Nano semibright nickel plating solution

A technology of semi-bright nickel and electroplating solution, which is applied in the field of electroplating solution, which can solve the problems of large number of pores and poor compactness of semi-bright nickel coating, and achieve the effect of low number of pores, good dispersion ability and good corrosion resistance

Inactive Publication Date: 2012-03-21
HUZHOU JINTAI PLATING IND
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the invention is to solve the problems of poor density and large number of pores in the existing semi-bright nickel coating, and provide a coating that makes the coating bright and fine in crystallization, has low number of pores per unit area, good dispersion of plating solution, and can improve the performance of multilayer nickel coatings. Corrosive nano-semi-bright nickel plating process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of nano semi-bright nickel plating solution, its composition is composed of: nickel sulfate 250 g / L, nickel chloride 35 g / L, boric acid 40g / L, lanthanum oxide 1×10 -3 g / L, wetting agent 1mL / L, filling agent 0.2mL / L, softener 6mL / L, water balance.

Embodiment 2

[0021] A nano semi-bright nickel plating solution, its composition is: nickel sulfate 300 g / L, nickel chloride 50 g / L, boric acid 50 g / L, yttrium oxide 5×10 -3 , Wetting agent 3mL / L, leveling agent 1.0mL / L, softener 8mL / L, water balance.

Embodiment 3

[0023] A nano semi-bright nickel plating solution, its composition is: nickel sulfate 280 g / L, nickel chloride 45 g / L, boric acid 45 g / L, yttrium oxide 2×10 -3 , Yttria 5×10 -4 , wetting agent 2mL / L, leveling agent 0.6mL / L, softener 5mL / L, water balance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nano semibright nickel plating solution, which belongs to technical field of surface treatment, and the ingredient of the solution comprises: 250-300 g / L of nickel sulfate, 35-50 g / L of nickel chloride, 40-50 g / L of boric acid, 1*10-3-5*10-3g / L of rare earth oxide, wherein the rare earth oxide is lanthanum oxide and / or yttrium oxide, compared with the existing semibright nickel plating solution, the invention is better on the plating solution dispersibility, can cause the plating layer to be bright and have fine crystallization, is small on pore number unit area, and can improve multiplayer nickel corrosivity.

Description

technical field [0001] The invention relates to an electroplating solution, in particular to a nano semi-bright nickel electroplating solution. Background technique [0002] Semi-bright nickel is a commonly used intermediate layer in electroplating. In addition to achieving leveling, uniformity and flexibility, the coating must be as bright as possible, and the semi-bright nickel coating must have good compactness and fewer pores. Conducive to the corrosion resistance of multilayer nickel. In modern electroplating production, semi-bright nickel nickel plating occupies an important position as bright nickel nickel plating. The main purpose of semi-bright nickel is not decoration, but to improve the corrosion resistance of multi-layer nickel. The multi-layer nickel system composed of semi-bright nickel / high-sulfur nickel / bright nickel is anode sacrificial type. One of the important factors affecting the corrosion resistance of this system is bright nickel and semi-bright nic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/12
Inventor 倪孝平吴凡
Owner HUZHOU JINTAI PLATING IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com