Method for preparing high-efficiency composite humidifying paper

A moisture-regulating paper and high-efficiency technology, applied in special paper, paper, papermaking, etc., can solve the problems of uneven distribution of sepiolite, unfavorable packaging use, loss of raw materials, etc., to achieve diversified application methods, low cost, and breakage resistance The effect of increased intensity

Inactive Publication Date: 2011-12-07
ZHEJIANG SCI-TECH UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN200910101495.6 provides a preparation method of museum micro-environment humidity-conditioning paper, which is used for cultural relics packaging, but the humidity-conditioning paper made by adding polyethylene glycol into pulp will become hard, which is not conducive to packaging use, and the sea The physical addition of sepiolite can easily cause the loss of raw materials during the papermaking process, and there is a defect that sepiolite is unevenly distributed in the paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-efficiency composite humidifying paper
  • Method for preparing high-efficiency composite humidifying paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of high-efficiency composite humidity-conditioning paper is characterized in that the following steps are adopted:

[0017] A) Get 15 parts of dry pulp by mass parts, 10 parts of acrylamide, 5.5 parts of sodium polyacrylate, 5.5 parts of carboxymethyl cellulose, 7 parts of sepiolite with a particle size of 100 mesh, 0.08 part of potassium persulfate, 0.015 part of N , N′-methylenebisacrylamide, added to 100 parts of water, and stirred and reacted for 5 hours at a temperature of 80° C., to obtain composite pulp;

[0018] B) dissociating the composite pulp in a fiber disintegrator to obtain pulp raw materials;

[0019] C) Paper pulp raw materials are directly made in a paper machine and dried to obtain high-efficiency composite humidity-controlling paper.

Embodiment 2

[0021] A preparation method of high-efficiency composite humidity-conditioning paper is characterized in that the following steps are adopted:

[0022] A) Get 20 parts of dry pulp by mass parts, 10 parts of acrylamide, 5.5 parts of sodium polyacrylate, 5.5 parts of carboxymethyl cellulose, 7 parts of sepiolite with a particle size of 100 mesh, 0.08 part of potassium persulfate, 0.015 part of N , N'-methylenebisacrylamide, added to 100 parts of water, at a temperature of 70 ° C, stirred and reacted for 4 hours to obtain composite pulp;

[0023] B) dissociating the composite pulp in a fiber disintegrator to obtain pulp raw materials;

[0024] C) Paper pulp raw materials are directly made in a paper machine and dried to obtain high-efficiency composite humidity-controlling paper.

Embodiment 3

[0026] A preparation method of high-efficiency composite humidity-conditioning paper is characterized in that the following steps are adopted:

[0027] A) Get 25 parts of dry pulp by mass parts, 10 parts of acrylamide, 5.5 parts of sodium polyacrylate, 5.5 parts of carboxymethyl cellulose, 7 parts of sepiolite with a particle size of 100 mesh, 0.08 part of potassium persulfate, 0.015 part of N , N'-methylene bisacrylamide, added to 100 parts of water, at a temperature of 60 ° C, stirred and reacted for 3 hours to obtain composite pulp;

[0028] B) dissociating the composite pulp in a fiber disintegrator to obtain pulp raw materials;

[0029] C) Paper pulp raw materials are directly made in a paper machine and dried to obtain high-efficiency composite humidity-controlling paper.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing high-efficiency composite humidifying paper. The method is characterized in that: a copolymerization reaction of sodium polyacrylate, carboxymethylcellulose, sepiolite, acrylamide and paper pulp is performed so as to obtain composite paper pulp, and the composite paper pulp is subjected to papermaking to form paper. Compared with the prior art, the method has the advantages that 1) the moisture content of the humidifying paper is high, and the humidifying rate is quick; 2) the relative humidity of microenvironment can be regulated to be between 50 and 60 percent within short time, and is maintained within the humidity range for a long time; 3) the preparation method is simple, the cost is low, paper materials are light, and application modesare diversified; and 4) compared with that of raw paper, the bursting strength of the composite humidifying paper is increased by over 50 percent.

Description

technical field [0001] The invention relates to a polymer functional material, in particular to a preparation method of high-efficiency composite humidity-conditioning paper. Background technique [0002] Energy-saving, environmentally friendly, and green ecological smart materials are attracting more and more attention. Among them, the research on humidity-controlling functional materials has gradually shifted from the research of traditional inorganic salts, silica gel, and inorganic minerals to the research of porous resins, organic-inorganic composites, and biomass materials. Mainly using the porous structure of inorganic minerals and the high moisture content of organic polymers, as well as the large amount of moisture-absorbing guiding groups in biomass, studies have proved that cellulose-based materials have better moisture-regulating properties than sodium acrylate and perlite, and porous minerals can Effectively use its own porous structure to absorb and dehumidify....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21H17/55
Inventor 杨海亮胡智文覃崬益彭志勤
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com