Method for producing two-layer transfer coating leather by aqueous polyurethane dry-method transfer coating process
A technology of water-based polyurethane and dry film transfer, which is applied in polyurea/polyurethane coatings, polyurea/polyurethane adhesives, leather surface treatment, etc., can solve the problems of MDF residues, etc., to solve the residue problems and eliminate environmental pollution problems , Improve the effect of hygienic performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] 1) Manufacture of back cover foam coating
[0022] By mass parts, 70 parts of soft water-based polyurethane, 5 parts of polyacrylic resin thickener, 3 parts of fluorine-modified hydroxyl-containing acrylic resin leveling agent and the industrialized high-dispersion pigment paste used in 5 parts of natural leather processing Mix evenly, and then 6 parts of blowing agent azobisisobutyronitrile (AIBN) are evenly dispersed in the mixed slurry to obtain a back cover foam coating;
[0023] Using the roller coating production line in the leather production process, the bottom cover foaming coating is rolled on the surface of the split leather, that is, the two-layer crust leather, and the application amount is 180g / m 2 , and then enter the drying tunnel to dry at 80°C, and finally use a roller ironing machine to iron and foam at 120°C to form a back cover foam coating on the surface of the split leather;
[0024] 2) Manufacture of surface coating
[0025] Mix 80 parts of med...
Embodiment 2
[0029] 1) Manufacture of back cover foam coating
[0030] In parts by mass, 50 parts of soft water-based polyurethane, 2 parts of polyacrylic resin thickener, 1 part of fluorine-modified hydroxyl-containing acrylic resin leveling agent and 3 parts of industrialized high-dispersion pigment paste used in natural leather processing Mix evenly, and then 4 parts of blowing agent azobisisobutyronitrile (AIBN) are evenly dispersed in the mixed slurry to obtain a back cover foam coating;
[0031]Using the roller coating production line in the leather production process, the bottom cover foaming coating is rolled on the surface of the split leather, that is, the two-layer crust leather, and the application amount is 240g / m 2 , and then enter the drying tunnel to dry at 65°C, and finally use a roller ironer to iron and foam at 140°C to form a back cover foam coating on the surface of the split leather;
[0032] 2) Manufacture of surface coating
[0033] Mix 60 parts of medium-hard wat...
Embodiment 3
[0037] 1) Manufacture of back cover foam coating
[0038] 80 parts of soft water-based polyurethane, 6 parts of polyacrylic resin thickener, 4 parts of fluorine-modified hydroxyl-containing acrylic resin leveling agent and the industrialized high-dispersion pigment paste used in 7 parts of natural leather processing by mass parts Mix evenly, and then 8 parts of blowing agent azobisisobutyronitrile (AIBN) are evenly dispersed in the mixed slurry to obtain a back cover foam coating;
[0039] Using the roller coating production line in the leather production process, the bottom cover foaming coating is rolled on the surface of the split leather, that is, the two-layer crust leather, and the application amount is 150g / m 2 , and then enter the drying tunnel to dry at 75°C, and finally use a roller ironing machine to iron and foam at 110°C to form a back cover foam coating on the surface of the split leather;
[0040] 2) Manufacture of surface coating
[0041] Mix 70 parts of medi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com