Nylon 6 special for low-noise, self-lubricated wear-resisting injection molding gear and preparation process thereof

A self-lubricating, injection-molding technology, applied in belts/chains/gears, components with teeth, portable lifting devices, etc., can solve the problems of uncertainty in the performance of finished products, high material costs, and troubles for exporting companies. The effect of improving comprehensive competitiveness, convenient production and procurement, and low cost

Inactive Publication Date: 2010-08-04
KECHUANG POLYMER SUZHOU
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it has caused serious troubles to many export enterprises in my country.
At the same time, since nylon 6 is a crystalline material, it is easy to generate large internal stress during molding, which leads to uncertainty in the performance of the finished product
At the same time, for components such as gears, the many advantages of ordinary nylon 6 are favored by designers, but the above shortcomings are very troublesome, especially when it comes to the requirement that the friction sound generated during gear operation can be effectively and greatly reduced. At the same time, the raw material It has strong wear resistance and can be used under harsh conditions where the temperature is sometimes high and sometimes low
The raw materials with the above functions currently available on the market are either expensive such as nylon 12, or are added with expensive additive materials such as polytetrafluoroethylene, which also leads to high material costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Embodiment 1 provides a low-noise, self-lubricating and wear-resistant nylon 6 for injection-molded gears, which is composed of the following components by weight: nylon 6: 52%; cross-linking wear-resistant agent: 22%; nylon 6 powder: 22% , antioxidant: 1.0%; heat stabilizer: 2.0%; other additives: 1.0%.

[0010] First dry nylon 6, nylon 6 powder and cross-linking wear-resistant agent at 85 degrees and 60 degrees respectively, then weigh them with antioxidants, heat stabilizers and other additives in proportion and mix them in a mixer at a low speed for 10 Minutes, the mixer adopts low-speed mixing, the gap between the mixing blade and the cylinder wall should be less than 0.5 cm, the mixing effect of raw and auxiliary materials should be visually observed that the various particles and powders are basically uniform, and there are no obvious agglomerates or agglomerations; the twin-screw extruder uses 40 long Diameter ratio, medium-strength shearing; the water-cooled st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an organic polymer composite material, in particular to a nylon 6 special for a low-noise, self-lubricated wear-resisting injection molding gear and a preparation method thereof. The nylon 6 consists of the following components in percentage by weight: 49.5-90 percent of nylon 6, 3-35 percent of cross-linking wear-resisting agent, 3-35 percent of nylon 6 powder, 0.3-1.5 percent of antioxidant, 0.3-3.0 percent of heat stabilizer and 0.3-5.5 percent of other addition agents. By the nylon 6 special for the low-noise, self-lubricated wear-resisting injection molding gear and the preparation method thereof, gears with different sizes can be rapidly produced by adopting an injection molding mode; the gear produced by the material has the characteristic of effectively eliminating noise when being used together with a metal gear, simultaneously has better self-lubricating and wear resisting performances and cannot fall off powder dust caused by wear, thereby providing longer service life.

Description

technical field [0001] The invention relates to an organic polymer composite material, and more specifically relates to a low-noise self-lubricating and wear-resistant nylon 6 special for injection molding grade gears and a preparation method thereof. Background technique [0002] Nylon 6 is one of the most widely used engineering plastics. Its amide group is polar and has a strong hydrogen bond in its structure, which makes nylon 6 have a high melting point and good physical and mechanical properties. And wear resistance and self-lubricating properties, these comprehensive characteristics are not available in other plastics. However, ordinary nylon 6 has high water absorption, low impact strength before water absorption, sharp drop in rigidity after water absorption, and unstable dimensions, which limit the application of nylon 6, which in turn reduces the material selection room for design engineers in downstream industries. Therefore, research on compound modification of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02F16H55/06
Inventor 孙平
Owner KECHUANG POLYMER SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products