Steel sheet for cans, hot-rolled steel sheet to be used as the base metal and processes for production of both

A manufacturing method and technology of steel plates, which are applied in the field of manufacturing steel plates for cans and their base metal hot-rolled steel plates, can solve problems such as increased manufacturing processes, lack of ductility, and poor processability of DR materials

Active Publication Date: 2009-12-02
JFE STEEL CORP
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, DR materials that lack ductility are difficult to apply to special-shaped cans and the like due to poor processability
In addition, DR material has higher production cost due to the increase of manufacturing process compared with the steel plate subjected to temper rolling (pressure adjustment) after normal annealing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel sheet for cans, hot-rolled steel sheet to be used as the base metal and processes for production of both
  • Steel sheet for cans, hot-rolled steel sheet to be used as the base metal and processes for production of both
  • Steel sheet for cans, hot-rolled steel sheet to be used as the base metal and processes for production of both

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0116] A steel containing the composition shown in Table 1 with the balance consisting of Fe and unavoidable impurities was smelted in a converter to obtain a billet. After reheating the obtained steel slab at 1250 degreeC, hot rolling was started. Hot rolling is carried out at a finishing temperature of 880°C to 900°C, cooled at an average cooling rate of 20°C to 40°C / s before coiling, and coiled at a coiling temperature of 620°C to 700°C. Next, after pickling, cold rolling is performed at a rolling reduction of about 90 to 94%, to manufacture a thin steel sheet of 0.17 to 0.2 mm. The obtained thin steel sheet was heated to 690 to 750° C. at a heating rate of 15° C. / second, and continuous annealing was performed at 690 to 750° C. for 20 seconds. Next, after cooling, temper rolling is performed so that the rolling ratio (measured by elongation) becomes 1.5% or less, and normal chrome plating (electroplating) is continuously performed to obtain a non-tin-plated steel sheet. I...

Embodiment 2

[0132] A steel containing the composition shown in Table 3 (same as No. 1 of Example 1) and the balance consisting of Fe and unavoidable impurities was melted in a real machine converter to obtain a billet. After reheating the obtained steel slab at 1250 degreeC, hot rolling was started. Hot rolling is carried out at a finishing temperature of 830°C to 900°C, cooled at an average cooling rate of 16°C to 45°C / s before coiling, and coiled at a coiling temperature of 580°C to 720°C. Next, cold rolling is performed at a rolling reduction of 75 to 94%, to produce a thin steel plate of 0.15 to 0.18 mm. The obtained thin steel sheet was heated to 630-740° C. at a heating rate of 20° C. / second, and continuous annealing was performed at 630-740° C. for 20-30 seconds. Next, after cooling, temper rolling was performed so that the rolling ratio was 1.5% or less, and normal chrome plating was continuously performed to obtain a non-tin-plated steel sheet. The detailed manufacturing condit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield ratioaaaaaaaaaa
yield pointaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

In producing a steel sheet for cans, a steel sheet which consists substantially of ferrite single-phase structure and has a mean grain diameter of 7[mu]m or below and which exhibits a yield strength of 500MPa or above, a yield ratio of 0.9 or above, a total elongation of 10% or above, and deltar of -0.50 to 0 after coating and baking is produced by incorporating C: 0.01 to 0.12%, Si: 0.005 to 0.5%, Mn: 0.3 to 1.5%, P: 0.005 to 0.2%, Al: 0.10% or below, N: 0.012% or below, and Nb: 0.005 to 0.10% and combining solid solution hardening, precipitation hardening, and grain refinement hardening. The hot rolling is conducted principally under the conditions of FT of 870 DEG C or above, cooling rate after hot rolling of 40 DEG C / s or below, and CT of 620 DEG C or above to adjust the mean grain size of a hot-rolled sheet serving as material for the steel sheet for cans to 6[mu]m or above.

Description

technical field [0001] The present invention relates to a tin mill black plate and a hot-rolled steel sheet used as a base material thereof. The present invention also relates to a manufacturing method of a steel plate for cans and a base material hot-rolled steel plate. Specifically, it relates to a steel sheet for cans having high ductility, high strength, and a small anisotropy (Δr) (in-plate plastic anisotropy), a hot-rolled steel sheet used as a base material thereof, and a method for producing the same. Background technique [0002] In recent years, in order to expand the demand for steel cans, strategies have been adopted such as reducing the cost of canning and introducing new types of cans such as bottle shaped cans and shaped cans into the market. [0003] The cost reduction of raw materials can be mentioned as a reduction strategy of a can manufacturing cost. That is, whether it is a two-piece can that is subjected to drawing (drawing) or a three-piece can that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/00C21D9/46C22C38/12
CPCC21D9/46C21D8/04C22C38/02C21D9/48C22C38/12C22C38/04
Inventor 西原友佳小岛克己岩佐浩树山下阳俊饭住健尔荻本省三
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com