Elastic metal shining coating and its preparation method

An elastic metal and coating technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of poor anti-cracking effect and no elasticity of fluorocarbon metal paint, achieve good metal flashing effect, durable crack coverage, good elastic effect

Inactive Publication Date: 2012-05-09
FIRST NEW MATERIAL TECH DEV
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The embodiment of the present invention provides an elastic metal glitter paint and a preparation method thereof, which can solve the problem that the existing fluorocarbon metal paint has no elasticity and poor anti-cracking effect. Long-Life Flexible Metallic Glitter Paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Elastic metal shining coating and its preparation method
  • Elastic metal shining coating and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of above-mentioned elastic metallic glitter coating specifically comprises the following steps:

[0035] Prepare component one:

[0036] Get each raw material of the component one that prepares elastic metallic glitter paint by above-mentioned formula;

[0037] Add the methyl isobutyl ketone, butyl acetate, fluorocarbon resin, dispersant and xylene accounting for 10% of the total weight of xylene in the raw material of component one, and the fluorocarbon resin accounting for 30% of the total weight of the fluorocarbon resin into the dispersion tank disperse at a speed of 300-400rpm for 5 minutes; then add leveling agent, anti-scratch additive and aluminum silver paste, disperse at a speed of 800-1000rpm for 20 minutes, adjust the speed to 300-400rpm, Add defoamer, polyester polyol resin, remaining xylene and remaining fluorocarbon resin under stirring state, and after the bubbles completely disappear, the obtained product is component one;

[00...

Embodiment 1

[0047] This embodiment provides an elastic metal glitter paint, which is composed of component one and component two, wherein component one is composed of xylene, MIBK, butyl acetate, PMA, fluorocarbon resin JF-2X, polyester multi-component Alcohol resin, dispersant 163, leveling agent 361, defoamer 2020, anti-scratch additive 996 and curing agent N-75, the raw materials of component 1 are as follows by mass percentage:

[0048] component one

mass (kg)

Xylene

20.0

MIBK

7.0

[0049] Butyl acetate

10.0

PMA

4.0

Fluorocarbon resin JF-2X

45.0

Aluminum silver paste 214

8.0

Dispersant 163

0.5

Leveling agent 361

0.2

Defoamer 2020

0.3

Anti-scratch additive 996

1.0

Polyester polyol resin

4.0

component two

mass (kg)

Curing agent 22A-75

12.5

[0050]The preparation method of the elastic metal gli...

Embodiment 2

[0056] This embodiment provides an elastic metal glitter paint, which is composed of component one and component two, wherein component one is composed of xylene, MIBK, butyl acetate, PMA, fluorocarbon resin JF-2X, polyester multi-component Alcohol resin, dispersant 163, leveling agent 361, defoamer 2020, anti-scratch additive 996 and curing agent N-75, the raw materials of component 1 are as follows by mass percentage:

[0057] component one

[0058] Dispersant 163

[0059] The preparation method of the elastic metallic glitter paint in this embodiment is basically the same as that in Embodiment 1, see Embodiment 1, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an elastic metal shining coating and its preparation method, and belongs to the field of building materials. The coating is composed of a component 1 and a component 2 at the weight ratio of 6-10:1. The component 1 contains the following raw materials of: by weight, xylene, hexone, butyl acetate, propylene glycol methyl ether acetate, a fluorocarbon resin, aluminum paste, a dispersant, a leveling agent, an antifoaming agent, a scratch-resistance auxiliary agent and a polyester polyol resin. The component 2 is a curing agent. The combination of a fluorine-containing polymer and the elastic polyester resin in the coating endows the paint film with good elasticity, resistance to chemicals, non-adhesiveness, low friction and the like. Therefore, the coating provided by the invention is an elastic and persistant coating with excellent comprehensive properties. The raw materials of the coating are easily available. The coating requires a simple production method and convenient manual operation, accords with application requirements, has an extensive application prospect, and can be used for resisting fine cracks on exterior walls of buildings.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an elastic metal flash paint with elastic flash effect for exterior walls of modern urban buildings and external thermal insulation walls and a preparation method thereof. Background technique [0002] Since the early 1980s, fluorocarbon coatings cured at room temperature have been successfully developed. This easy-to-use coating has unparalleled weather resistance, chemical resistance, corrosion resistance, non-staining properties, water resistance, high hardness and Excellent properties such as high gloss. However, fluorocarbon metal paint itself has no elasticity, and the anti-cracking effect is not good. In recent years, conventional fluorocarbon metal paint has cracked on the insulation base surface with the cracking of the insulation base layer, causing serious cracking of the fluorocarbon metal paint film, which affects the appearance of the entire building. Image, and e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D175/06C09D7/12C09D5/00
Inventor 李娅刘东华郭丽娟
Owner FIRST NEW MATERIAL TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com