Color gel coat for sanitary ware and preparation method thereof

A technology for sanitary ware and gel coat, which is applied in the field of colored gel coat for sanitary ware and its preparation, can solve the problems of difficult production, difficult to control the gel solidification time, etc., and achieves the effect of ensuring water resistance, rich colors and good surface tension

Active Publication Date: 2015-09-16
CHANGZHOU ZHONGJIE COMPOSITES
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In particular, it is difficult to control the gelation and curing time in the production process of the gel coat with a lighter color, which makes it difficult to be practically used in production for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color gel coat for sanitary ware and preparation method thereof
  • Color gel coat for sanitary ware and preparation method thereof
  • Color gel coat for sanitary ware and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1）

[0019] The colored gel coat of the sanitary ware of the present embodiment is ivory white, and it is made by the component of following parts by weight:

[0020] 100 parts of matrix resin; among them, 90 parts of medium-active matrix resin, whose molecular weight distribution index (Mw / Mn) ≤ 2.5, specifically adopts the m-phenylene neopentyl glycol type matrix resin of Huari Company's model 251, in which unsaturated di The number of moles of basic acid is 50% of the total number of moles of dibasic acid; 10 parts of highly active matrix resin, its molecular weight distribution index (Mw / Mn) ≤ 2.5, the specific use of Huari company's model is 230 isophthalic new Pentylene glycol-based matrix resin, in which the mole number of unsaturated dibasic acid is 70% of the total mole number of dibasic acid.

[0021] 12 parts of styrene.

[0022] 20 parts of talcum powder.

[0023] Fumed silica 2 parts.

[0024] 0.15 part of thixotropic stabilizer, what adopt is the PR600 type thixotr...

Embodiment 2～ Embodiment 5）

[0033] Each embodiment is basically the same as Embodiment 1, and the differences are shown in Table 1.

[0034]

[0035]

[0036]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colored gel coat for sanitary ware and a manufacturing method of the colored gel coat. The colored gel coat for the sanitary ware is manufactured by components including, by weight, 100 parts of matrix resin, 8-20 parts of styrene, 10-30 parts of functional filler, 2-3 parts of thixotropic agent, 0.12-0.2 part of thixotropic stabilizer, 0.6-1.2 parts of surface auxiliaries, 10-20 parts of color paste and 0.1-0.4 part of accelerator. The manufacturing method includes weighing the components for use according to formula; firstly placing the matrix resin into a dispersing reactor, adding the functional filler with stirring, dispersing after adding, adding the thixotropic stabilizer, adding the thixotropic agent with stirring, dispersing after adding and obtaining the matrix gel coat; adding the color paste, the styrene, the surface auxiliaries and the accelerator into the gel coat, and uniformly stirring to obtain the colored gel coat for the sanitary ware. The colored gel coat for the sanitary ware is colorful and has excellent resistance to heat and cod impact.

Description

technical field [0001] The invention relates to a gel coat and a preparation method thereof, in particular to a colored gel coat for sanitary ware and a preparation method thereof. Background technique [0002] At present, the materials of sanitary ware are mostly ceramic or enamel, and some are made of acrylic. Among them, the biggest disadvantage of ceramics and enamel is that the comfort is poor, especially when used in winter, it feels cold and very uncomfortable. Although acrylic has better comfort, its wear resistance, stain resistance and weather resistance are not good, and the surface is prone to aging and discoloration. [0003] Gel coat is a surface material with certain thixotropy, good rheology and excellent mechanical properties obtained by adding thixotropic agent and rheological additive to a suitable matrix resin through high-speed dispersion or grinding. Due to its good comprehensive performance, it is widely used in ships, vehicles, buildings, clothing a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/06C09D7/12C09D5/29
Inventor 孙全收龚方红
Owner CHANGZHOU ZHONGJIE COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com