Matt alkyd resin and preparation method thereof

An alkyd resin, matte technology, applied in the field of resin, can solve the problems of poor paint film fullness and transparency, poor matte alkyd resin fullness, poor paint film transparency and other problems, and achieve excellent performance. , easy to implement, good fullness and vividness

Active Publication Date: 2014-12-10
JIANGMEN SANMU CHEM
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Some resins have good matting properties, but poor fullness and transparency of the paint film
[0004] 2. Some resin paint films have good fullness and transparency, but poor matting properties
Therefore most of the matte alkyds do not have good fullness
In order to improve the fullness of the paint film, the matting property of the paint film is sacrificed. Therefore, in order to achieve the required gloss when making paint, the amount of matte powder will be increased, which not only increases the cost, but also deteriorates the transparency of the paint film, because The transparency of the paint film decreases when more matte powder is added

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. A matte alkyd resin, which is made from the following raw materials in parts by weight:

[0033] 15 parts of coconut oil, 14 parts of soybean oil fatty acid, 15 parts of monopentaerythritol, 30 parts of phthalic anhydride, 5 parts of glycerin, 10 parts of ethylene glycol, 0.2 parts of hypophosphorous acid, 6 parts of xylene, 25 parts of toluene, and 8 parts of ethyl acetate.

[0034] 2, the preparation method of matte alkyd resin, comprises the following steps:

[0035] (1) Put 15 parts of coconut oil acid, 14 parts of soybean oil fatty acid, 15 parts of monopentaerythritol, 30 parts of phthalic anhydride, 5 parts of glycerin, 10 parts of ethylene glycol, 0.2 parts of hypophosphorous acid, and 6 parts of xylene into the reaction kettle, stir and mix Uniform;

[0036] (2) Feed nitrogen into the reaction kettle to remove the oxygen in the reaction kettle, then raise the temperature to 180°C, keep warm for esterification for 4 hours, then raise the temperature to 190°C...

Embodiment 2

[0039] 1. A matte alkyd resin, which is made from the following raw materials in parts by weight:

[0040] 10 parts of lauric acid, 8 parts of cotton oil fatty acid, 10 parts of monopentaerythritol, 25 parts of phthalic anhydride, 1 part of glycerin, 5-10 parts of neopentyl glycol, 0.05 parts of triphenyl phosphite, 3 parts of xylene, 20 parts of trimethylbenzene Parts, 4 parts of dimethyl carbonate.

[0041] 2, the preparation method of matte alkyd resin, comprises the following steps:

[0042] (1) 10 parts of lauric acid, 8 parts of cotton oil fatty acid, 10 parts of monopentaerythritol, 25 parts of phthalic anhydride, 1 part of glycerin, 5-10 parts of neopentyl glycol, 0.05 parts of triphenyl phosphite, and 3 parts of xylene Put it into the reaction kettle, stir and mix evenly;

[0043] (2) Introduce carbon dioxide protective gas into the reaction kettle to remove the oxygen in the reaction kettle, then raise the temperature to 180°C, keep warm for esterification for 4 ho...

Embodiment 3

[0046] 1. A matte alkyd resin, which is made from the following raw materials in parts by weight:

[0047] 12 parts of caprylic acid, 12 parts of linseed oil fatty acid, 12 parts of monopentaerythritol, 28 parts of phthalic anhydride, 3 parts of glycerin, 7 parts of methyl propylene glycol, 0.05 parts of hypophosphorous acid and 0.05 parts of triphenyl phosphite, 3 parts of xylene, trimethylbenzene 22 parts, 6 parts of dimethyl carbonate.

[0048] 2, the preparation method of matte alkyd resin, comprises the following steps:

[0049](1) 12 parts of caprylic acid, 12 parts of linseed oil fatty acid, 12 parts of monopentaerythritol, 28 parts of phthalic anhydride, 3 parts of glycerin, 7 parts of methyl propylene glycol, 0.05 parts of hypophosphorous acid and 0.05 parts of triphenyl phosphite, 3 parts of xylene Pour into the reaction kettle, stir and mix evenly;

[0050] (2) Introduce carbon dioxide protective gas into the reaction kettle to remove the oxygen in the reaction ke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a matt alkyd resin and a preparation method thereof. The matt alkyd resin is prepared by the following components: 10-15 parts of short-chain fatty acid, 8-14 parts of octadecanoic alkene vegetable oil acid, 10-15 parts of mono-pentaerythritol, 25-30 parts of phthalic anhydride, 1-5 parts of glycerol, 5-10 parts of divalent alcohol, 0.05-0.2 part of color subtraction agent, 3-6 parts of dimethyl benzene, 20-25 parts of diluted aromatic solvent and 4-8 parts of diluted low-boiling-point esters solvent. According to the matt alkyd resin provided by the invention, the components and mixture ratios of all raw materials are screened through lots of experiments so as to prepare and obtain the matt alkyd resin with appropriate molecular weight, and the matt alkyd resin has the advantages of excellent matting property, good transparency and fullness and wide application range. The preparation method of the matt alkyd resin has the advantages of reasonable process design, high preparation efficiency, low energy consumption and easiness in implementation, the whole preparation technology has strong operability and the matt alkyd resin prepared by adopting the preparation method has excellent performances.

Description

technical field [0001] The invention relates to a resin, in particular to a matte alkyd resin and a preparation method thereof. Background technique [0002] Matte alkyd resin is mainly used for matte polyester paint for home decoration, and the market demand is very large. In the paint making process, matt powder is mainly added to the matte resin to achieve matting, but the matte produced by different matte alkyd resins Varnish properties vary. To evaluate the quality of matt resin, it mainly reflects the matting property (that is, the gloss after being made into a paint), transparency, and fullness. The matte alkyd resins currently on the market for matte polyester paints have the following problems: [0003] 1. Some resins have good matting properties, but poor fullness and transparency of the paint film. [0004] 2. Some resin paint films have good fullness and transparency, but poor matting properties. [0005] Because most of the matte alkyd resins currently on th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/49C08G63/81
Inventor 杨森薛伟邵瑞峰
Owner JIANGMEN SANMU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com