Polythiol epoxy resin curing agent and preparation method thereof

An epoxy resin curing and epoxy resin technology, which is applied in the field of polythiol epoxy resin curing agent and its preparation, can solve problems such as complicated product purification steps, and achieves low production raw material cost, good compatibility, and raw material cost. reduced effect

Inactive Publication Date: 2012-03-28
XIAMEN UNIV
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this preparation method is that the purification steps of the product are complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 15.1 parts of sorbitol, 0.002 parts of p-toluenesulfonic acid, 54.2 parts of mercaptoacetic acid and 30.6 parts of toluene were successively added to a 250 ml three-necked flask equipped with a condenser tube and a stirrer. After reflux reaction for 4h, vacuum distillation was carried out. Add 9.1 parts of epoxy resin (638) and react at 100°C for 1 hour.

Embodiment 2

[0020] 15.1 parts of sorbitol, 0.002 parts of p-toluenesulfonic acid, 54.2 parts of mercaptoacetic acid and 30.6 parts of toluene were successively added to a 250 ml three-necked flask equipped with a condenser tube and a stirrer. After reflux reaction for 4h, vacuum distillation was carried out. Add 12.1 parts of epoxy resin (6101) and react at 100°C for 1.5h.

Embodiment 3

[0022] 15.1 parts of sorbitol, 0.002 parts of p-toluenesulfonic acid, 54.2 parts of mercaptoacetic acid and 30.6 parts of toluene were successively added to a 250 ml three-necked flask equipped with a condenser tube and a stirrer. After reflux reaction for 4h, vacuum distillation was carried out. Add 18.1 parts of epoxy resin (618) and react at 100°C for 2 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a curing agent, particularly a polythiol epoxy resin curing agent and a preparation method thereof. The polythiol epoxy resin curing agent uses cheap and accessible raw materials to greatly lower the cost of the polythiol epoxy resin fast curing agent. The preparation method comprises the following steps: after esterifying sorbitol, thioglycollic acid, p-toluenesulfonic acid and methylbenzene, distilling out the liquid under reduced pressure at uniform speed by controlling the temperature and vacuum degree until no liquid is distilled out, and adding epoxy resin to carry out chain extending reaction, thereby obtaining the polythiol epoxy resin curing agent. The polythiol epoxy resin curing agent is a colorless or light yellow transparent liquid poly-sulfhydryl epoxy grafted compound with certain viscosity, the pH value is 2-4, and the density is 1.2-1.3 g / cm<3>.

Description

technical field [0001] The invention relates to a curing agent, in particular to a polythiol epoxy resin curing agent and a preparation method thereof. Background technique [0002] Epoxy resin adhesive has good physical and chemical properties. It has excellent bonding strength to the surface of metal and non-metal materials, good dielectric properties, small shrinkage rate, good dimensional stability of products, high hardness and high flexibility. Good, excellent processing technology, stable to alkali and most solvents, so it is widely used in various sectors of national defense and national economy, and has a wide range of applications in casting, impregnation, lamination, adhesives, coatings, etc. Commonly used curing agents for epoxy resins mainly include amines, acid anhydrides, imidazoles, etc. [0003] The polythiol curing agent has a thiol group (-SH) at the end. When used alone, the activity is very poor, and the reaction is extremely slow at room temperature an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/66
Inventor 邹友思洪阿乐林华端吕耕敏蒲珏文尚明屹黄莺郑延清
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com