Inorganic-organic colored waterproofing agent

A water repellent, organic technology, applied in the direction of coating, can solve the problems of surrounding environmental pollution, short service life of waterproof materials, construction difficulties, etc., to achieve the effect of convenient construction, long service life, and widespread application value

Inactive Publication Date: 2010-01-13
伍少欢 +1
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the waterproof materials used for construction at home and abroad are usually organic waterproof materials. Most of these waterproof materials have a short service life, and most of the materials are in powder form, which will bring many difficulties to the construction.
Some use asphalt oil as waterproof material, which can only be used on the roof, and will emit an unpleasant smell under the sunlight, causing serious pollution to the surrounding environment
Some use organic waterproof materials instead of asphalt as waterproof materials, but they are basically colorless pigments. During continuous construction, it is difficult to distinguish which parts have been applied and which parts have not been applied, which has caused a lot of inconvenience to the construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1 A kind of organic-inorganic binary system, comprises following components: silicone resin solution 4% (percentage by weight), silicone resin solution is preferably methyltriethoxysilane, ethyl orthosilicate, dimethyl dimethoxysilane One or several mixtures of ethoxysilane mixed with lye and water; penetrating agent isobutyl triethoxysilane 1.2%; tackifier 0.6% is aminopropyl triethoxyalkane and chlorine Ferric oxide aqueous solution mixed; inorganic pigment 1.8%, preferably ferric oxide (black), ferric oxide (red), ferric hydroxide (yellow), chromium oxide green (green), iron brown (brown), Titanium dioxide (white) is a solution in which several average weight fractions are mixed; the remaining components are pure water, making up 100%. When preparing, all organic and inorganic components are dissolved in pure water, filtered, and stirred at a high speed at room temperature to form a solution. Because the organic matter in the organic-inorganic binary syst...

Embodiment 2

[0038] Embodiment 2 A kind of organic-inorganic binary system, comprises following components: silicone resin solution 4% (percentage by weight), silicone resin solution is preferably methyltriethoxysilane, ethyl orthosilicate, dimethyl dimethoxysilane One or several mixtures of ethoxysilane mixed with lye and water; penetrating agent isobutyl triethoxysilane 1.2%; tackifier 0.6% is aminopropyl triethoxyalkane and chlorine Iron oxide aqueous solution is mixed; inorganic pigment 1.8%, preferably a single type of ferric oxide (black), ferric oxide (red), ferric hydroxide (yellow), chromium oxide green (green), iron brown ( Brown), titanium dioxide (white) solution; the rest of the water is pure water, making up 100%. When preparing, all organic and inorganic components are dissolved in pure water, filtered, and stirred at a high speed at room temperature to form a solution.

[0039] When in use, apply the above-mentioned waterproof agent that dissolves a single inorganic pigmen...

Embodiment 3

[0040] Embodiment 3 A kind of organic-inorganic binary system, comprises following components: silicone resin solution 4% (percentage by weight), silicone resin solution is preferably methyltriethoxysilane, ethyl orthosilicate, dimethyl dimethoxysilane One or several mixtures of ethoxysilane mixed with lye and water; penetrating agent isobutyl triethoxysilane 1.2%; tackifier 0.6% is aminopropyl triethoxyalkane and chlorine Ferric chloride aqueous solution is mixed; inorganic pigment 1.8%, preferably a single type of ferric oxide (black), ferric oxide (red), iron hydroxide (yellow) solution, accounting for 80% of the total weight fraction of inorganic pigments ; Then on the basis of the above three main colors, auxiliary chromium oxide green (green), iron brown (brown), and titanium dioxide (white) solution are added, accounting for 20% of the total weight fraction of inorganic pigments; the rest of the components in water are pure water , make up 100%. When preparing, all org...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an inorganic-organic colored waterproofing agent comprising the following components in percentage by weight: 1-20 percent of silicone resin solution, 0.5-5 percent of osmotic agent, 0.2-6 percent of adhesion agent, 0.05-8 percent of inorganic pigment, and the balance of water, wherein the sum of the percentages of all the components is 100 percent. The invention firstly adopts an inorganic-organic binary system as a novel liquid waterproofing agent; and meanwhile, by reasonably adjusting the proportion of the waterproofing agent and adding the inorganic pigment in the waterproofing agent, the invention not only can satisfy the waterproofing requirements on roofs, external walls or internal walls of buildings, but also can not pollute the surrounding environment and have longer service life than an organic waterproofing agent. Through the color presented by the pigment belonging to the inorganic-organic binary system, the invention can clearly differentiate which parts are coated and which parts are not coated in the coating process, thereby bringing great convenience to construction and achieving wide promotion and application values.

Description

technical field [0001] The invention belongs to the technical field of waterproofing agents, and in particular relates to an inorganic-organic colored waterproofing agent which can distinguish whether to apply the waterproofing agent by color. Background technique [0002] At present, the waterproof materials used for construction at home and abroad are usually organic waterproof materials. Most of these waterproof materials have a short service life, and most of the materials are in powder form, which will bring many difficulties to the construction. Some use asphalt oil etc. as waterproof materials, which can only be used on the roof of buildings, and will emit unpleasant smells under the irradiation of sunlight, causing relatively serious pollution to the surrounding environment. Some use organic waterproof materials instead of asphalt as waterproof materials, but they are basically colorless pigments. During continuous construction, it is difficult to distinguish which p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/00
Inventor 伍少欢丁家翔
Owner 伍少欢
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap