UV (ultraviolet) curing ink and application thereof

A technology of ink and resin, applied in UV curing ink and its application field, can solve the problems of high processing cost, adverse effects on human health and safety production, etc., and achieve the effect of good cutting fluid resistance, small environmental hazards, and high surface hardness

Active Publication Date: 2013-08-07
深圳市美丽华科技股份有限公司
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to provide a UV curable ink and its application, which is a UV curable ink that can be peeled off from glass with a low-concentration acid and has a protective effect. Solve the problem of high processing cost and adverse effects on human health and safety production in the existing mobile phone glass processing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV (ultraviolet) curing ink and application thereof
  • UV (ultraviolet) curing ink and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0102] The present invention is described in further detail as follows by embodiment 1-4 as shown in table 1:

[0103] Table 1

[0104]

[0105] Add the components of any proportion of Examples 1 to 4 in the above Table 1 into the container according to the stated ratio, mix well under stirring conditions, and then construct according to the following process and parameters.

[0106] Process sequence:

[0107] Substrate cleaning→printing→IR baking→UV curingsurface processing→removal of low-concentration acid solution→clean water cleaning.

[0108] Process parameters:

[0109] Mesh: 200-300 mesh / inch (77-120 / cm);

[0110] Film thickness: 16-20um (Mitutoyo);

[0111] Cumulative UV energy 1500~2200mj / cm 2 (EIT UV Power Puck II);

[0112] Spectral range: 180~420nm;

[0113] UV lamp power: 80-120W / cm;

[0114] IR temperature: 100-110°C: 2-3min.

[0115] The properties of the ink layer obtained in Examples 1-4 on the glass surface are shown in Table 2.

[0116] Table ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a UV (ultraviolet) curing ink and application thereof. The UV curing ink comprises the following components in percentage by weight: 30-40% of high-functionality polyurethane acrylate, 10-20% of dual-functionality polyurethane acrylic resin, 5-10% of amine-modified polyether acrylate prepolymer, 5-10% of thermoplastic acrylic resin, 10-15% of 1,6-hexanediol diacrylate, 2-4% of photosensitizer, 1-2% of nano aluminum oxide dispersion and 15-20% of filler. The UV photocuring ink is used for temporary protection in the glass surface working process; and after the UV photocuring ink is subjected to UV photocuring, a tough ink layer can be formed on the glass surface, thereby effectively ensuring the glass not to be scratched in the surface working process. After finishing the glass working, the glass can be soaked in 5% sulfuric acid solution, which is heated to 50 DEG C, to remove the UV curing ink on the glass surface without influencing the glass.

Description

technical field [0001] The invention relates to the field of inks, in particular to a UV curable ink and its application. Background technique [0002] At present, mobile phones are developing in the direction of smart phones, among which touch screen mobile phones are popular, so glass is becoming a common and important material in mobile phone manufacturing. Usually mobile phone glass processing technology: glass raw materialcutting→profiling→fine carving→rough grinding→fine polishing→cleaning→strengthening→printing→packaging. Among them, coarse grinding and fine polishing are mainly to solve the problem of glass being scratched in the first few processing processes, but the processing cost of these two processes is very high, and the dust has a great adverse effect on the health and safety of workers. [0003] Therefore, the prior art needs to be perfected and developed. Contents of the invention [0004] In view of the above-mentioned deficiencies in the prior art, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C03C17/32C09D11/00C09D11/101
Inventor 鲁春风
Owner 深圳市美丽华科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products