Foamed micropore layer of artificial leather for lining of PE shoes and method for preparing artificial leather by using same
A technology of artificial leather and microporous layer, which is applied in the field of artificial leather to achieve the effect of high foaming ratio, low stiffness and high stiffness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0060] The raw material ratio of PE-shoe lining artificial leather foamed microporous layer of the present invention: expressed in parts by weight, 100 parts of polyethylene PE, 28 parts of ethylene-vinyl acetate copolymer EVA, 55 parts of styrene-butadiene copolymer SBS , active CaCO 3 85 parts, 6 parts of azodicarbonamide Ac, 3 parts of zinc oxide ZnO, 2 parts of titanium dioxide, 3 parts of dicumyl peroxide DCP and 1.8 parts of antioxidant (1.8 parts of antioxidant is made of thiodipropyl Dilauryl acid DLTP 0.5 parts, antioxidant 10100.5 parts and antioxidant 2640.8 parts).
[0061] Active CaCO used in the raw material of PE-shoe lining artificial leather foaming microporous layer of the present invention 3 The fineness is 200-500 mesh.
[0062] Active CaCO 3 The treatment method of this method: prepare light calcium carbonate and titanate coupling agent (3-aminopropyltrimethoxysilane) in a ratio of 100:0.3 by weight, add it to a high-speed mixer, and heat it at a temper...
Embodiment 2
[0069] Embodiment 2: basically the same as Embodiment 1, the difference is:
[0070] The raw material ratio of PE-shoe lining artificial leather foamed microporous layer of the present invention: expressed in parts by weight, 100 parts of polyethylene PE, 30 parts of ethylene-vinyl acetate copolymer EVA, 53 parts of styrene-butadiene copolymer SBS , active CaCO 3 90 parts, 6.5 parts of azodicarbonamide Ac, 3 parts of zinc oxide ZnO, 2 parts of titanium dioxide, 3 parts of dicumyl peroxide DCP and 1.8 parts of antioxidant (1.8 parts of antioxidant is made of thiodipropyl 0.5 part of dilauryl DLTP, 0.5 part of antioxidant 1010 and 2640.8 parts of antioxidant).
[0071] Active CaCO 3 The treatment method: light calcium carbonate and titanate coupling agent (3-aminopropyltriethoxysilane) are prepared in a ratio of 100:0.5 by weight, and added to a high-speed mixer, at a temperature of Mix at 60°C for 30 minutes at a speed of 2000r / min. After mixing, it becomes active light calc...
Embodiment 3
[0077] Embodiment 3: basically the same as Embodiment 1, the difference is:
[0078] The raw material ratio of PE-shoe lining artificial leather foamed microporous layer of the present invention: expressed in parts by weight, 100 parts of polyethylene PE, 26 parts of ethylene-vinyl acetate copolymer EVA, 53 parts of styrene-butadiene copolymer SBS , active CaCO 3 80 parts, 6 parts of azodicarbonamide Ac, 3 parts of zinc oxide ZnO, 2 parts of titanium dioxide, 3 parts of dicumyl peroxide DCP and 1.8 parts of antioxidant (1.8 parts of antioxidant is made of thiodipropyl 0.5 part of dilauryl DLTP, 0.5 part of antioxidant 1010 and 2640.8 parts of antioxidant).
[0079] Active CaCO 3 The treatment method: prepare light calcium carbonate and titanate coupling agent (vinyl triethoxysilane) at a ratio of 100:0.1 by weight, add it to a high-speed mixer, and heat it at a temperature of 55°C , mixed for 35 minutes at a rotating speed of 2000r / min, after mixing, it will be active light...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com