Ethanol-soluble acrylic acid thermoplastic resin and preparation method thereof

A thermoplastic resin and acrylic technology, applied in application, coating, ink, etc., can solve the problems of poor wetting and dispersibility of pigments, influence on popularization and use, and high price, and achieve good printing suitability, fast drying, and less environmental hazards.

Inactive Publication Date: 2013-10-16
贺宏伟
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, although water-based and alcohol-soluble polyurethane plastic gravure inks and other types of alcohol-soluble inks have appeared in the market, there are problems such as high price, poor wetting and dispersibility of pigments, and slow drying, which affect the popularization and use of such products. As far as acrylic related resins and inks are concerned, only a few kinds of products are used in China, and there is no supply of such resins for full-chromatographic alcohol-soluble plastic gravure inks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An alcohol-soluble acrylic thermoplastic resin, comprising the following raw materials in the weight ratio: 20 parts of ethyl methacrylate, 50 parts of methyl acrylate, 10 parts of acrylic acid, 2 parts of glycidyl tertiary carbonate, N.N- ethyl diaminoacrylate 2 parts, 0.5 parts of azobisisobutyronitrile, 15 parts of rosin anhydride resin, and 0.5 parts of p-benzenemethanesulfonic acid. It is made by the following steps:

[0040] (1) Mix 10 parts of isopropanol and 45 parts of absolute ethanol and add them into the reaction kettle evenly to prepare a mixed solvent for subsequent use;

[0041] (2) Dissolve 20 parts of ethyl methacrylate, 50 parts of methyl acrylate, 10 parts of acrylic acid, 2 parts of glycidyl tertiary carbonic acid ester, 2 parts of ethyl N.N-diaminoacrylate, and 0.5 parts of azobisisobutyronitrile in In a mixed solution of 5 parts of isopropanol and 10 parts of absolute ethanol, a monomer mixed solution was prepared and placed in a high-level tank f...

Embodiment 2

[0045] An alcohol-soluble acrylic thermoplastic resin, including raw materials in the following weight ratio: 9.1 parts of butyl methacrylate, 50 parts of ethyl acrylate, 20 parts of β-hydroxyethyl acrylate, 5 parts of glycidyl tertiary carbonate, N.N-di 5 parts of ethyl aminoacrylate, 0.7 parts of benzoyl peroxide, 10 parts of maleic anhydride, 0.2 parts of terephthalic acid.

[0046] It is made by the following steps:

[0047] (1) Mix 10 parts of isopropanol and 45 parts of absolute ethanol and add them into the reaction kettle evenly to prepare a mixed solvent for subsequent use;

[0048] (2) 9.1 parts of butyl methacrylate, 50 parts of ethyl acrylate, 20 parts of β-hydroxyethyl acrylate, 5 parts of glycidyl tertiary carbonic acid ester, 5 parts of N.N-diaminoethyl acrylate, 0.7 parts of azobisisobutyronitrile Parts were dissolved in a mixed solution of 5 parts of isopropanol and 10 parts of absolute ethanol to obtain a monomer mixed solution, which was placed in a high-le...

Embodiment 3

[0052] An alcohol-soluble acrylic thermoplastic resin, comprising the following raw materials in the weight ratio: 28 parts of a 1:1 mixture of ethyl methacrylate and butyl methacrylate, 35 parts of butyl acrylate, 15 parts of acrylamide, glycidyl tertiary acid 4 parts of ester, 4 parts of N.N-ethyl diaminoacrylate, 0.6 part of azobisisobutyronitrile, 13 parts of polymerized rosin, and 0.4 part of p-benzenemethanesulfonic acid.

[0053] It is made by the following steps:

[0054] (1) Mix 10 parts of isopropanol and 45 parts of absolute ethanol and add them into the reaction kettle evenly to prepare a mixed solvent for subsequent use;

[0055] (2) 28 parts of ethyl methacrylate, butyl methacrylate 1:1 mixture, 35 parts of butyl acrylate, 15 parts of acrylamide, 4 parts of glycidyl tertiary carbonic acid ester, 4 parts of N.N-ethyl diaminoacrylate, Dissolve 0.6 parts of azobisisobutyronitrile in a mixed solution of 5 parts of isopropanol and 10 parts of absolute ethanol to prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An alcohol-soluble acrylic thermoplastic resin and a preparation method thereof. The resin comprises raw materials in the following weight ratio: 8-30 parts of methacrylate, 25-50 parts of acrylate, 10-20 parts of active functional group monomer, tertiary carbonic acid 2-5 parts of glycidyl ester, 2-5 parts of cationic functional monomer, 0.5-0.7 part of initiator, 10-15 parts of rosin addition polymer, and 0.2-0.5 part of catalyst. It has the characteristics of low pollution, low cost, good wetting and dispersibility of pigments, fast drying, and good printing suitability.

Description

technical field [0001] The invention relates to a synthetic resin and a preparation method thereof, in particular to a packaging resin material and a preparation method thereof. Background technique [0002] Alcohol-soluble acrylic thermoplastic resin is the main material used in printing inks for plastic packaging, and is also used in adhesives for composite packaging, and can be used for adhesives in paint production. The performance of its resin determines the solvent type of ink and coating, and determines the printing suitability of ink, pigment dispersibility, adhesion fastness, ink toxicity and environmental protection performance. For a long time, my country's plastic gravure ink is synthesized with benzene-soluble Resin is the main body, and the ink contains a large amount of benzene solvents. Therefore, there is volatilization pollution of benzene solvents during the manufacture and use of inks, which endangers the health of producers and consumers. What's more ser...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/14C08F220/18C08F220/06C08F220/34C08F220/28C08F222/06C08F220/56C09D11/10C09D133/08C09D11/107
Inventor 贺宏伟
Owner 贺宏伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap