Solar automatic temperature control foamed cement building block for construction and production method thereof
A technology for building cement and self-controlling temperature, which is applied in construction, building components, building structure, etc., can solve the problems of destroying land resources, low cost of clay bricks, and high profits, and achieves the advantages of reducing structural vibration, dimensional stability, and energy saving. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0028] First take 70 kg of phase change thermal storage insulation material, 330 kg of 425# ordinary Portland cement, 589 kg of fly ash with a particle size below 100 mesh sieve, 5 kg of cement reinforcing agent, 5 kg of compound agent, and enough to mix the above The materials are bonded together with water (water-cement ratio W / C=0.45~0.65), and mix it under constant stirring; then, add 1 kg of foaming agent under stirring, and after mixing, pour it on the In a mold with a width of 240*600*90mm / block, the finished product will be finished after 28 days of stacking.
[0029] The compounding agent is made from 15 kilograms of calcium oxide, 10 kilograms of active aluminum powder, and 1.5 kilograms of calcium sulfate in two crystal waters, which are fully stirred and mixed to obtain the finished product.
[0030] Foaming agent then is by 1.5 kilograms of diazodicarbonamide as cell opening agent, 2.5 kilograms of N, N' dinitrosopentamethylenetetramine as cell opening agent H, YA...
example 2
[0035] First take 70 kg of phase change heat storage insulation material, 300 kg of 425# ordinary portland cement, 580 kg of fly ash whose particle size is below 100 mesh sieve, 6.5 kg of cement reinforcing agent, 4.5 kg of compound agent, and enough to mix the above The water (water-cement ratio W / C=0.45~0.65) that the materials are bonded into one body is mixed under continuous stirring; then, 1.2 kg of foaming agent is added under stirring, and after mixing, pouring In a mold with a width of 240*600*90mm / block, the finished product will be finished after 28 days of stacking.
[0036] The compounding agent is made from 15 kilograms of calcium oxide, 9 kilograms of active aluminum powder, and 2.0 kilograms of calcium sulfate in two crystal waters, which are fully stirred and mixed to obtain the finished product.
[0037] Foaming agent then is by 1.5 kilograms of diazodicarbonamide as cell opener, 2.6 kilograms of N, N' dinitrosopentamethylenetetramine as cell opener H, YAP as f...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com