Inner container of refrigeration equipment and preparation method thereof

A technology of refrigeration equipment and inner tank, which is applied in household refrigeration equipment, lighting and heating equipment, chemical instruments and methods, etc., can solve the problems of low intensity of high-gloss surface layer, long purchase cycle, and no corrosion resistance, so as to reduce the risk of cracking. , Improve strength, good anti-corrosion effect

Inactive Publication Date: 2012-09-12
HEFEI MIDEA REFRIGERATOR CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The high-gloss surface layer has low strength, brittleness, and no corrosion resistance. The resulting lining, especially the box lining, is easy to crack, and there are quality risks;
[0004] 2. In order to reduce the possibility of cracking, the thickness of the surface layer is usually less than 3%, and the mold is also affected. The gloss of the obtained box lining is actually very low, and even the gloss cannot be seen;
[0005] 3. The thickness of the extruded board surface layer is not easy to control, and the qualified rate of extruded board and blister is low;
[0008] 1. Different grades of ABS special materials provided by different suppliers have differences in color and performance;
[0009] 2. There are compatibility problems between different ABS special materials, and they cannot be mixed, which causes inconvenience to production management;
[0010] 3. At present, only a few companies can produce this kind of ABS special material, all rely on imports, the purchase cycle is long, and the price is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inner container of refrigeration equipment and preparation method thereof
  • Inner container of refrigeration equipment and preparation method thereof
  • Inner container of refrigeration equipment and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1: Door liner of refrigeration equipment (total thickness 1.8mm)

[0036] The material of the surface layer is Chevron natural color HIPS-D6007.

[0037] The primary raw material is Yangba HIPS-2710, dyed with masterbatch, and 70% crushed material or recycled granulated material is used as the recycled material.

[0038] The base material is TOTAL HIPS-8265, dyed with masterbatch.

[0039] Mix Yamba HIPS-2710, color masterbatch and recycled materials evenly to obtain mixed materials;

[0040] Chevron natural color HIPS-D6007, Total HIPS-8265 and the mixture are melted and co-extruded through the extruder die to form a semi-finished sheet. By adjusting the speed of the metering pump, the surface layer thickness of the HIPS three-layer composite sheet is 0.15. mm, the thickness of the base layer is 1.50mm, and the thickness of the bottom layer is 0.15mm, wherein the temperature of the extruder head is 190-240°C, and the melting temperature is 180-240°C;

[0041...

Embodiment 2

[0044] Example 2: Door liner of refrigeration equipment (total thickness 1.8mm)

[0045] The material of the surface layer is Chevron natural color HIPS-D6007.

[0046] The base material is Styron HIPS-1173, dyed with masterbatch, and 70% crushed material or recycled granulated material is used as the recycled material.

[0047] The base material is TOTAL HIPS-8265, dyed with masterbatch.

[0048] Mix Styron HIPS-1173, color masterbatch and recycled material evenly to obtain the mixed material;

[0049] Chevron natural color HIPS-D6007, Total HIPS-8265 and the mixture are melted and co-extruded through the extruder die to form a semi-finished sheet. By adjusting the speed of the metering pump, the surface layer thickness of the HIPS three-layer composite sheet is 0.15. mm, the thickness of the base layer is 1.50mm, and the thickness of the bottom layer is 0.15mm, wherein the temperature of the extruder head is 190-240°C, and the melting temperature is 180-240°C;

[0050] Th...

Embodiment 3

[0053] Embodiment 3: tank of refrigeration equipment (total thickness 4.8mm)

[0054] The material of the surface layer is Chevron natural color HIPS-D6007.

[0055] The raw material of the base layer is Yangba HIPS-2710, dyed with masterbatch, and 50% crushed material or recycled granulated material is used as the recycled material.

[0056] The bottom material is PE-PS alloy.

[0057] Mix Yamba HIPS-2710, color masterbatch and recycled materials evenly to obtain mixed materials;

[0058] Chevron natural color HIPS-D6007, PE-PS alloy and the mixed material are melted and then co-extruded through the extruder die to form a semi-finished sheet. By adjusting the speed of the metering pump, the surface layer thickness of the HIPS three-layer composite sheet is 0.45mm. , the thickness of the base layer is 3.90mm, and the thickness of the bottom layer is 0.45mm, wherein, the extruder head temperature is 190-240°C, and the melting temperature is 180-240°C;

[0059] The semi-finis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an inner container of refrigeration equipment and a preparation method thereof. The inner container of the refrigeration equipment is formed by an HIPS (high impact polystyrene) three-layer composite board, the HIPS three-layer composite board comprises a surface layer, a basic layer and a bottom layer, wherein the surface layer is composed of a surface layer HIPS, and the surface layer HIPS is selected from one or more types of natural color HIPS, tinction HIPS and modification extrusion grade HIPS; and the basic layer comprises the natural color extrusion grade HIPS and a feeding material, and the bottom layer is composed of a resistance foaming agent erosion HIPS. According to the inner container of the refrigeration equipment provided by the embodiment of the invention, the HIPS three-layer composite board is adopted to shape, and the surface layer, the basic layer and the bottom layer of the HIPS three-layer composite board are all made of HIPS materials; the different HIPS materials after screening have good consistency, and can be mutually mixed; and the appearance and processing behaviour of the board can not be obviously influenced, the intensity of the board is improved, and the cracking risk is reduced.

Description

technical field [0001] The invention relates to the technical field of preparation of household appliances, and more specifically, the invention relates to an inner container of a refrigeration device and a preparation method thereof. Background technique [0002] The high-gloss HIPS composite panels for refrigerators / freezers in the prior art all adopt a three-layer composite system, and the surface layer is high-gloss HIPS. The bottom layer is HIPS for ordinary extrusion grade refrigerators. This board has the following disadvantages: [0003] 1. The high-gloss surface layer has low strength, brittleness, and no corrosion resistance. The resulting lining, especially the box lining, is easy to crack, and there are quality risks; [0004] 2. In order to reduce the possibility of cracking, the thickness of the surface layer is usually less than 3%, and the mold is also affected. The gloss of the obtained box lining is actually very low, and even the gloss cannot be seen; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F25D23/00B32B27/30B29C51/10
Inventor 曹家汉王巍项灵芝贾丽石祥祚
Owner HEFEI MIDEA REFRIGERATOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products