High-fluidity tire forming gypsum powder and preparation process thereof

Abstract

A high-fluidity tire forming gypsum powder and a preparation process thereof are provided. The gypsum powder is composed of the following raw materials in parts by weight: 100 parts of alpha-gypsum powder, 15-25 parts of white silicate cement, 0.5-1.5 parts of sulfonated melamine formaldehyde resin, 1-3 parts of peach gum, and 5-15 parts of magnesium sulfate. The invention further provides a preparation process of the high-fluidity tire forming gypsum powder. The high-fluidity tire forming gypsum powder of the invention not only has long effective stirring time and flowing time but also has proper initial coagulation time and final coagulation time; the tire forming gypsum die prepared by the invention is featured with high intensity, wide application range and long service life; and the preparation process is simple and easy in operation. In this way, the high-fluidity tire forming gypsum powder of the invention is beneficial to industrial production.

Description

technical field [0001] The invention relates to a high fluidity tire casting gypsum powder and a preparation process thereof. Background technique [0002] At present, most tire casting gypsum mold manufacturers directly use high-strength gypsum (α-gypsum) powder as raw material when making tire casting gypsum molds, and mix it with water at a mass ratio of 1:0.5-0.55 for mold making. The obtained gypsum slurry has a high degree of thinness and consistency, and its effective stirring time is only 3 minutes, the flow time is 3-5 minutes, the initial setting time is 9 minutes, and the final setting time is 30 minutes. In addition, the mold made by using the above-mentioned α-gypsum powder has a large expansion coefficient of about 0.5; a low dry flexural strength of about 7MPa; and a low dry compressive strength of about 22MPa. Because the initial setting time of the material is too short, the effective mixing time and flow time are also short, especially the fluidity is poor...

AI Technical Summary

Problems solved by technology

In addition, the mold made by using the above-mentioned α-gypsum powder has a large expansion coefficient, about 0.5; the dry flexural strength is low, about 7MPa; the dry compressive strength is also low, about 22MPa

Because the initial setting time of the material is too short, the effective mixing time and flow time are also short, especially the fluidity is poor, which not only causes certain limitations to the operation, but also is not conducive to the trimming of the mold made, especially because of the strength Insufficient, the service life of the mold is also low