Method for manufacturing core-shell type supported catalysts and core-shell type supported catalysts formed thereby

A supported catalyst, core-shell technology, applied in the field of preparing core-shell supported catalysts, can solve problems such as industrial difficulties in mass production, and achieve the effects of optimizing loading, shortening time, and reducing the amount of platinum

Inactive Publication Date: 2013-06-19
HYUNDAI MOTOR CO LTD +1
View PDF6 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, mass production using this method is industrially difficult because a reduction process requiring a high-temperature heat treatment process is performed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing core-shell type supported catalysts and core-shell type supported catalysts formed thereby
  • Method for manufacturing core-shell type supported catalysts and core-shell type supported catalysts formed thereby
  • Method for manufacturing core-shell type supported catalysts and core-shell type supported catalysts formed thereby

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0067] Hereinafter, the present invention will be described in detail with reference to the following examples, which illustrate embodiments of the present invention and are not intended to limit the scope of the present invention.

[0068] [Example]

[0069] According to the preparation method of the present invention, a catalyst is prepared, wherein palladium (Pd) and platinum (Pt) are supported on the surface of carbon at a metal weight ratio (Pd:Pt) of 5:5, 3:7 and 7:3 .

[0070] Hereinafter, the preparation process will be described in detail.

[0071] First, 300 g of deionized water (DI water) was mixed with 300 g of acetylene black to form a 600 mg mixture, and the mixed solution was repeatedly stirred, homogenized, and sonicated to disperse the acetylene black. Then, the resulting solution was mixed with SDS (sodium dodecyl sulfate) added at 0.5 times the weight relative to carbon. The addition of SDS disperses the carbon uniformly in the aqueous solution and acts t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A method for manufacturing a core-shell type supported catalyst, wherein alloy particles having a core-shell structure with a different interior and exterior are supported on a complex carbon support. The method includes: 1) dissolving and dispersing a carbon support in a solvent using a stabilizer; 2) dissolving a core precursor in the solution, and adding a strong reducing agent to reduce and support a transition metal of the core precursor on a surface of the carbon support; 3) filtering and washing the carbon support on which the transition metal is supported; 4) re-dispersing the filtered and washed carbon support in a shell precursor aqueous solution; and 5) adding a weak reducing agent to the solution of step 4) at 60-80 DEG C. so that metal ions of a shell precursor are selectively reduced and deposited on the transition metal.

Description

technical field [0001] The invention relates to a method for preparing a core-shell type supported catalyst. More specifically, the present invention relates to a method for preparing a core-shell type supported catalyst in which alloy particles having different inner and outer core-shell structures are supported on a composite carbon support. Background technique [0002] A fuel cell is a device that converts the chemical energy of a fuel, such as hydrogen, into electrical energy. Such fuel cells have theoretical efficiencies as high as 100%, and typically have high efficiencies of 80-50%. Thus, much research has been done on the efficient use of fuel cells and the use of hydrogen as a renewable energy source, especially with limited available fossil fuel resources. [0003] The electrical energy generation of fuel cells is mainly based on electrochemical reactions accompanied by electron transfer. It is important to initiate a reaction that minimizes the overvoltage in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/44B01J35/00H01M4/92
CPCH01M4/921H01M4/926Y02E60/50B01J13/02B01J21/00B01J23/42B01J23/44
Inventor 卢范旭
Owner HYUNDAI MOTOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com