CaCu3Ti4O12 micro nano sized fiber and its preparation method

A micro-nano fiber technology, applied in fiber processing, spinning solution preparation, filament/thread forming, etc., can solve problems such as inability to carry out electrospinning, difficult electrospinning process, and increased viscosity of spinning solution. Achieve the effect of easy control, mild conditions and wide application

Inactive Publication Date: 2012-06-27
SUZHOU UNIV
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned technical solution provides fibers for preparing simple oxides, while CaCu 3 Ti 4 O 12 ceramics are composed of three metal elements in fixed proportions Composition, when titanium alkoxides and calcium and copper corresponding inorganic salts are used as raw materials, due to the crystal water contained in the calcium and copper inorganic salts and their own water absorption, the metal alkoxides will quickly Hydrolysis and polymerization, even part of the gel is produced, so that the viscosity of the spinning solution increases geometrically, far beyond the range that can be used for electrospinning. presents difficulties and even makes electrospinning impossible, therefore, the use of CaCu 3 Ti 4 O 12 nanofibers has not been seen so far , in the prior art, there is no report on the preparation of CaCu 3 Ti 4 O 12 micro-nano fibers by electrospinning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CaCu3Ti4O12 micro nano sized fiber and its preparation method
  • CaCu3Ti4O12 micro nano sized fiber and its preparation method
  • CaCu3Ti4O12 micro nano sized fiber and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1. Under stirring conditions, add 10 ml of absolute ethanol, 1.04 g of calcium nitrate tetrahydrate and 2.63 g of copper acetate monohydrate into the reaction vessel, and react at a constant temperature of 30°C for 2 hours to obtain solution A;

[0027] 2. Under stirring conditions, add 1.5 g of polyvinylpyrrolidone, 10 ml of absolute ethanol, 3 ml of acetic acid and 6 ml of butyl titanate into the reaction vessel, and react at a constant temperature of 30 ° C for 1 hour to obtain a solution B;

[0028] 3. Under stirring conditions, all the solution B prepared in step 2 was slowly added dropwise to solution A at a rate of 100 ml per hour to obtain solution C;

[0029] 4. Electrospinning solution C, the voltage used for electrospinning is 16.50 kV, the injection rate is 6.5 ml / hour, the curing distance is 12 cm, the receiving device is aluminum foil, and the electrospinning time is 3 hours. corresponding fibers;

[0030] 5. Dry the fiber obtained by electrosp...

Embodiment 2

[0034] 1. Under stirring conditions, add 15 ml of absolute ethanol, 1.04 g of calcium nitrate tetrahydrate and 2.63 g of copper acetate monohydrate into the reaction vessel, and react at a constant temperature of 45°C for 3 hours to obtain solution A;

[0035] 2. Under stirring conditions, add 2.5 grams of polyvinylpyrrolidone, 15 milliliters of absolute ethanol, 1.5 grams of tetramethylammonium hydroxide and 6 milliliters of butyl titanate into the reaction vessel, and react at a constant temperature of 45°C for 3 Hour, obtain solution B;

[0036] 3. Under stirring conditions, slowly add all the solution B prepared in step 2 to solution A at a rate of 200 ml per hour to obtain solution C;

[0037] 4. Electrospinning solution C, the voltage used for electrospinning is 19.50 kV, the injection rate is 8.5 ml / hour, the curing distance is 15 cm, the receiving device is aluminum foil, and the electrospinning time is 2 hours. corresponding fibers;

[0038] 5. Dry the fib...

Embodiment 3

[0040] 1. Under stirring conditions, add 20 ml of absolute ethanol, 2.08 g of calcium nitrate tetrahydrate and 5.26 g of copper acetate monohydrate into the reaction vessel, and react at a constant temperature of 50° C. for 1 hour to obtain solution A;

[0041] 2. Under stirring conditions, add 3 grams of polyvinylpyrrolidone, 20 milliliters of absolute ethanol, 3 grams of tetramethylammonium hydroxide and 12 milliliters of butyl titanate into the reaction vessel, and react at a constant temperature of 50 ° C for 1 Hour, obtain solution B;

[0042] 3. Under stirring conditions, all the solution B prepared in step 2 was slowly added dropwise to solution A at a rate of 150 ml per hour to obtain solution C;

[0043] 4. Electrospinning solution C, the voltage used for electrospinning is 23.50 kV, the injection rate is 9.5 ml / hour, the curing distance is 15 cm, the receiving device is aluminum foil, and the electrospinning time is 2 hours. corresponding fibers;

[0044] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a CaCu3Ti4O12 micro nano sized fiber and its preparation method, which belongs to the inorganic material technical field. The CaCu3Ti4O12 micro nano sized fiber comprises the elements of Ca, Cu, Ti and O with the mol ratio of 13412, and the diameter is 200-300 nanometers. The preparation method comprises the following steps mixing anhydrous ethyl alcohol, calcium nitrate tetrahydrate and copper acetate monohydrate to obtain a solution A; mixing anhydrous ethanol, butyl titanate and a spinning auxiliary agent to obtain a solution B; slowly adding the solution B in the solution A, and using a static spinning technology to prepare the CaCu3Ti4O12 micro nano sized fiber. The method of the invention can effectively control the hydrolysis process of the raw materials by selecting and adjusting the ratio of raw materials and the spinning auxiliary agent, the obtained static spinning solution possesses spinnability, and the method of the invention provides the novel CaCu3Ti4O12 micro nano sized fiber. The preparation method has the advantages of simple process, mild condition, easy control and wide applicability.

Description

Technical field [0001] The present invention involves a technique of inorganic fiber material, which specifically involves a micro -nano ceramic fiber and its preparation methods. Background technique [0002] Materials of High -Syrian constant can be used in the manufacturing of small -volume capacitance devices, which provides very possibilities for the miniaturization of electronic devices. Therefore, it has a wide range of uses in the fields of miniature resonators, filters, and portable phones.The microelectronics industry plays an increasingly important role. [0003] Subramanian et al. 3 TI 4 O 12 (Abbreviation is CCTO) It has a high dielectric constant (generally greater than 10000) within the temperature range of 100 to 500K, and within a wide temperature range, there is no structural phase phase and iron electrical phase.The application of materials in the electronics industry has a broad prospect. [0004] One -dimensional micro -elevation material represented by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/462C04B35/622D01D5/00D01D1/02
Inventor 秦大可顾嫒娟梁国正
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com