Method for firing domestic porcelain

A porcelain and daily-use technology, which is applied in the firing field of high-grade daily-use porcelain such as bowls and cups, can solve problems such as deformation, and achieve the effects of light shape, convenient operation, and high rate of high-quality products

Active Publication Date: 2012-10-17
FUJIAN DEHUA JIASHUN CRAFTS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to overcome the deformation problem of daily-use porcelain in the prior art during the firing process, and provide a firing method for high-grade daily-use porcelain that is simple and convenient, and the shape of the fired product is light.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for firing domestic porcelain
  • Method for firing domestic porcelain
  • Method for firing domestic porcelain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment one builds the firing of " white porcelain " rice bowl

[0023] Step 1: Take 10kg of "Jianbai Porcelain" clay that has been vacuum-fired;

[0024] Step 2, making 10 green bodies of the rice bowl with the female die roll forming;

[0025] Step 3, after trimming, buckle it on the cake pad and dry it;

[0026] Step 4, put the green body into the kiln and biscuit once at a low temperature of 900°C;

[0027] Step 5: After polishing the biscuit body, evenly apply a layer of "Jianbai Porcelain" glaze on the front and back sides of the body;

[0028] Step 6: Use a damp sponge to carefully wipe off the glaze layer on the edge of the bowl and the bottom foot;

[0029] Step 7, smoothing the surface of the silicon carbide refractory shed plate coated with alumina paint;

[0030] Step 8, carefully turn the glaze body upside down on the refractory shed, pay attention not to touch the bowls, and leave a proper gap;

[0031] Step 9: According to the firing curve tempera...

Embodiment 2

[0034] In step 12, after cooling, the finished product can be obtained, and the high-quality product rate of the finished product is 90%, and the qualified rate is 100%. The firing of embodiment two high-grade teacups

[0035] Step 1, take 15kg of porcelain clay that has been vacuum-fired;

[0036] Step 2, make 20 green bodies of teacups with female mold roll forming;

[0037] Step 3, after trimming, buckle it on the cake pad and dry it;

[0038] Step 4, put the body into the kiln and biscuit once at a low temperature of 850°C;

[0039] Step five, after polishing the biscuit body, apply a layer of enamel evenly on both sides of the body;

[0040] Step 6, use a damp sponge to carefully wipe off the glaze layer on the edge of the cup and the bottom foot;

[0041] Step 7, smoothing the surface of the silicon carbide refractory shed plate coated with alumina paint;

[0042] Step 8, carefully turn the glaze body upside down on the refractory shed board, pay attention not to to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for firing a domestic porcelain, in particular to the method for firing high-grade domestic porcelains, such as bowels and cups. The method comprises the following steps of: 1, drying a finished body, placing the body into a kiln to perform biscuit firing at the low temperature of 800 to 900 DEG C, and polishing the biscuit-fired body to smooth; 2, glazing the biscuit-fired body and removing glaze at the mouth rim and foot of the product; 3, directly placing the product on a refractory slab in a reversing way for primary high-temperature glaze firing; and 4, turning the product over, cleaning and partially glazing the mouth rim of the product, placing the product into the kiln again in an erecting way for secondary high-temperature glaze firing, and cooling the product to obtain the finished product. Compared with the conventional low-temperature biscuit-firing high-temperature glaze-firing method or high-temperature biscuit-firing low-temperature glaze-firing method, the method is convenient to operate, ensures the light weight and high superior quality rate of the fired finished product, and is very applied to the production of various high-grade domestic porcelain products, such as the bowels and the cups.

Description

technical field [0001] The invention relates to a firing method of daily-use porcelain, in particular to a firing method of high-grade daily-use porcelain such as bowls and cups. Background technique [0002] Over the years, in order to solve the deformation problem of daily-use porcelain, a large number of ceramic scientific and technological workers and production enterprises have carried out a large number of experiments and research work, and the whole process of production from ceramic mud formulation, molding, drying to firing is controlled. In addition to being harmonious and beautiful in the design of the device type, it is generally necessary to add a thickened edge to the edge of the mouth of the cup, dish and dish; in terms of firing, the currently commonly used firing methods mainly include low-temperature plain firing There are two forms of high-temperature glaze firing and high-temperature plain firing and low-temperature glaze firing, but both have advantages ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/622C04B33/24
Inventor 苏志强苏志坚
Owner FUJIAN DEHUA JIASHUN CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com