High-strength high-toughness aluminum alloy pre-tensioned thick plate and preparation method thereof
A manufacturing method and pre-stretching technology, applied in the field of aluminum alloy pre-stretching thick plate and its manufacturing, can solve the problems of low strength, poor toughness of aluminum alloy structural materials, unreasonable addition amount, etc., and achieve simple operation and fatigue strength. and the effect of improving fracture toughness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
specific Embodiment approach 1
[0007] Embodiment 1: The high-strength and high-toughness aluminum alloy pre-stretched thick plate of this embodiment, the thick plate is composed of 1.40%-2.00% Cu, 1.80%-2.80% Mg, 0.20%-0.60% by weight Mn, 0.10%-0.25% Cr, 5.00%-6.50% Zn, 0-0.10% Si, 0.05%-0.25% Fe, 0-0.05% Ti, 0-0.10% Ni, 0.01- Composed of 0.05% single impurity, 0.01-0.10% total impurity and the balance Al, the thickness of the thick plate is 11mm-85mm, and the model of the thick plate is 7B04.
specific Embodiment approach 2
[0008] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the thick plate of this embodiment consists of 1.70% Cu, 2.40% Mg, 0.40% Mn, 0.15% Cr, 6.00% Zn, 0.05% Si, 0.15% Fe, 0.03% Ti, 0.05% Ni, 0.03% single impurity, 0.05% total impurity and the balance Al, the thickness of the thick plate is 50mm.
specific Embodiment approach 3
[0009] Specific Embodiment Three: The manufacturing method of the high-strength, high-toughness aluminum alloy pre-stretched thick plate of this embodiment is completed by the following steps: 1. Melting and casting of the flat aluminum alloy ingot; 2. Homogenization of the flat aluminum alloy ingot For annealing, set the melting furnace temperature to 490°C and heat for 5h to 7h; then set the melting furnace temperature to 455°C and heat for 49h to 51h to heat the flat aluminum alloy ingot to 450°C to 460°C; Hot rolling of aluminum alloy ingots. During hot rolling, the heating temperature of the ingots is 370°C-420°C, and the heat preservation is 1h-2h; the hot-rolled plate thickness is 11mm-85mm. 4. Quenching and pre-stretching the hot-rolled plates Stretching: first use a roller hearth quenching furnace to quench the thick plate, quenching: the temperature of solution treatment is 470°C±2°C, heat preservation for 1h-2h, transfer time is less than 30s, cooling water temperatu...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com