Surface treating agent applicable to toy plastic material and preparation method thereof

A technology for surface treatment agents and plastic materials, applied in chemical instruments and methods, ampholytes/electroneutral surface active compounds, detergent compounding agents, etc., can solve problems such as high cost, non-environmental protection, and affecting the health of operators. Achieve the effect of low cost, good coating effect and good decontamination effect

Active Publication Date: 2012-07-04
ZHONGSHAN YONGHUI CHEM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Currently on the market, organic solvents (white oil, alcohol or isopropanol and other organic solvents) are mainly used to clean the plastic surface. The advantage is that the cleaning is relatively clean, and the solubility of the organic solvent can be adjusted according to different substrates; the disadvantage is that the cost is high. Not environmentally friendly, affecting the health of operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The surface treatment agent of the present embodiment, its raw material formula is made up of each component of following percentage by weight:

[0035] Sodium laureth sulfate 0.2~0.4%;

[0036] Disodium lauryl sulfosuccinate 0.2~0.5%;

[0037] Lauryl amidopropyl hydroxysultaine 0.2~0.5%;

[0038] Cocamide MEA 0.05~0.1%;

[0039] Polyquaternium-7 0.05~0.1%;

[0040] Dilute phosphoric acid 3-8%;

[0041] Disodium EDTA 0.5~1%;

[0042] DMDM hydantoin 0.25~0.3%;

[0043] The balance is deionized water.

[0044] The above-mentioned substances are all commercially available products, and dilute phosphoric acid is commercially available reagent grade.

[0045] The preparation method of present embodiment surface treatment agent is:

[0046] According to the raw material formula of the surface treatment agent above, sodium lauryl polyether sulfate, disodium lauryl sulfosuccinate, lauryl amidopropyl hydroxy sulfobetaine, cocamide MEA, polyquaternium-7, EDTA The disodiu...

Embodiment 2

[0048] The surface treatment agent of the present embodiment, its raw material formula is made up of each component of following percentage by weight:

[0049] Sodium laureth sulfate 0.05~0.1%;

[0050] Disodium lauryl sulfosuccinate 0.05~0.1%;

[0051] Lauryl amidopropyl hydroxysultaine 0.1~0.15%;

[0052] Cocamide MEA 0.1~0.15%;

[0053] Polyquaternium-7 0.15~0.2%;

[0054] Dilute phosphoric acid 8-15%;

[0055] Disodium EDTA 0.3~0.4%;

[0056] DMDM hydantoin 0.3~0.4%;

[0057] The balance is deionized water.

[0058] The above-mentioned substances are all commercially available products, and dilute phosphoric acid is commercially available reagent grade.

[0059] The preparation method of surface treatment agent of the present invention is:

[0060] According to the raw material formula of the surface treatment agent above, sodium lauryl polyether sulfate, disodium lauryl sulfosuccinate, lauryl amidopropyl hydroxy sulfobetaine, cocamide MEA, polyquaternium-7, EDTA Th...

Embodiment 3

[0062] The surface treatment agent of the present embodiment, its raw material formula is made up of each component of following percentage by weight:

[0063] Sodium laureth sulfate 0.1~0.2%;

[0064] Disodium lauryl sulfosuccinate 0.1~0.2%;

[0065] Lauryl amidopropyl hydroxysultaine 0.05~0.1%;

[0066] Cocamide MEA 0.15~0.2%;

[0067] Polyquaternium-7 0.2~0.3%;

[0068] Dilute phosphoric acid 15-20%;

[0069] Disodium EDTA 0.1~0.3%;

[0070] DMDM hydantoin 0.2~0.25%;

[0071] The balance is deionized water.

[0072] The above-mentioned substances are all commercially available products, and dilute phosphoric acid is commercially available reagent grade.

[0073] The preparation method of present embodiment surface treatment agent is:

[0074] According to the raw material formula of the surface treatment agent above, sodium lauryl polyether sulfate, disodium lauryl sulfosuccinate, lauryl amidopropyl hydroxy sulfobetaine, cocamide MEA, polyquaternium-7, EDTA The dis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a surface treating agent applicable to a toy plastic material and a preparation method thereof. The raw material formula of the surface treating agent consists of sodium laureth sulfate, laurinol disodium stearamido measulfosuccinate, lauramide propyl gydroxysulfobetaine, cocamide MEA, polyquaternium-7, ethylenediaminetetraacetic acid disodium salt, 1,3-dihydromethyl-5,5-dimethyl hydantion and dilute phosphoric acid. The surface treating agent can be applied to performing surface pretreatment on toy plastic materials such as acrylonitrile butadiene styrene (ABS) / polyvinyl chloride (PVC) and the like before coating. In the formula of the surface treating agent, environment-friendly materials are adopted completely, so the discharging quantity of volatile organic compounds (VOC) is close to 0. Compared with the traditional solvent type clean treating agent, the surface treating agent has better cleaning effect and better coating effect of the coating. The surfacetreating agent has a simple preparation method and low cost of the raw material formula, and can meet requirements of toy manufacturers and requirements of national low-carbon economy.

Description

technical field [0001] The invention relates to a surface treatment process of plastic materials, in particular to a surface treatment agent suitable for toy plastic materials and a preparation method thereof. Background technique [0002] At present, the vast majority of the toy market uses plastic materials such as ABS\PVC, and paints are used to present the ornamental properties of toys. The first step is crucial. [0003] ABS (acrylonitrile-butadiene-styrene copolymer), which is a thermoplastic resin plastic material, has strong mechanical properties and processing properties. When painting, problems such as poor adhesion, loss of gloss and pitting often occur. The main reasons are: the surface tension is less than 100Mm / cm, the solubility parameters are quite different from the solubility parameters of the resin and solvent in the paint, the surface is prone to static electricity and dust absorption during molding, and the stripping method used for easy demoulding duri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C11D1/94C11D3/30C11D3/60
Inventor 叶凤麒朱振亚
Owner ZHONGSHAN YONGHUI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap