Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof

A production method and an environment-friendly technology, applied in the field of environment-friendly low-toxicity white light lamination crystal panels, can solve the problem that it is difficult to achieve white, transparent and bright low-toxicity white light lamination to thick sheet appearance standards, and the color of transparent light-colored products is difficult to control. , poor transparency and brightness, etc., to achieve the effect of excellent elasticity, good surface flatness and high transparency

Active Publication Date: 2010-07-14
TIANJIN HONGMAO PLASTICS
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This processing technology has a long production process, is not easy to control, requires a large amount of stabilizer, and takes a long time to heat the material.
The low-toxic PVC laminated thick film produced by this processing technology has poor transparency and brightness, and it is more difficult to control the color of transparent light-colored products. It is difficult to achieve white, transparent and bright low-toxic white laminated sheets that comply with REACH regulations. Thick slice appearance standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0099] 1) Selection: Shin-Etsu TK1000 PVC 100kg

[0100] Diisononyl phthalate (DINP) 40kg

[0101] Liquid barium zinc stabilizer 2.3kg

[0102] Non-toxic phosphate ester 0.4kg

[0103] Acrylic processing aid with a molecular weight of 1.5 million 0.6kg

[0104] 0.07kg of purple pigment with model number SF-7088B

[0105] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate DINP, liquid barium zinc stabilizer and non-toxic phosphate are discharged into the high mixer in sequence;

[0106] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in sequence, and the total mixing time is 400 seconds;

[0107] 3) Perform cooling and stirring, discharge the high-speed mixed materials into the mixer for cooling and stirring, and lower the temperature by feeding circulating cooling water into the mixer until the temperature drops below 80°C, and discharge them in...

example 2

[0124] 1) Selection: Japan Dayang TH1000 PVC 100kg

[0125] Diisononyl phthalate (DINP) 50kg

[0126] Liquid barium zinc stabilizer 2kg

[0127] Non-toxic phosphate ester 0.3kg

[0128] Acrylic processing aid with a molecular weight of 1.5 million 0.3kg

[0129] 0.05kg of purple pigment with model number SF-7088B

[0130] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate DINP, liquid barium zinc stabilizer and non-toxic phosphate are discharged into the high mixer in sequence;

[0131] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in sequence, and the total mixing time is 420 seconds;

[0132] 3) Cooling and stirring, the high-speed mixed materials are discharged into the mixer for cooling and stirring, and the temperature is lowered by passing circulating cooling water into the mixer until the temperature drops below 80°C, and then discharge...

example 3

[0149] 1) Choice: Formosa Plastics S65S PVC 100kg

[0150] Diisononyl phthalate (DINP) 60kg

[0151] Liquid barium zinc stabilizer 1.8kg

[0152] Acrylic processing aid with a molecular weight of 1.5 million 0.3kg

[0153] Purple powder pigment of model SF-7088B 0.05kg

[0154] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate (DINP) and liquid barium zinc stabilizer are discharged into the high mixer in sequence;

[0155] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in turn. The total mixing time is 450 seconds;

[0156] 3) Perform cooling and stirring, discharge the high-speed mixed materials into the mixer for cooling and stirring, and lower the temperature by feeding circulating cooling water into the mixer until the temperature drops below 80°C, and discharge them into the storage tank.

[0157] 4) The material in the storage barrel is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly low-toxicity white-light gluing crystal board and a manufacture method thereof. The formula of the crystal board comprises the following components: 100 polrvinyl chloride, 40-60 diisononyl ortho-phthalate, 1.8-2.5 liquid Ba-Zn stabilizer, 0.3-0.6 acrylicacid processing aid, 0.05-0.08 pigment and 0.3-0.6 PHR nontoxic phosphate. The process comprises the following working procedures of automatically metering; mixing at a high speed; stirring by cooling; plasticizing by using a planet extruder; filtering; four-roll calendaring; calendaring and cooling; bait reusing; calendaring and winding; gluing and feeding; gluing, preheating and gluing; gluing, cooling and cutting edge; gluing and winding; and packing and put finished products in storage. The invention accords with the REACH regulatory requirements and has short process flow, less material plasticizing and processing time and high production efficiency. The environment-friendly low-toxicity white-light gluing crystal board has superior elasticity to glass, high surface transparency and brightness, good surface planeness and small water wave; in addition, a single gluing film is approximate to be colorless, has high transparency and has the characteristics of glass.

Description

technical field [0001] The invention belongs to a polyvinyl chloride calendered and laminated crystal plate, in particular to an environmentally friendly low-toxicity white light laminated crystal plate that meets the requirements of REACH regulations, is similar to glass, has small water marks, and can achieve white, transparent and bright appearance effects and its production method. Background technique [0002] Polyvinyl chloride (hereinafter referred to as PVC) resin is a kind of strong polar polymer, and its intermolecular force is large, which leads to higher softening temperature and melting temperature of PVC resin, and generally requires 160-210°C to process. In addition, the substituted chlorine groups contained in the molecular structure of PVC can easily lead to the dehydrochlorination reaction of PVC resin, thereby causing the degradation reaction of PVC. PVC is extremely unstable to heat, and the temperature rise will greatly promote the dehydrochlorination re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K5/12C08K5/521B29C47/92B29C43/58B29C43/24B29C48/92
Inventor 张明奇苗启军
Owner TIANJIN HONGMAO PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com