Electroplating solution for surface of zinc alloy workpiece with blind hole
A workpiece surface and zinc alloy technology is applied in the field of electro-galvanizing solution on the surface of zinc alloy workpieces containing blind holes. Complete effect of coating
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] Zinc alloy die-casting parts with different depths of blind holes were used as workpieces to be plated. The blind holes were circular holes with a diameter of 10 mm and depths of 30 mm, 40 mm, 50 mm and 60 mm, respectively.
[0034] The electroplating process is: degreasing, water washing, rust removal, water washing, electrogalvanizing, water washing, drying, and detecting whether a coating is formed on the inner wall of the blind hole. The composition of the electroplating solution is: ZnCl 2 45g / L; KCl 155g / L; H 3 BO 3 21g / L; Surfactant A 0.28g / L, the balance is water. Solution temperature 25°C, cathode current density 1A / dm 2 , pH value = 5.5, electroplating time 60min. The resulting coating has good compactness, good gloss and good corrosion resistance. Plating is formed on all inner walls of blind holes with a depth of 30mm, 40mm, and 50mm, but no plating is formed on the bottom of a blind hole with a depth of 60mm
Embodiment 2
[0048] Zinc alloy die-casting parts with different depths of blind holes were used as workpieces to be plated. The blind holes were circular holes with a diameter of 10mm and depths of 30mm, 40mm, 50mm, and 60mm, respectively.
[0049] The electroplating process is: degreasing, water washing, rust removal, water washing, electrogalvanizing, water washing, drying, and detecting whether a coating is formed on the inner wall of the blind hole. The composition of the electroplating solution is: ZnCl 2 45g / L; KCl 155g / L; H 3 BO 3 21g / L; Surfactant A 0.28g / L; TX-10 0.15g / L, the balance is water. Solution temperature 25°C, cathode current density 1A / dm 2 , pH value = 5.5, electroplating time 60min. Coatings are formed on all inner walls of blind holes with different depths, and the obtained coatings have good compactness, good gloss and good corrosion resistance.
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
depth | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com