Scratch-resistant modified polypropylene composite material and preparation method thereof

A composite material, polypropylene technology, applied in the preparation of the modified polypropylene composite material, the field of scratch-resistant modified polypropylene composite material, can solve the problems such as rubber toughening, and achieve excellent mechanical properties , good impact resistance and strength, the effect of a wide range of sources

Inactive Publication Date: 2010-04-28
SUZHOU SUNWAY POLYMER
View PDF3 Cites 73 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2. U.S. patents US5585420 and US5731376 proposed a method of adding organosiloxane to improve the scratch resistance of talcum powder filled polypropylene, but did not mention rubber toughening

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Prepare according to the following formula:

[0038] (a) 70 parts by mass of polypropylene

[0039] (b) 10 parts by mass of toughening agent (POE)

[0040] (c) 20 parts by mass of mineral filler (talcum powder)

[0041] (d) 7 parts by mass of wear-resistant agent / scratch-resistant agent

[0042] (e) 1 part by mass of other additives

[0043] Among them, wear-resistant / scratch-resistant agents include: nano-scale polytetrafluoroethylene ultrafine powder, organic modified siloxane, modified silicone mixture, and reactive modified polysiloxane. According to the mass ratio, nano Grade polytetrafluoroethylene ultrafine powder: organic modified siloxane: modified silicone mixture: reactive modified polysiloxane = 5: 0.4: 0.6: 1;

[0044] First mix polypropylene and toughener at 1200 rpm for 5 minutes, then add mineral fillers, stir at 1500 rpm for 10 minutes, and finally add wear-resistant / scratch-resistant agent and Auxiliary, stirred at 1200 rpm for 5 minutes to obtain...

Embodiment 2

[0055] Prepare according to the following formula:

[0056] (a) 70 parts by mass of polypropylene

[0057] (b) 10 parts by mass of toughening agent (POE)

[0058] (c) 20 parts by mass of mineral filler

[0059] (d) 7 parts by mass of wear-resistant agent / scratch-resistant additive

[0060] (e) 1 part by mass of other additives

[0061] Wherein, the mineral filler includes: talcum powder and calcium carbonate, according to mass ratio, talcum powder: calcium carbonate=1: 1; Wear-resisting agent / scratch-resisting agent include: nanoscale polytetrafluoroethylene ultrafine powder, organic matter modified silicon Oxane, modified silicone mixture, reactive modified polysiloxane, according to the mass ratio, nanoscale polytetrafluoroethylene ultrafine powder: organic modified silicone: modified silicone mixture: reactive modified polysiloxane Sexual polysiloxane=5:0.4:0.8:0.8;

[0062] First mix polypropylene and mineral filler at 1200 rpm for 5 minutes, then add odor adsorbent, ...

Embodiment 3

[0073] Prepare according to the following formula:

[0074] (a) 70 parts by mass of polypropylene

[0075] (b) 10 parts by mass of toughening agent (POE)

[0076] (c) 20 parts by mass of mineral filler

[0077] (d) 7 parts by mass of wear-resistant agent / scratch-resistant additive

[0078] (e) 1 part by mass of other additives

[0079] Wherein, the mineral filler includes: talcum powder and calcium carbonate, according to mass ratio, talcum powder: calcium carbonate=1: 1; Wear-resisting agent / scratch-resistant agent include: nanoscale polytetrafluoroethylene ultrafine micropowder, organic matter modified silicon Oxane, modified silicone mixture, reactive modified polysiloxane, according to the mass ratio, nanoscale polytetrafluoroethylene ultrafine powder: organic modified silicone: modified silicone mixture: reactive modified polysiloxane Sexual polysiloxane=5:0.4:1:0.6;

[0080] First mix polypropylene and toughener at 1200 rpm for 5 minutes, then add mineral fillers, s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of modified polypropylene composite materials and relates to a scratch-resistant modified polypropylene composite material which is applicable to manufacturing automotive interior parts and comprises the following components by parts by weight: 60-90 parts of polypropylene, 5-20 parts of plasticizer, 5-20 parts of mineral filler, 0.1-4 parts of wear-resistant agent / scratch-resistant agents and 0.1-3 parts of additives, wherein the wear-resistant agent / scratch-resistant agents can be selected from the mixture of nano-polytetrafluoroethylene superfine micro-powder, organic matter-modified siloxane, modified silicone mixture and reactive modified polysiloxane. The prepared modified polypropylene composite material has high surface gloss and better impact-resistant performance, strength, melt fluidity and mechanical performance; furthermore, due to the use of the various wear-resistant agents / scratch-resistant agents, the scratch-resistant performance of the product is excellent; and the resources of the required raw materials are simultaneously extensive and easy to obtain.

Description

technical field [0001] The invention belongs to the field of modified polypropylene composite materials, in particular to a kind of wear-resistant agent / scratch-resistant agent-modified polypropylene composite material, and in particular to a kind of scratch-resistant modified polypropylene suitable for manufacturing automotive interior parts Composite material; the present invention also relates to the preparation method of the modified polypropylene composite material. Background technique [0002] Compared with engineering plastics, polyolefin materials such as polypropylene, toughener-modified polypropylene, thermoplastic polyolefin and thermoplastic elastomer have the advantages of recyclability, light weight and low cost, so they are increasingly used in automotive and other fields. However, polyolefins are significantly less resistant to scratches, which is a critical property for automotive interior applications such as instrument panels, consoles and door skins. S...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/14C08L23/08C08L23/16C08L27/18C08L83/04C08K3/34C08K5/5419C08K3/26
Inventor 顾在春任俊余林华
Owner SUZHOU SUNWAY POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com