Thick electrode with good electrochemical performance and preparation method thereof

An electrochemical and electrode technology, which is applied in the field of thick electrodes and its preparation, can solve the problems of reducing the electrochemical performance of the outer layer of the pole piece, unable to retain the electrolyte, etc., to solve the problem of concentration polarization, good electrochemical performance, and improve Effect of Magnification Performance

Active Publication Date: 2016-03-30
DONGGUAN AMPEREX TECH +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the charge-discharge cycle of the battery, the transmission of lithium ions in the electrode pole piece is from the outside (away from the current collector) to the inside (close to the current collector). The structural design of non-uniform porosity with reduced fluid direction, after a period of charging and discharging cycles, the outer layer of the electrode with small porosity cannot retain sufficient electrolyte for the transmission of lithium ions, so it will reduce the outer layer of the electrode. Continuous performance of layer electrochemical performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thick electrode with good electrochemical performance and preparation method thereof
  • Thick electrode with good electrochemical performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The production of the positive electrode sheet: the positive electrode active material lithium cobaltate (LiCoO 2 ), the conductive agent carbon black, the binder polyvinylidene fluoride (PVDF) and the solvent N-methylpyrrolidone (NMP) are uniformly mixed in a weight ratio of 92:3:5:80 to obtain the inner layer slurry to be coated ;The inner layer slurry is evenly coated on the aluminum foil current collector with a thickness of 14 microns, and then dried at 110°C, and the inner layer diaphragm with a coating thickness of about 150 microns is obtained after the first cold pressing treatment.

[0047] The positive electrode active material lithium cobaltate (LiCoO) coated with 0.6% aluminum oxide 2 ), carbon nanotubes, polyvinylidene fluoride (PVDF) and solvent N-methylpyrrolidone (NMP) in a weight ratio of 94:1.5:4.5:80 to uniformly mix the outer layer slurry to coat the baked The dried inner membrane is then dried at 110° C., and the outer membrane with a coating thic...

Embodiment 2

[0051] The production of the positive electrode sheet: the positive electrode active material lithium cobaltate (LiCoO 2 ), the conductive agent carbon black, the binder polyvinylidene fluoride (PVDF) and the solvent N-methylpyrrolidone (NMP) are uniformly mixed in a weight ratio of 92:3:5:80 to obtain the inner layer slurry to be coated ; The inner layer slurry is evenly coated on the aluminum foil current collector with a thickness of 14 microns, the thickness of the coating is about 150 microns, and then dried at 110° C. to obtain the inner membrane.

[0052] The positive electrode active material lithium cobaltate (LiCoO) coated with 0.6% aluminum oxide 2 ), carbon nanotubes, benzoic acid, polyvinylidene fluoride (PVDF) and solvent N-methylpyrrolidone (NMP) in a weight ratio of 92: 1.5: 1.5: 5: 80 to uniformly mix the outer layer slurry Coating on the baked inner membrane, the thickness of the coating is about 150 microns, and then drying at 110°C to obtain the outer memb...

Embodiment 3

[0056] The production of the positive electrode sheet: the positive electrode active material lithium cobalt oxide (LiCoO 2 ), the conductive agent carbon black, the binder polyvinylidene fluoride (PVDF) and the solvent N-methylpyrrolidone (NMP) are uniformly mixed in a weight ratio of 90:3:7:80 to obtain the inner layer slurry to be coated ; The inner layer slurry is evenly coated on an aluminum foil current collector with a thickness of 14 microns, the coating thickness is about 250 microns, and then dried at 110° C. to obtain an inner membrane.

[0057] The positive electrode active material lithium cobaltate (LiCoO) coated with 0.6% aluminum oxide 2 ), carbon nanotubes, benzoic acid, polyvinylidene fluoride (PVDF) and solvent N-methylpyrrolidone (NMP) in a weight ratio of 90:1.5:1.5:7:80 to uniformly mix the outer layer slurry Coating on the dried inner membrane, the thickness of the coating is about 300 microns, and then drying at 110°C to obtain the outer membrane, thus...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thick electrode with good electrochemical performance, which includes a current collector and an electrode membrane distributed on the current collector containing active materials and conductive materials. The electrode membrane includes an inner layer membrane close to the current collector and a The outer diaphragm of the current collector, the thickness of the electrode diaphragm is greater than 300 μm, the conductivity of the electrode diaphragm decreases from the inner diaphragm to the outer diaphragm, and the pores of the electrode diaphragm from the inner diaphragm to the outer diaphragm rate increase. The electrical conductivity of the inner membrane is relatively high, so that the electrons at the current collector can quickly enter or exit the inner membrane. The outer diaphragm has a large porosity, which can absorb more electrolyte, which solves the problem of poor electrolyte wettability caused by thick electrodes. In addition, the invention also discloses a method for preparing a thick electrode with good electrochemical performance.

Description

technical field [0001] The invention belongs to the field of lithium ion batteries, more specifically, the invention relates to a thick electrode with good electrochemical performance and a preparation method thereof. Background technique [0002] At present, with the continuous advancement of science and technology, the application field of lithium-ion batteries has also expanded rapidly, and has expanded from the initial portable mobile devices such as mobile phones and cameras to large electric devices with high power and high energy requirements such as electric bicycles and electric vehicles. Therefore, the requirements for the design and manufacturing process of lithium-ion batteries are getting higher and higher. [0003] Large-scale equipment such as electric bicycles and electric vehicles require lithium-ion batteries to have high energy density. From a design point of view, the ideal way to increase the energy density is to increase the content of active materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/13H01M4/139
CPCY02E60/10
Inventor 赵丰刚陈治汪颖许瑞郎野王娜
Owner DONGGUAN AMPEREX TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com