Impregnating compound for basalt fiber filter felt

A technology of basalt fiber and filter felt, which is applied in fiber processing, textiles and papermaking, etc., can solve the problems of poor working environment of basalt fiber filter felt, achieve the effects of reduced high-temperature loss rate, good anti-static performance, and improved product performance

Active Publication Date: 2012-09-26
SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a basalt fiber filter felt wetting agent with high temperature resistance and antistatic performance, so as to overcome the problem of the harsh working environment of the basalt fiber filter felt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Impregnating compound for basalt fiber filter felt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Graphite emulsion 20% solids 5%

[0015] 60% solids PTFE solution 8%

[0016] 60% Solids Silicone Oil Emulsion (SE-2203) 5%

[0017] 30% solids polyacrylate emulsion (LI-3) 4%

[0018] water balance

Embodiment 2

[0020] Graphite emulsion at 20% solids 6%

[0021] 60% solids PTFE solution 10%

[0022] 60% Solids Silicone Oil Emulsion (SE-2203) 6%

[0023] 30% solids polyacrylate emulsion (LI-3) 5%

[0024] water balance

[0025] The following are the test results: (all in percent)

[0026]

[0027] It can be seen from the detection results that after the surface of the basalt fiber filter felt is coated with the present invention, the high temperature loss rate of the basalt fiber filter felt is greatly reduced, and the high temperature resistance performance is greatly improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature filter felt impregnating compound with high temperature resistance and antistatic property, which is particularly suitable for a basalt fiber filter felt. The invention aims to provide a high temperature-resistant and antistatic impregnating agent for the basalt fiber filter felt to solve the problem that the working environment of the basalt fiber filter felt is severe. The technical scheme is that: the impregnating agent for the basalt fiber filter felt comprises the following components in percentage by weight: 5 to 6 percent of graphite emulsionwith the solid content of 20 percent, 8 to 10 percent of PTFE solution with the solid content of 60 percent, 4 to 6 percent of silicone emulsion with the solid content of 60 percent, 3 to 5 percent of polyacrylate with the solid content of 30 percent, and the balance of water. After the impregnating compound is coated on the basalt fiber filter felt, the basalt fiber filter felt has good high temperature resistance and antistatic property. Actual detection proves that the heat loss of the basalt fiber filter felt produced by the formula is greatly reduced, and the product performance is greatly improved.

Description

technical field [0001] The invention relates to a high temperature filter felt sizing agent with high temperature resistance and antistatic properties, which is especially suitable for basalt fiber filter felt. Background technique [0002] At present, basalt fiber filter felt is a brand-new filter material, and there is no special sizing agent for post-treatment. Because basalt fiber filter felt is generally used in transportation, construction, petrochemical and other fields, the working environment is relatively harsh, and the performance requirements for high temperature resistance and anti-static are relatively high. Therefore, a sizing agent is needed to improve the high temperature resistance and antistatic properties of the basalt fiber filter felt and prolong its service life. SUMMARY OF THE INVENTION [0003] The technical problem to be solved by the present invention is to provide a basalt fiber filter felt sizing agent with high temperature resistance and anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/256D06M15/643D06M15/263D06M11/74
Inventor 李大福王玉华张茂奎
Owner SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com