Method for single-stage vanadium extraction in same converter

A single vanadium extraction and converter technology, which is applied in the manufacture of converters, etc., can solve the problems of reduced scrap processing and large heat loss, and achieve the effect of solving large heat loss and reducing energy consumption in the converter process

Active Publication Date: 2012-07-11
SICHUAN DAZHOU IRON & STEEL GROUP
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, my country's double converter vanadium extraction process not only requires a separate converter to extract vanadium from molten iron, but also has a large heat loss in the process of vanadium extraction from molten iron, resulting in a reduction in the amount of scrap steel to be processed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for single-stage vanadium extraction in same converter
  • Method for single-stage vanadium extraction in same converter

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The method for extracting vanadium in the same furnace single-connected converter provided in this embodiment comprises the following steps:

[0027] (1) Put the vanadium-containing molten iron into the converter, and the charging amount is controlled at 82.0 tons / furnace, wherein the carbon content of the molten iron is 3.6%, which is 0.20%, the temperature of the molten iron is 1290°C, and the total content of silicon, manganese, and titanium is 0.90% , the total content of silicon and titanium is 0.60%;

[0028] (2), molten iron pretreatment desulfurization, desulfurization of molten iron to 0.070%;

[0029] (3), remove the slag in the molten iron, so that the amount of slag in the molten iron is 0.5%;

[0030] (4) Temperature measurement and sampling of molten iron. The composition and temperature of molten iron in the furnace must meet the requirements of conditions (1) and (2), and the molten iron + pig iron block is blended into the converter;

[0031] (5) Vana...

Embodiment 2

[0040] The method for extracting vanadium in the same furnace single-connected converter provided in this embodiment comprises the following steps:

[0041] (1), vanadium-containing molten iron is loaded into the converter, and the charging amount is controlled at 79.0 tons / furnace, wherein the carbon content of the molten iron is 5.8%, the vanadium content is 0.40%, the temperature of the molten iron is 1250 ° C, and the total content of silicon, manganese and titanium is 0.50%, the total content of silicon and titanium is 0.40%;

[0042] (2), molten iron pretreatment desulfurization, desulfurization of molten iron to 0.030%;

[0043] (3), remove the slag in the molten iron, so that the amount of slag in the molten iron is 0.2%;

[0044] (4) Temperature measurement and sampling of molten iron. The composition and temperature of molten iron in the furnace must meet the requirements of conditions (1) and (2), and the molten iron + pig iron block is blended into the converter; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for single-stage vanadium extraction in the same converter. In a blowing early stage, lime is not added for slagging, vanadium in molten iron is oxidized to enter slag, and silicon, manganese and titanium in the molten iron are oxidized to enter a slag phase; and blowing is stopped after the vanadium is oxidized, vanadium slag is discharged, lime and other slag formers are added for slagging and steelmaking, and qualified molten steel is produced. Compared with the prior art, the method for single-stage vanadium extraction in the same converter has the advantages of reducing temperature loss in the vanadium extracting process, improving the production efficiency of a converter workshop and reducing production cost.

Description

technical field [0001] The invention relates to the field of battery production, in particular to a method for single-connected vanadium extraction with a converter and a furnace. Background technique [0002] As an important metal, vanadium is widely used in many fields. At present, the world's vanadium resources are very limited, which mainly comes from vanadium-titanium magnetite, which accounts for a large proportion of vanadium-containing resources. The main way to recover vanadium from this mine is to convert vanadium-titanium magnetite Raw ore is smelted into vanadium-containing pig iron through blast furnace, and vanadium is recovered from vanadium-containing pig iron. At present, the methods for extracting vanadium from molten iron mainly include shaking ladle vanadium extraction in South Africa and top-bottom dual-link method of converter vanadium extraction in China. However, my country's double converter vanadium extraction process not only requires a separate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C5/36
Inventor 王皎月龚波张琦喻春亮王林张华
Owner SICHUAN DAZHOU IRON & STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com