Oil well cement chlorine-free coagulation accelerating early strength agent

A technology for early-strength and oil-well cement, applied in the field of early-strength accelerators, can solve the problems of long induction period, unfavorable cement stone cementation, slow cement hydration speed, etc., achieve short transition time, prevent annular interface channeling flow, preventing micro-cracks

Active Publication Date: 2012-01-18
BC P INC CHINA NAT PETROLEUM CORP +2
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Temperature is one of the main factors affecting the hydration reaction of Portland cement. It mainly affects the hydration rate of cement, the properties, stability, and form of hydrates. Increasing the temperature can greatly accelerate the hydration rate of cement, but at low temperatures The hydration rate of cement is very slow, especially the induction period is long, which is not conducive to the cementation of cement stone. Therefore, it is necessary to adjust the performance of cement slurry by developing a low-temperature early-strength agent. The early-strength agent is added to the cement slurry for the purpose of Shorten the hardening time, the induction phase, or to accelerate the hardening process, the reaction acceleration phase and the reaction slowdown phase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil well cement chlorine-free coagulation accelerating early strength agent
  • Oil well cement chlorine-free coagulation accelerating early strength agent
  • Oil well cement chlorine-free coagulation accelerating early strength agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh various samples according to the following proportions:

[0035] Magnesium sulfate: triethanolamine: formamide: calcium formate: urea: naphthalenesulfonate = 1:0.1:0.1:2:1:0.5

[0036] Add the above-mentioned materials in turn in the mortar, pound into powder with a mortar stick, and mix evenly to make a coagulation accelerator and early strength agent. Use A01 as the coagulation accelerator and early strength agent code.

[0037] Table 1 Properties of cement slurry mixed with the accelerator and early strength agent under different test conditions

[0038]

Embodiment 2

[0040] Weigh various samples according to the following proportions:

[0041] Magnesium sulfate: triethanolamine: formamide: calcium formate: urea: naphthalenesulfonate = 2: 0.1: 0.1: 1: 1: 0.5

[0042] Add the above-mentioned materials in turn in the mortar, pound into powder with a mortar stick, and mix evenly to make a coagulation accelerator and early strength agent. Use A02 as the coagulation accelerator and early strengthening agent code.

[0043] Table 2 Properties of cement slurry mixed with the accelerator and early strength agent under different test conditions

[0044]

Embodiment 3

[0046] Weigh various samples according to the following proportions:

[0047] Magnesium sulfate: triethanolamine: formamide: calcium formate: urea: naphthalenesulfonate = 1.5: 0.1: 0.1: 2: 0.5: 0.5

[0048] Add the above-mentioned materials in turn in the mortar, pound into powder with a mortar stick, and mix evenly to make a coagulation accelerator and early strength agent. Use A03 as the coagulation accelerator and early strengthening agent code.

[0049] Table 3 Properties of cement slurry mixed with the accelerator and early strength agent under different test conditions

[0050]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an oil well cement chlorine-free coagulation accelerating early strength agent, which consists of the following components in parts by weight: 1.0-2.0 parts of sulfate, 0.05-0.10 part of triethanolamine, 0.05-0.10 part of formamide, 1.0-2.5 parts of calcium formate, 0.5-2.0 parts of urea and 0.5-1.0 part of naphthalene sulfonate, wherein the suitable temperature of the coagulation accelerating early strength agent is 20-45 DEG C; the coagulation accelerating early strength agent can be applied to cement slurry systems of various densities, has high compatibility with various additive systems and does not have influence on cement slurry performance; a product designed by the invention does not contain any chloride; the cement slurry thickening time can be shortened; the cement slurry stability is improved; the cement stone early strength is improved; the critical time is shortened; thus, water channeling after well cementation is effectively prevented; and the early strength agent can be matched with corresponding additive and admixture for use and can be widely applied to low-temperature shallow wells and adjustment well cementation construction.

Description

technical field [0001] The invention relates to a cement admixture used in the cementing field of oilfield well completion technology, which belongs to the coagulation accelerator and early strength agent. Background technique [0002] With the deepening of oil and gas exploration and development, there are more and more low-temperature shallow wells and offshore oil and gas drilling and cementing. Under low temperature conditions, on the one hand, due to the slow hydration rate and long waiting time of cement slurry, oil and gas water channeling is prone to occur during the waiting process, which affects interlayer isolation; on the other hand, due to the slow development of cement stone strength and low early strength , leading to an increase in the well construction cycle and reducing the economic benefits of oil and gas field exploration and development. This requires the use of low-temperature coagulation accelerators to accelerate the hydration rate of cement under lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/467
Inventor 邢秀萍谢承斌滕兆健李立荣霍明江
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com