Process method capable of improving comprehensive mechanical property of multielement zinc-aluminum alloy

A zinc-aluminum alloy and comprehensive mechanics technology is applied in the field of improving the comprehensive mechanical properties of multi-element zinc-aluminum alloys, and can solve the problems of low dimensional stability, poor creep resistance, and low working temperature.

Inactive Publication Date: 2012-10-10
ZHENJIANG YINUOWEI SHAPE MEMORY ALLOYS
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, aluminum-zinc alloys also have disadvantages such as poor plasticity and toughness, low dimensional stability, low working temperature, poor creep resistance, and poor corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process method capable of improving comprehensive mechanical property of multielement zinc-aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Based on industrial aluminum ingot No. A00, zinc ingot No. 0, electrolytic copper, composite modifier (including Ni20-30%, Ti15-25%, Mn5-15%, Cr5-15%, Si5-10%, Ce5-10%, La5-10%, Y1-6%, Nb1-6%, V1-6%, the remainder is aluminum), pure magnesium as raw materials. The composition is calculated by weight percentage, weighing according to the proportion of Al28%, Cu2.3% (in the form of aluminum copper master alloy containing 50% copper), composite modifier 0.6%, Mg 0.015%, and the balance being Zn. Melting in an intermediate frequency induction melting furnace. The smelting process is as follows: first add aluminum ingots, zinc ingots, aluminum-copper intermediate alloys, and composite modifiers. After the materials are all melted, heat up to 600~650℃ and keep them for 6min-8min to homogenize the elements in order to reduce the burning loss of magnesium Use the bell jar to press the magnesium into the molten metal, and use the 0.2% dehydrated ZnCl containing the molten metal ...

Embodiment 2

[0012] Based on industrial aluminum ingot No. A00, zinc ingot No. 0, electrolytic copper, composite modifier (including Ni20-30%, Ti15-25%, Mn5-15%, Cr5-15%, Si5-10%, Ce5-10%, La5-10%, Y1-6%, Nb1-6%, V1-6%, the remainder is aluminum), pure magnesium as raw materials. The composition is calculated by weight percentage, weighing according to the proportion of Al28%, Cu2.3% (in the form of aluminum copper master alloy containing 50% copper), composite modifier 0.6%, Mg 0.015%, and the balance being Zn. Melting in an intermediate frequency induction melting furnace. The smelting process is as follows: first add aluminum ingots, zinc ingots, aluminum-copper intermediate alloys, and composite modifiers. After the materials are all melted, heat up to 600~650℃ and keep them for 6min-8min to homogenize the elements in order to reduce the burning loss of magnesium Use the bell jar to press the magnesium into the molten metal, and use the 0.2% dehydrated ZnCl containing the molten metal ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a multielement zinc-aluminum alloy capable of improving comprehensive mechanical property, belonging to the technical field of zinc-aluminum alloy preparation. The multielement zinc-aluminum alloy is characterized in that the multielement zinc-aluminum alloy is prepared from the following raw materials: industrial aluminum ingot NO.A00, zinc ingot NO.0, electrolytic copper, composite modifier and pure magnesium, wherein the composite modifier contains 20-30% of Ni, 15-25% of Ti, 5-15% of Mn, 5-15% of Cr, 5-10% of Si, 5-10% of Ce, 5-10% of La, 1-6% of Y, 1-6% of Nb, 1-6% of V and the balance of aluminum; the multielement zinc-aluminum alloy is smelted in a medium-frequency induction melting furnace after weighing 27-29% of Al, 2-2.5% of Cu (added in the form of aluminum-copper intermediamidstfrequencye alloy containing 50% of copper ), 0-1.2% of composite modifier, 0.01-0.02% of Mg and the balance of Zn based on percentage by weight. A round-rod-shaped blank iscasted by a common metal type and metal type vibrational casting method, and then processed to a national standard test rod to be subjected to mechanical property testing.

Description

Technical field [0001] The invention belongs to the technical field of zinc aluminum alloy preparation, and particularly refers to a process method that can improve the comprehensive mechanical properties of multiple zinc aluminum alloys. Background technique [0002] The application and development of aluminum-zinc alloys was one of the hot spots in the field of metal materials research in the 1980s and 1990s. This is because as a substitute material for copper, tin and their alloys, aluminum-zinc alloy has the advantages of high tensile strength and hardness, good damping, good wear resistance, small friction coefficient, low friction temperature rise, and low material and manufacturing costs. . However, aluminum-zinc alloys also have disadvantages such as poor plastic toughness, low dimensional stability, low working temperature, poor creep resistance, and poor corrosion resistance. Over the years, people have made unremitting efforts to overcome these shortcomings in order ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C18/04C22C21/10C22C1/03C22C1/06C22C30/06B22D1/00
Inventor 李晓薇杨嵩司松海刘光磊陆松华
Owner ZHENJIANG YINUOWEI SHAPE MEMORY ALLOYS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com