Method for desilicating molten iron by stirring
A technology for molten iron and desiliconization, which is applied in the field of molten iron stirring and desiliconization, and desiliconization of casting pig iron. Good, responsive effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] In this example, 5 tanks of desiliconization were carried out. The desiliconization route of molten iron sinter is: molten iron tank—a small amount of slag removal—lowering stirring paddle for stirring—feeding of sinter and mixture—stirring and desiliconization—lifting the paddle to stop stirring—slagging off. The inner height of the hot metal treatment tank is 4120mm, the mouth diameter is 3100mm, and the average clearance height of the hot metal tank is 1.25m. Sintered ore powder T.Fe>55%, the mixture is a mixture of lime and fluorite, the mixing mass ratio is 9:1, lime powder CaO>85%; fluorite powder CaF 2 >85%, see Table 1, Table 2 and Table 3. The raw material ratio and addition amount of the desiliconizing agent are shown in Table 4.
[0029] Table 1 Composition of sinter
[0030] Fe 2 o 3 / %
FeO / %
T.Fe / %
CaO / %
SiO 2 / %
67.3
6.0
55.4
10
4
[0031] Table 2 Composition of lime powder
[0032] ...
Embodiment 2
[0042] In this example, 5 tanks of desiliconization were carried out. The process route for desiliconization of molten iron oxide scale is: molten iron tank—a small amount of slag removal—adding oxide scale and mixture—stirring desiliconization——slagging off. The average clearance height of the hot metal tank is 1.3m. The T.Fe=72.03% of the iron oxide scale, the mixture is the mixed powder of lime and fluorite, and the composition is shown in Table 2 and Table 3. The raw material ratio and addition amount of the desiliconizing agent are shown in Table 6 and Table 7.
[0043] Table 6 Iron oxide scale composition
[0044] T.Fe / %
T.O / %
CaO / %
S / %
SiO 2 / %
72.03
30.87
1.07
0.025
0.91
[0045] Table 7 The relationship between the amount of desiliconization agent
[0046] Hot metal ΔSi / %
Rolled steel sheet / kg / t 铁
Mixture / kg / t 铁
0.1
4.6
1.7
0.15
6.9
2.5
0.2
9.2
...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com