Two-way stretch polypropylene film with functions of antibiosis and mildew resistance and preparation method thereof

A biaxially stretched film, anti-bacterial and anti-mildew technology, applied in the field of plastics, can solve the problems of silver-based anti-bacterial agents turning yellow, reducing anti-bacterial BOPP anti-bacterial timeliness, cumbersome steps, etc., to achieve good anti-bacterial and anti-mildew effects, good anti-bacterial Anti-mildew effect, good water resistance and stability

Active Publication Date: 2014-03-12
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent CN 2789254Y proposes a method for preparing an antibacterial BOPP film, which uses a polyamine and guanidinium polymer masterbatch, or uses a silver-containing composite masterbatch. The patent does not mention the use of Whether the polyamine and guanidinium salt polymer masterbatch is self-made or commercially available, but the guanidinium salt polymer is first made into a masterbatch and then made into a BOPP film. The steps are cumbersome and increase the cost. In addition, the silver-based antibacterial agent used in this patent The problem of yellowing will appear after long-term light or aging, and the patented BOPP film does not mention that it has anti-mildew properties
If polyguanidine is simply added to BOPP, there is still the disadvantage that polyguanidine is easy to precipitate in the BOPP film, especially in some applications with high humidity, which will reduce the antibacterial timeliness of antibacterial BOPP

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-way stretch polypropylene film with functions of antibiosis and mildew resistance and preparation method thereof
  • Two-way stretch polypropylene film with functions of antibiosis and mildew resistance and preparation method thereof
  • Two-way stretch polypropylene film with functions of antibiosis and mildew resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Weigh polyhexamethylene guanidine propionate (Shanghai Gaoju F3000) 21.0g (0.098mol), join in 200mL deionized aqueous solution, stir to make it dissolve; In addition, weigh sodium pyrithione (Hangzhou Wanjing NPT ) 20.0g (0.134mol), added to 200mL deionized water, stirred to dissolve; at room temperature (about 25°C), slowly pour polyhexamethylene guanidine propionate into the aqueous solution of sodium pyrithione In, and constantly stirring, after mixing completely, fully stir again 20 minutes, the product is dried, pulverizes, obtains the polyhexamethylene guanidine pyrithione salt (antibacterial and antifungal agent 1) that completely replaces.

Embodiment 2

[0059] Weigh polyhexamethylene biguanide hydrochloride (Shanghai Shande Industrial Co., Ltd. PHMB) 20g (0.091mol), join in 200mL aqueous solution, stir to make it dissolve; ) 35.0g (0.235mol), added to 200mL of water, stirred to dissolve; at 40°C, slowly pour polyhexamethylene biguanide hydrochloride into the aqueous solution of sodium pyrithione, and keep stirring, After the mixing is complete, stir fully for another 20 minutes, dry and pulverize the product to obtain a fully substituted polyhexamethylene biguanide pyrithione (antibacterial and antifungal agent 2).

Embodiment 3

[0061] Weigh 21.0g (0.133mol) of polyhexamethyleneguanidine hydrochloride (Shanghai Gaoju F1000), add it to 200mL aqueous solution, and stir to dissolve it; g (0.080mol), was added to 50mL of water, stirred to dissolve; at room temperature (about 25°C), the aqueous solution of sodium pyrithione was slowly poured into the polyhexamethyleneguanidine hydrochloride solution, And keep stirring, after the mixing is complete, then fully stir for 20 minutes, the product is dried and pulverized to obtain partially substituted polyhexamethyleneguanidine pyrithione (antibacterial and antifungal agent 3).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a two-way stretch polypropylene film with functions of antibiosis and mildew resistance and a preparation method, the polypropylene film comprises the following mixed components: 100 parts of polypropylene resin, 0.1-3 parts of anti mildew agent; an anti mildew agent is poly-guanidine pyrithione acid salt which is prepared by mixing poly-guanidine inorganic acid salt or an organic acid salt aqueous solution and a sodium pyrithione aqueous solution, wherein the mol ratio of guanidyl in the poly-guanidine to pyrithione acid salt is 1:(0.1-5); the polypropylene resin is specially used for BOPP. The method comprises the following steps: mixing or performing a melt blending to the components according to the proportion, casting into sheets, and then performing a two-way stretch to the polypropylene film with functions of antibiosis and mildew resistance. According to the invention, the BOPP film prepared by the invention has good effects of antibiosis and mildew resistance, and the components of antibiosis and mildew resistance is difficult to precipitate from the film, the invention has the advantages of good water resistance and stability as well as high transparency, so that the two-way stretch polypropylene film can be widely used.

Description

technical field [0001] The invention relates to the field of plastics, in particular to an antibacterial and antifungal polypropylene biaxially stretched film and a preparation method thereof. Background technique [0002] Polypropylene (PP) has the advantages of good mechanical properties, non-toxicity, heat resistance, chemical corrosion resistance, easy processing and low cost, etc., and has been more and more widely used in many fields. With the rapid development of the packaging industry, biaxially oriented polypropylene film (BOPP for short) has been widely used in the packaging of food, candy, fruit, etc. The rich nutrients in food can easily lead to the growth of microorganisms, resulting in food corruption, resulting in Waste, also can bring harm to health after people eat at the same time; In addition, along with the strengthening of people's hygiene consciousness, and the popular of multiple infectious diseases in recent years, to the articles for use in some publ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12B29C55/12
Inventor 李杰杨庆泉徐萌吕明福吕芸邹浩刘涛张洪波李魁张浩张丽英张师军
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products