Light color roofing decorative tile

A colorful and light-weight technology, applied to roofs, roof coverings, and roofs using tiles/slate tiles, etc., can solve the problems of unsightly tiles and achieve light weight, stable performance, and long service life.

Inactive Publication Date: 2010-12-29
高俊荣
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Also, existing tiles are not aesthetically pleasing, so there is a need to improve existing tiles to meet the increasing demands of the construction industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Lightweight colored roof decorative tiles are prepared from the following raw materials in proportions by weight: magnesium oxide powder: cement: polyamide curing agent: red iron oxide: pearlescent pigment powder: bentonite: color paste: water = 65:48: 3:6:8:37:4:135.

[0014] The method for manufacturing the light-weight colored roof decorative tiles comprises the following steps:

[0015] (1), preparation of fabric: after selecting raw materials according to the above parts by mass, mix magnesium oxide powder, pearlescent pigment powder, iron oxide red with color paste and water, then add polyamide curing agent and stir evenly for subsequent use;

[0016] (2), preparation of back material: after selecting material according to above-mentioned raw material variety specification, bentonite is mixed with cement, water, then add polyamide solidifying agent and stir evenly for subsequent use;

[0017] (3) Select a flat surface and spread a layer of polyester film. After f...

Embodiment 2

[0019] The light-weight colored roof decorative tile is characterized in that it is prepared from the following raw materials in parts by weight: magnesium oxide powder: cement: polyamide curing agent: red iron oxide: pearlescent pigment powder: bentonite: color paste: water=75 :50:1:3:5:33:2:120. Embodiment 1 of the method for manufacturing light-weight colored roof decorative tiles.

Embodiment 3

[0021] Lightweight colored roof decorative tiles are prepared from the following raw materials in proportions by weight: magnesium oxide powder: cement: polyamide curing agent: iron oxide red: pearlescent pigment powder: bentonite: color paste: water = 60:46: 4:5:15:40:3:140. Embodiment 1 of the method for manufacturing light-weight colored roof decorative tiles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the construction and decoration industry, in particular to a light color roofing decorative tile. The light color roofing decorative tile is characterized by comprising the following raw materials in parts by weight: 55-75 parts of magnesium oxide powder, 50-60 parts of cement, 1-5 parts of polyamide curing agent, 3-9 parts of iron oxide red, 5-12 parts of pearlescent pigment powder, 33-43 parts of bentonite, 2-6 parts of color paste and 120-150 parts of water. The light color roofing decorative tile has the advantages of stable performance, innocuity and pollution-free environment, endurable color and luster, long service life, low cost, good rigidity, good toughness and light weight. The various-color tile can be cooperatively matched with a building exterior wall, thus being ideal light color roofing decorative tiles for the building industry.

Description

technical field [0001] The invention relates to a construction and decoration industry, in particular to a light-weight colored roof decorative tile. Background technique [0002] With the delisting of modern earth-fired tiles, although the cost of cement tiles is low enough, they lack sufficient weather resistance, and often crack and peel off, which has become a major problem for developers, especially for high-rise buildings. The harm caused by the peeling off of the skin is not just the worry about waterproofing. With the renovation of old houses in China, there is a demand for flat to slope conversion and energy-saving renovation. In addition, existing tiles are unattractive and there is a need to improve existing tiles to meet the increasing demands of the construction industry. Contents of the invention [0003] The present invention is proposed in view of the problems in the above-mentioned prior art, and its purpose is to provide a light-weight colored roof deco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04D1/00C04B28/10
Inventor 高俊荣
Owner 高俊荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com