 215℃, the temperature of the die is 220℃. After high-speed twin-screw (screw speed of 600r / min) shearing, mixing, extrusion, drawing, air cooling, drying, pelletizing and packaging by the head, the low-temperature resistant copolymer polypropylene modified material is prepared.

[0057] Table 1 Sources and properties of raw materi...

Embodiment 2

[0060] The preparation method is as in Example 1, the source of raw materials and properties are shown in Table 2, and the amount of raw materials is shown in Table 6.

[0061] Table 2 Raw material source and performance

[0062]

[0063]

Embodiment 3

[0065] The preparation method is as in Example 1, the source of raw materials and properties are shown in Table 3, and the amount of raw materials is shown in Table 6.

[0066] Table 3 Raw material source and performance

[0067]

[0068]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-temperature resisting co-polypropylene modified material as well as a preparation method and an application thereof. The low-temperature resisting co-polypropylene modified material comprises the following raw materials in percentage by weight: 60-98% of co-polypropylene, 1-20% of an elastomer, 0-10% of linear low-density polyethylene, 0-8% of stem grafting polyethylene, 0.1-1% of a stabilizer and 0.1-1% of a processing agent. The modified material has both good tension strength and high-temperature property and good low-temperature property, the performances of a conventional polypropylene plastic sealing stripe are improved, the requirements on use of the plastic sealing stripe at high and low temperatures are met, and the modified material can be used for preparing various plastic sealing stripes, such as air container sealing stripes, cultivation sealing stripes, self-locking type sealing stripes and anti-theft sealing stripes.

Description

Technical field [0001] The invention relates to a polypropylene modified material in the field of polymer materials, in particular to a low-temperature resistant copolymerized polypropylene modified material, and a preparation method and application thereof. Background technique [0002] A plastic seal is an accessory made of plastic. It consists of two parts. One end is a round or square plastic mouth with a hook-shaped elastic plastic buckle, and the other end is a plastic seal body with serrations. The body can be bent through the front plastic opening and form a loop, similar to the belt of pants, which can be used for binding and packaging; plastic seals are usually made by one injection molding process, which can be made into yellow, blue, white, green, orange, and red And other bright colors. Since the serrations on the seal strip can be tightly fitted with the elastic plastic buckle inside the plastic mouth, the plastic seal can play a very firm role in fixing. It is no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/08C08L51/06B29B9/06B29C47/92B29C48/92
Inventor 郑京连黄志杰李俊张鑫
Owner CGN JUNER NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap