Polyoxy propane diethylene glycol borate polymer, preparation method thereof and environment-friendly water-soluble anti-rust quenching liquid prepared with polymer

A technology of polyoxypropylene diethylene glycol borate and diethylene glycol borate, applied in quenching agents, manufacturing tools, heat treatment equipment, etc. Not hard and other problems, to achieve the effect of good anti-rust effect, low cost of use, deep hardened layer

Active Publication Date: 2014-05-14
上海德润宝特种润滑剂有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the quenching medium used in the metal heat treatment process is mainly mineral oil or water. Mineral oil quenching is mainly used for medium and low carbon steels with a high quenching tendency. Due to the slow cooling rate of oil, it often occurs that the quenching is not hard or the quenching layer is shallow. The problem is that water is mainly used as a quenching medium for alloy steel with a small tendency to quench cracking. Since the characteristic of water is that the cooling rate is faster in high and low temperature areas, it is difficult to control during the production process. Quenching cracks often occur and quenching is not hard or quenching is not good. average phenomenon
At present, some units are also researching some water-soluble quenching liquids, mainly adding some lipophilic and hydrophilic organic compounds and inorganic salts to the water, often with poor anti-rust performance, or adding carcinogenic and teratogenic ingredients such as nitrite or nitrate Anti-rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyoxy propane diethylene glycol borate polymer, preparation method thereof and environment-friendly water-soluble anti-rust quenching liquid prepared with polymer
  • Polyoxy propane diethylene glycol borate polymer, preparation method thereof and environment-friendly water-soluble anti-rust quenching liquid prepared with polymer
  • Polyoxy propane diethylene glycol borate polymer, preparation method thereof and environment-friendly water-soluble anti-rust quenching liquid prepared with polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Weigh 25g of potassium borate and 3g of potassium sorbate and add them to 422g of water and stir, add 550g of polyoxypropylene diethylene glycol borate polymer B and stir for 2 hours at the same time to prepare the environment-friendly water-soluble anti-rust quenching liquid sample of the present invention.

[0050] The 10% aqueous solution of this sample was subjected to a damp heat test for 7 days according to the test method of GB / T2361, and the result was grade 1, meeting the standard.

[0051] Typical cooling rate characteristic curves of different concentrations of this sample's environment-friendly water-soluble anti-rust quenching liquid and tap water are as follows: figure 1 As shown (tested by IVF cooling rate tester in accordance with ISO 9950 standard). From figure 1 It can be seen that the cooling rate of the environment-friendly water-soluble anti-rust quenching liquid of the present invention is significantly lower than that of water in the convection s...

Embodiment 2

[0053] The quenching material is: 5CrMnMo, the size is: 760X310X280 die steel, the surface hardness after heat treatment is required to be 40-45HRC (the hardness difference is within 3HRC), and no rust can occur within 15 days after treatment. Quenching process: Preheat once at 500-550°C, heat at 830-850°C, temper twice at 450-480°C, and hold for 2 hours. Quenching tank volume is 15m 3 , can hold quenching medium 10-15 tons.

[0054] Add 500 kg of polyoxypropylene diethylene glycol borate polymer B to 473 kg of water to which 23 kg of potassium borate and 4 kg of potassium sorbate have been added and stir for 2.5 hours to prepare an environmentally friendly water-soluble anti-rust quenching liquid. The prepared environment-friendly water-soluble anti-rust quenching liquid is added to the quenching tank already equipped with 10 tons of water, and the pump is circulated to stir, and the quenching process also uses the pump to circulate.

[0055] Quality inspection results: Aft...

Embodiment 3

[0057] Step 1. Feed 124.136kg (2000mol) of ethylene glycol and 61.83kg (1000mol) of boric acid into the reaction kettle, fill it with nitrogen protection, stir and heat to about 175°C, keep it warm for 4.5 hours, pass in toluene and azeotrope the mixed solution, Diethylene glycol borate A138kg (1000mol) was obtained by distilling off the azeotrope of water and toluene.

[0058] Step 2. Add 138 kg (1000 mol) of diethylene glycol borate A and 10 kg of potassium hydroxide obtained in step 1 into a polymerization tank cooled by ice-salt water circulation at about 0°C and stir, then feed nitrogen into the polymerization tank to switch The air in the kettle, when the nitrogen in the polymerization kettle maintains a positive pressure, use the nitrogen feed tank to push 1742.4kg (30000mol) propylene oxide into the polymerization kettle, while stirring and raising the temperature to 100°C, and adjusting the pressure to 0.3MPa. After 16 hours of polymerization, Extrude the polymer in the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyoxy propane diethylene glycol borate polymer, a preparation method thereof and an environment-friendly water-soluble anti-rust quenching liquid prepared with the polymer. The polymer has a chemical formula shown in the description, wherein n is an integer from 30 to 40. The preparation method of the polymer comprises the steps of: reacting ethylene glycol with boric acid in a molar ratio of 2:1 to obtain diethylene glycol borate; and reacting the diethylene glycol borate with epoxy propane in a molar ratio of 1:(30-40) to obtain the polymer. The environment-friendly water-soluble anti-rust quenching liquid comprises the following components, by weight: 40-80% of polyoxy propane diethylene glycol borate polymer (containing a small amount of potassium hydroxide, diethylene glycol poly propyl ether and boric acid potassium salt), 2-3% of potassium borate, 0.1-0.5% of potassium sorbate, and the balance of water. The environment-friendly water-soluble anti-rust quenching liquid provided by the invention has rapid cooling capacity similar to that of water at a low temperature zone, slow cooling performance similar to that of oil at a high temperature zone, and inverse solubility to water; and because of the special cooling performance of the quenching liquid, it can effectively substitute a traditional process of water quenching and oil cooling, and is convenient and reliable for operation, healthful and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of heat treatment antirust quenching, and in particular relates to a polyoxypropylene diethylene glycol borate polymer, a preparation method thereof and an environment-friendly water-soluble antirust quenching liquid prepared from the polymer. Background technique [0002] At present, the quenching medium used in the metal heat treatment process is mainly mineral oil or water. Mineral oil quenching is mainly used for medium and low carbon steels with a high quenching tendency. Due to the slow cooling rate of oil, it often occurs that the quenching is not hard or the quenching layer is shallow. The problem is that water is mainly used as a quenching medium for alloy steel with a small tendency to quench cracking. Since the characteristic of water is that the cooling rate is faster in high and low temperature areas, it is difficult to control during the production process. Quenching cracks often occur and quenc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G65/28C21D1/60
Inventor 张乃庆吴启东
Owner 上海德润宝特种润滑剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products