Method for quickly repairing damaged pavement by combustion process

A combustion method and fast technology, applied in the direction of roads, roads, road repair, etc., can solve problems such as affecting traffic and long time for road repair, and achieve the effect of saving transportation links and shortening the time for repair and curing.

Active Publication Date: 2014-12-03
RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the technical problem to be solved by the present invention is that in the prior art, the road repair time is relatively long, which leads to the problem of long-term road closures affecting traffic, and then provides a method for quickly repairing the road surface with a shorter curing time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0057] (1) Heat 60 parts of ceramic sand aggregate with a particle size of 70-140 mesh and a specific gravity of 1.8-2.0 to 150-160°C;

[0058] (2) heating and melting 30 parts of thermoplastic phenolic resin, and adding it into the ceramic sand aggregate while it is hot and stirring evenly to obtain a stable coating material;

[0059] (3) Mix 1 part of urotropine and 0.5 part of solid potassium permanganate particles evenly, and add 1.5 parts of water to disperse them evenly;

[0060] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0061] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a particle size of 70-140 mesh, and sieve it to obta...

Embodiment 2

[0067] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0068] (1) Heat 95 parts of ceramsite aggregate with a particle size of 70-140 mesh and a specific gravity of 1.7-2.5 to 700-800°C, and then naturally cool to 90-100°C;

[0069] (2) Heat and melt 4 parts of thermoplastic boron phenolic resin, and add it to the ceramsite aggregate while it is hot and stir evenly to obtain a stable coating material;

[0070] (3) Mix 10 parts of urotropine and 1 part of solid potassium chlorate particles evenly, and add 4 parts of water to disperse them evenly;

[0071] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0072] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a particle size of 70-140 mesh, and s...

Embodiment 3

[0078] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0079] (1) Heat 85 parts of small steel ball aggregates with a particle size of 20-40 mesh and a specific gravity of 7.9 to 160-200°C, and then naturally cool to 90-100°C;

[0080] (2) Heat and melt 10 parts of thermosetting silicone-modified epoxy resin, and add it into the small steel ball aggregate while it is hot and mix evenly to obtain a stable coating material;

[0081] (3) Mix 2 parts of ammonium chloride and 0.6 parts of solid sodium nitrate particles evenly, and add 2.5 parts of water to disperse them evenly;

[0082] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0083] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a particl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of pavement repair, and particularly relates to a method for quickly repairing a damaged pavement by heating a repair material capable of releasing oxygen under heat by a combustion process. The method provided by the invention comprises the following steps: (1) filling a fast-curing repair material capable of releasing oxygen into pits in the damaged pavement, and flattening; and (2) spraying an inflammable liquid onto the flattened parts of the pavement, and igniting to cure the fast-curing repair material capable of releasing oxygen under heat, thereby repairing the damaged pavement. The fast-curing pavement repair material capable of releasing oxygen is prepared from 60-95 parts of compact aggregate, 4-30 parts of thermoplastic resin binding agent, 1-10 parts of heat-initiated latent curing agent capable of inducing fast curing of the thermoplastic resin binding agent under heat, and 0.5-1 part of solid oxidant capable of releasing oxygen under heat. The method can implement curing of the repair material within 50-70 minutes, thereby greatly shortening the repair curing time.

Description

technical field [0001] The invention belongs to the field of road construction, and in particular relates to a method for quickly repairing damaged road surfaces by using heated cocoa oxygen-releasing repair materials combined with combustion heating. Background technique [0002] With the rapid development of my country's economy, the number of airport runways has increased rapidly, a large number of high-grade highways have been constructed, and the implementation of concrete projects such as city squares and municipal highways has improved the quality of human life and promoted the healthy development of the national economy. Most of the existing roads use concrete construction pavement, which not only has good quality but also has a long service life. However, the maintenance of the concrete pavement after the pavement is damaged during use is more complicated. It needs to be closed and out of service for repair, and it needs to use relatively large machinery to plan and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/14C04B26/12E01C23/09C04B111/72
Inventor 秦升益王振邦汪卫坤
Owner RENCHSAND ECO ENVIRONMENT PROTECTION SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com