Mg-Mn-Ca-Zn-Sr sacrificial anode with high current efficiency

A sacrificial anode and current efficiency technology, applied in the field of sacrificial anodes, can solve the problem of low current efficiency of magnesium anodes, and achieve the effects of reducing intergranular corrosion tendency, improving efficiency, and reducing spalling

Active Publication Date: 2011-06-15
山东宏泰科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to address the disadvantages of low current efficiency of traditional magnesium anodes, increase the dissolution uniformity and corrosion resistance of magnesium anodes, and improve the current efficiency of magnesium anodes by adding trace elements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mg-Mn-Ca-Zn-Sr sacrificial anode with high current efficiency

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0019] 1) The chemical composition of the sacrificial anode is composed of the following elements by weight percentage in terms of elements: Mn0.93%, Ca0.13%, Zn0.05%, Sr0.07%, Si<0.045%, Cu<0.018%, Ni< 0.001%, Fe<0.030%, the balance is Mg.

[0020] The current efficiency of the sacrificial anode is 65%, and the working potential is -1.65V-1.7V.

[0021] 2) Preparation method: Add metal halides of Zn, Ca, Sr, and Mn in proportion to the molten magnesium solution, and then shape it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses an Mg-Mn-Ca-Zn-Sr sacrificial anode with high current efficiency, which belongs to the technical field of sacrificial anodes and is characterized by comprising the following elements in percentage by weight: 0.93 percent of Mn, 0.13 percent of Ca, 0.05 percent of Zn, 0.07 percent of Sr, less than 0.045 percent of Si, less than 0.018 percent of Cu, less than 0.001 percent of Ni, less than 0.030 percent of Fe, and the balance of Mg. Aiming at the defect that the conventional magnesium anode has low current efficiency, by adding trace elements, the dissolution evenness and corrosion resistance of the magnesium anode are increased, and the current efficiency of the magnesium anode is improved.

Description

technical field [0001] The invention belongs to the technical field of sacrificial anodes, in particular to a Mg-Mn-Ca-Zn-Sr sacrificial anode with high current efficiency. Background technique [0002] Electrochemical protection is one of the most important methods to prevent metal corrosion. It uses external current to change the potential of the corroded metal to slow down or inhibit the corrosion of the metal. Pass enough anode current to the metal surface to make the metal undergo anodic polarization, that is, the potential becomes positive and is in a passivation state, and the dissolution of the metal is greatly slowed down, which is called anodic protection. At present, there are three types of sacrificial anode materials that have been successfully developed and widely used: magnesium anode, zinc anode and aluminum anode. [0003] "Research on the Electrochemical Performance of AZ63B Magnesium Sacrificial Anode" (Journal of Qinghai Normal University (Natural Scienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F13/14
Inventor 翟慎宝王在峰吴中文孙启明
Owner 山东宏泰科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com