Spherical magnesium halide adduct and preparation method and application thereof

A technology of magnesium halides and adducts, applied in the direction of magnesium organic compounds, etc.

Active Publication Date: 2014-11-05
CHINA PETROLEUM & CHEM CORP +1
View PDF22 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the magnesium halide adduct prepared according to the method of this patent application has a large amount of irregular particles, such as needle-shaped particles and rod-shaped particles, and when the catalyst using the magnesium halide adduct as a carrier is used for olefin polymerization, it will undoubtedly cause The resulting polymer also has a large number of irregular particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spherical magnesium halide adduct and preparation method and application thereof
  • Spherical magnesium halide adduct and preparation method and application thereof
  • Spherical magnesium halide adduct and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0024] According to one embodiment of the present invention, the spherical magnesium halide adduct may or may not contain o-hydroxybenzoate and / or polyol ester. In this case, the spherical magnesium halide adduct can be represented by the general formula MgXY-mROH-nCH 3 OH-sG-tDOE-qH 2 O represents, wherein, MgXY, ROH, m, n and q are all the same as the above definitions, G represents o-hydroxybenzoate, s is 0-0.05, DOE represents polyol ester, and t is 0-0.1. When s and t are all 0 (that is, the spherical magnesium halide adduct does not contain o-hydroxybenzoate and polyol ester), the general formula MgXY-mROH-nCH 3 OH-sG-tDOE-qH 2 O is equivalent to the general formula MgXY-mROH-nCH 3 OH-qH 2 O; when t is 0, but s is not 0 (that is, the spherical magnesium halide adduct contains o-hydroxybenzoate, but does not contain polyol ester), the general formula MgXY-mROH-nCH 3 OH-sG-tDOE-qH 2 O is equivalent to the general formula MgXY-mROH-nCH 3 OH-sG-qH 2 O; when s is 0, b...

Embodiment 1

[0060] This example is used to illustrate the spherical magnesium halide adduct provided by the present invention and its preparation method and application.

[0061] (1) Preparation of spherical magnesium chloride adduct

[0062] In a 300L autoclave, add 90L of white oil, 90L of silicone oil, 9.0kg of magnesium chloride (94.7mol) and 14.5L of ethanol (249.0mol), raise the temperature to 125°C under stirring, and stir at 125°C for 2.5 Hour, then, the mixed liquid obtained enters in the hexane that is cooled to-30 ℃ in advance after being fully sheared and dispersed by the high-gravity rotating bed, filters off liquid, and washes five times with hexane, obtains the solid matter of 18kg after drying ( Alcoholate of magnesium chloride).

[0063] In a 1.6L reactor, add 900ml of hexane, add 90 grams of the above-mentioned solid matter, and then dissolve 45ml of dimethoxypropane solution (dimethoxypropane) in 180ml of hexane The content is 0.37mol) was added therein, then, the tem...

Embodiment 2

[0070] This example is used to illustrate the spherical magnesium halide adduct provided by the present invention and its preparation method and application.

[0071] Preparation of spherical magnesium chloride adduct, preparation of olefin polymerization catalyst, and polymerization of propylene were carried out in the same manner as in Example 1, except that the amount of hydrogen added during the polymerization of propylene was 5.0 L.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a spherical magnesium halide adduct and a preparation method thereof. The method comprises the following steps of: (1) mixing magnesium halide and alcohols except methanol with optional inert liquid media and heating the obtained mixture under stirring until a melt of the magnesium halide adduct is formed; (2) adding the melt of the magnesium halide adduct to cooling media after shearing and dispersing the melt to form spherical solid particles; and (3) carrying out contact reaction on the spherical solid particles and dimethoxy propane in the inert dispersion media. The invention also provides application of the magnesium halide adduct as a catalyst carrier. The magnesium halide adduct has the following beneficial effects: the morphology of particles of the magnesium halide adduct is more regular and is basically spherical; the particle size distribution is more concentrated; basically special-shaped particles do not exist; and the catalyst prepared by adopting the spherical magnesium halide adduct as the catalyst carrier has better hydrogen regulation sensitivity in propylene polymerization reaction.

Description

technical field [0001] The present invention relates to a spherical magnesium halide adduct, a preparation method of the spherical magnesium halide adduct, a spherical magnesium halide adduct prepared by the method, and an application of the spherical magnesium halide adduct as a catalyst carrier . Background technique [0002] The preparation of Ziegler-Natta catalysts by supporting titanium compounds and electron donor compounds on active magnesium halides is well known in the prior art. Usually, the active magnesium halide uses an adduct of magnesium halide and alcohol, which is used as a carrier to react with titanium halide and an electron donor compound to obtain a spherical catalyst. When the spherical catalyst is used for olefin polymerization (especially propylene polymerization), it has high polymerization activity and stereospecificity, and the obtained polymer has good particle shape. [0003] The disclosed adducts of magnesium halides and alcohols generally in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07F3/02C08F4/02C08F10/00
Inventor 夏先知刘月祥赵瑾张纪贵凌永泰李威莅乔素珍谭扬彭人琪高平高富堂张志会
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com