Honed embossed adhesive tape basilemma and production method thereof

A production method and embossing technology, applied in the field of unstretched matte embossed tape base film, can solve the problems of large difference in longitudinal and transverse tearing properties, poor coating performance on the surface of the film, poor appearance effect and hand feeling, etc. The effect of good longitudinal and transverse tear resistance, uniform surface roughness, and excellent gluing effect

Inactive Publication Date: 2009-12-30
湖北慧狮塑业股份有限公司
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention mainly solves the technical problems of poor coating performance on the surface of the film, large difference in vertical and horizontal tearing properties, poor appearance and feel, and high production cost when the existing common matting film is used to make adhesive tape products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Honed embossed adhesive tape basilemma and production method thereof
  • Honed embossed adhesive tape basilemma and production method thereof
  • Honed embossed adhesive tape basilemma and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0031]Embodiment 2: production line speed is 60m / min, and polypropylene resin is put into the hopper of screw extruder, after extruder is fully melted and plasticized, the melt that forms molten state is from the T-type die head (die head) of extruder Temperature 210 ~ 240 ℃) extrusion; the extruded polyolefin resin melt immediately enters the gap between the rollers formed by the rubber roller and the pressure roller. The surface roughness Ra of the rubber roller is 40μinch, and the roller surface The temperature is controlled at 60°C, the surface roughness Ra value of the pressure roller is 200μinch, the surface temperature of the roller is controlled at 40°C, the pressure between the rollers is 2bar, the roller is initially cooled to the melt, and the roller is melted at the same time. Hot pressing to obtain an embossed film with different embossments on the front and back sides, and the embossed film is then passed through a cooling roller with a surface temperature of 20°C...

Embodiment 3

[0032] Embodiment 3: production line speed is 60m / min, and polypropylene resin is put into the hopper of screw extruder, after extruder is fully melted and plasticized, the molten melt that forms molten state is from the T-type die head (die head) of extruder Temperature 210~240 ℃) extrusion; the extruded polyolefin resin melt immediately enters the gap between the rollers formed by the rubber roller and the pressure roller. The surface roughness Ra value of the rubber roller is 60μinch, and the surface The temperature is controlled at 55°C, the surface roughness Ra value of the pressure roller is 150μinch, the surface temperature of the roller is controlled at 30°C, the pressure between the rollers is 1bar, the roller is initially cooled to the melt, and the roller is melted at the same time. Hot pressing to obtain an embossed film with different embossments on the front and back sides, and the embossed film is then passed through a cooling roller with a surface temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Shore hardnessaaaaaaaaaa
Login to View More

Abstract

A honed embossed adhesive tape basilemma is made of pure polyolefin resin, the roughness of the front face Ra value is 20-60 mu inch, the roughness of the back face Ra value is 60-200 mu inch, the production method thereof comprises steps of melting and extruding, embossing and finishing. The honed embossed adhesive tape basilemma prepared by the invention has special honed effect, even surface roughness, even thickness stability, good longitudinal and transverse tear resistance, good anti-blocking effect and excellent gluing effect. The method of the invention does not change the inner structure of the basilemma material, thus not influencing the physical performance of the basilemma material, and being applicable to production of honed embossed adhesive tape basilemma and production of honed basilemma for other special uses.

Description

technical field [0001] The invention relates to a matt embossed film, an unstretched matt embossed adhesive tape base film and a production method thereof. Background technique [0002] In recent years, with people's pursuit of aesthetics, tape products with a unique matt effect have become more and more popular among consumers due to their unique elegant, simple and noble visual effects; at the same time, on some special occasions, For example, in tape products such as side-to-side and front-to-back stickers of diapers used in hygiene products, people have very high requirements for the surface roughness, hand feel, thickness uniformity, vertical and horizontal tearing performance, and glue coating performance of the base film of the tape. Although adding a matting agent to the film can make a film product with a matte effect, the addition of foreign components such as a matting agent (such film products must also be added with additives such as slip agents and antistatic a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/00B29C59/04C08L23/12
Inventor 王焕清罗建明吴朋袁向华卢长伟曾志明伍冬瑞
Owner 湖北慧狮塑业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com