Light rubber plastic foam material and production method and application thereof

A rubber-plastic foam material, lightweight technology, used in applications, shoe soles, clothing and other directions, can solve the problems of lack of tensile strength, tear strength and resilience, and achieve lightweight and beautiful appearance, small compression permanent deformation, tearing high crack strength

Inactive Publication Date: 2010-07-07
沈中伟
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Other existing rubber and plastic foam materials can only be used for packaging and cladding due to lack of tensile strength, tear strength, resilience, etc.; as the application number is 200610096913. Rubber and plastic foam, it is just spirally wound rubber and plastic foam with elastic rubber and plastic foam strips that tend to curl for pipe insulation packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] The lightweight rubber and plastic foaming material provided by the present embodiment comprises natural rubber, EVA plastic particles, blowing agent, crosslinking agent, sulfur and accelerator, and the ingredients by weight are 20 parts of natural rubber, EVA plastic 80 parts of particles, thus forming 100 parts of rubber and plastic main material, the foaming agent added in the rubber and plastic main material is Ac foaming agent, and the amount is 100 parts by weight of adding 3 parts of Ac foaming agent to the rubber and plastic main material The cross-linking agent is zinc oxide, and the dosage is 100 parts by weight of the rubber and plastic main material, and 2.5 parts of zinc oxide are added; the addition of sulfur and accelerator TMTD is 1 part per 100 parts by weight of the rubber and plastic main material. sulfur and 0.1 parts accelerator TMTD.

[0017] The operation steps are:

[0018] (1) Batching: take the natural rubber and EVA plastic particles determin...

Embodiment 2

[0025] The lightweight rubber and plastic foaming material described in this embodiment, the ingredients by weight ratio are 30 parts of natural rubber and 70 parts of EVA plastic particles, thus forming 100 parts of rubber and plastic main material, and adding in the rubber and plastic main material The foaming agent is Ac foaming agent, and the dosage is 100 parts by weight of the rubber and plastic main material, adding 4 parts of Ac foaming agent, and the crosslinking agent is zinc oxide, and the consumption is 100 parts by weight of the rubber and plastic main material, adding 2. Part zinc oxide; The addition of sulfur and accelerator TMTD is to add 1 part of sulfur and 0.1 part of accelerator TMTD in the rubber and plastic main body material of every 100 parts by weight. The lightweight rubber-plastic foam material made by this formula is used to make imitation leather sheet. The lightweight rubber and plastic foam material has a hardness of 65 degrees when tested by a S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a light rubber plastic foam material and a production method and application thereof. The material is characterized in that: the material comprises the following components in part by weight: 20 to 30 parts of natural rubber, 80 to 70 parts of EVA plastic granules, 3 to 4 parts of Ac foaming agent added based on 100 parts of rubber plastic main material, 2.5 parts of zinc oxide serving as a cross-linking agent added based on 100 parts of rubber plastic main material, and 1 part of sulphur and 0.1 part of accelerating agent TMTD added based on 100 parts of rubber plastic main material. The light rubber plastic foam material obtained by the production method has light and attractive appearance quality, realizes comfortable feeling when used for making soles and has an even and dense internal structure. The light rubber plastic foam material has the characteristics of high tensile strength, high tearing strength, good rebound resilience and low compression set.

Description

technical field [0001] The invention relates to a production technology of chemical materials, in particular to a lightweight rubber and plastic foam material and its production method and application. Background technique [0002] Application No. 200910020027.6 is a medical rubber-plastic composite material, which is composed of polyvinyl chloride (PVC) resin powder, composite rubber-plastic particles, phthalates, stabilizers and lubricants, etc. This rubber-plastic composite material Its chemical properties are stable, flexible, elastic, and tough, but it is not suitable for foaming shoe soles or imitation leather products. Other existing rubber and plastic foam materials can only be used for packaging and cladding due to lack of tensile strength, tear strength, resilience, etc.; as the application number is 200610096913. Rubber and plastic foam, it is just that the rubber and plastic foam has elastic rubber and plastic foam strips that tend to curl and is spirally wound ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/08C08L31/04C08L7/00C08K3/22C08K3/06C08J9/10B29C44/02B29C35/02B29C71/02B29B7/28A43B13/04
Inventor 沈中伟
Owner 沈中伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com