Flame-retardant chain-extended polybutylene terephthalate composition and preparation method thereof

A technology of polybutylene terephthalate and a composition is applied in the field of polymer material modification, and can solve the problems of low thermal stability, high flame retardant cost, and decreased mechanical properties of PBT such as tensile strength, notched impact strength, etc. , to achieve the effect of reducing the total amount of flame retardants and improving the mechanical properties

Active Publication Date: 2013-02-06
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aluminum diethylphosphinate has the advantages of lower density, better color, higher CTI value (up to 600V) and higher thermal stability (decomposition temperature > 350°C), etc. Its flame retardancy is not enhanced by PBT, and its quality is When the dosage is 13%, the flame retardant grade of PBT can reach UL94 V-01.6mm , but at this dosage, the mechanical properties of PBT such as tensile strength, bending strength, notched impact strength, etc. all have a large degree of decline, and the degree of decline is directly related to the dosage. The greater the dosage, the more obvious the impact on the mechanical properties; In addition, aluminum diethylphosphinate is currently very expensive, and the flame retardant cost is very high at this dosage, which has become a major obstacle to its practical application. Therefore, reducing its dosage is very important to maintain its mechanical properties and obtain practical applications. the meaning of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant chain-extended polybutylene terephthalate composition and preparation method thereof
  • Flame-retardant chain-extended polybutylene terephthalate composition and preparation method thereof
  • Flame-retardant chain-extended polybutylene terephthalate composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]The control total amount is 1000g, by mass percentage (recorded as wt%), with 87.5wt%PBT, 9wt% aluminum diethylphosphinate, 3wt% side group band epoxy polysiloxane (PPM1), 0.2wt% Antioxidant B215 and 0.3wt% anti-dripping agent FA-500 were added to a high-speed mixer, and after stirring and mixing at room temperature, the resulting premix was melted, kneaded, extruded, cooled, pelletized and processed by a twin-screw extruder. dry. The model of the twin-screw extruder used is LTE26 / 40 (LabTech, Germany), and the temperature of each zone of the screw barrel is: the first zone: 160°C, the second zone: 225°C, the third zone: 230°C, and the fourth zone : 230℃, the fifth zone: 230℃, the sixth zone: 230℃, the seventh zone: 230℃, the eighth zone: 230℃, the ninth zone: 230℃, the machine head: 225℃, the feeding speed: 25r / min, host speed: 150r / min. The prepared pellets were injection-molded into standard specimens for testing according to the standard size, and the mechanical p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant chain-extended polybutylene terephthalate (PBT) composition and a preparation method of the PBT composition. The composition comprises the following raw materials by weight: 85%-90% of PBT, 9%-12% of aluminum diethylphosphinate, 0.4%-3% of polysiloxane containing an epoxy group in the side group, and 0.3%-0.7% of processing agent, wherein the processing agent is an antioxidant and an anti-dripping agent. According to the invention, the adopted polysiloxane containing the epoxy group in the side group and aluminum diethylphosphinate have obvious flame retardant synergistic effects on PBT. When the flame retardant property reaches to UL94V-0@1.6mm, the dose of aluminum diethylphosphinate is reduced by about 20% and the total flame retardant dose is reduced by about 12%. Under the premise of same flame retardant level, the mechanical properties of the composition provided by the invention is greatly improved.

Description

technical field [0001] The invention relates to a flame-retardant chain-extended polybutylene terephthalate composition, which belongs to the technical field of polymer material modification. Background technique [0002] Polybutylene terephthalate (PBT) is a thermoplastic semi-crystalline resin with excellent mechanical, electrical, chemical corrosion resistance, easy molding and low moisture absorption. It is an engineering plastic with excellent comprehensive properties. It is widely used in the fields of electronic and electrical, automobile industry, mechanical instrumentation, communication equipment and lighting components. However, PBT itself is easy to burn, and it will release a lot of heat when it burns, accompanied by a lot of smoke and toxic gases. Therefore, it is necessary to carry out flame-retardant modification of PBT, especially environmental protection flame-retardant modification, to reduce its potential fire hazard. It is a major problem that needs to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L83/06C08K5/5313B29C47/92B29C48/92
CPCB29C48/0022B29C48/04B29C48/40B29C48/911B29C48/92
Inventor 赵建青韩潇刘述梅袁彦超朱亚明刘运春
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com