Fireproofing agent capable of efficiently resisting sparks generated in electric welding and preparation method thereof

A technology of fire retardant and spark, applied in the direction of fire retardant coatings, etc., can solve the problems of serious environmental pollution, poor fire prevention effect, inconvenient use, etc., and achieve the effect of low price, good fire prevention effect and strong flame retardant ability

Inactive Publication Date: 2013-06-19
SHANGHAI INST OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] One of the purposes of the present invention is to provide a high-efficiency flame-retardant electric welding spark-proof agent for solving the problems of inconvenient use, poor fire-proof effect, and serious environmental pollution in the prior art. fire retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A high-efficiency flame-retardant fireproofing agent for sparks during electric welding, its composition is calculated as follows by weight percentage:

[0038] Sodium silicate 30.00g(20.00%)

[0039] Disodium hydrogen phosphate 9.00g(6.00%)

[0040] Titanium dioxide 2.31g (1.54%)

[0041] Chalk powder 0.84g (0.56%)

[0042] Sodium dodecyl sulfonate 2.85g (1.90%)

[0043] Water 105g(70.00%)

[0044] The preparation method of the above-mentioned high-efficiency flame-retardant electric welding spark fireproofing agent comprises the steps:

[0045] (1) Mix 30.00g (20.00%) sodium silicate with 105g (70.00%) water, and control the stirring speed at 800-1000 / min until the solid is completely dissolved;

[0046] (2) After the solid in step (1) is completely dissolved, add 9.00g (6.00%) disodium hydrogen phosphate, and stir at room temperature for 15-20min at a stirring speed of 800-1000r / min to make it evenly mixed;

[0047] (3) Add 0.84g (0.56%) chalk powder and 2.31g ...

Embodiment 2

[0051] A high-efficiency flame-retardant fireproofing agent for sparks during electric welding, its composition is calculated as follows by weight percentage:

[0052] Sodium silicate 35.00g(23.95%)

[0053] Disodium hydrogen phosphate 7.21g(4.93%)

[0054] Titanium dioxide 1.70g (1.16%)

[0055] Chalk powder 0.40g (0.27%)

[0056] Sodium dodecyl sulfonate 1.80g (1.23%)

[0057] Water 100.00g (100ml) (68.44%)

[0058] The preparation method of the above-mentioned high-efficiency flame-retardant electric welding spark fireproofing agent comprises the steps:

[0059] (1) Mix 35.00g (23.95%) sodium silicate with 100ml (68.44%) water, and control the stirring speed at 800-1000 / min until the solid is completely dissolved;

[0060] (2) After the solid in step (1) is completely dissolved, add 7.21g (4.93%) disodium hydrogen phosphate, and stir at room temperature for 15-20min at a stirring speed of 800-1000r / min to make it evenly mixed;

[0061] (3) Add 0.40g (0.27%) chalk powd...

Embodiment 3

[0065]A high-efficiency flame-retardant fireproofing agent for sparks during electric welding, its composition is calculated as follows by weight percentage:

[0066] Sodium silicate 36.00g(28.00%)

[0067] Disodium hydrogen phosphate 9.15g(7.12%)

[0068] Titanium dioxide 1.40g(1.09%)

[0069] Chalk powder 0.41g (0.32%)

[0070] Sodium dodecyl sulfonate 1.95g (1.52%)

[0071] Water 79.65g (61.95%)

[0072] (1) Mix 36.00g (28.00%) sodium silicate with 79.65ml (61.95%) water, and control the stirring speed at 800-1000 / min until the solid is completely dissolved;

[0073] (2) After the solid in step (1) is completely dissolved, add 9.15g (7.12%) disodium hydrogen phosphate, and stir at room temperature for 15-20min at a stirring speed of 800-1000r / min to make it evenly mixed;

[0074] (3) Add 0.41g (0.32%) chalk powder and 1.40g (1.09%) titanium dioxide, add 1.95g (1.52%) sodium dodecylsulfonate and continue stirring for 25 minutes to completely dissolve the solid;

[0075...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-efficiency fire retardant for flame-retardant sparks during electric welding and a preparation method thereof. Its raw material components are calculated by weight percentage from 20% to 28% sodium silicate, 5% to 9% disodium hydrogen phosphate, 1% to 2% titanium dioxide, 0.2% to 0.6% chalk powder, 1% to 2% sodium dodecyl sulfonate and 60%~70% water. The preparation method is to mix sodium silicate with water, stir until the solid is completely dissolved, then add disodium hydrogen phosphate, stir to make it evenly mixed, add chalk powder and titanium dioxide, then add sodium dodecylsulfonate and continue stirring to make the solid completely Dissolved, and the resulting reactant was cooled to room temperature to obtain a high-efficiency flame-retardant fireproofing agent for sparks during electric welding of the present invention. The present invention has a high-efficiency fire retardant for flame-retardant sparks during electric welding, which can be used as a spray-type portable reagent. At the same time, the reagents used in this solution are basically inorganic reagents, which not only have good fire prevention effect, but also are low in price and are environmentally friendly and harmless.

Description

technical field [0001] The invention relates to a high-efficiency fire retardant for flame-retardant sparks during electric welding and a preparation method thereof. Background technique [0002] The fire protection methods generally used in the market are as follows: [0003] (1) Use fire-resistant coatings for fire prevention. This method can only be applied to fixed places such as walls, doors and windows of some buildings, and it is not easy to move; [0004] (2) Flame retardant materials are fireproof. This is a new type of high-tech product, and the price is very expensive. Not every household can afford it. fit. [0005] (3) Add flame retardant additives. This method is only suitable for adding to plastics and has relatively large limitations. Generally, chlorine and bromine are the majority, and these organic compounds have great pollution to the environment; [0006] (4) Install fire alarm system. This is a method that is more suitable for use in prosperous bui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K21/02
Inventor 何奇胜方人杰陶伟赵欣周祖新
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap