Nano red light conversion agent special for agricultural film and preparation thereof

A light-transforming agent and nanotechnology, which is applied in the field of core-shell structure nano-red light-transforming agents, can solve the problems of affecting the light transmittance of the film, reducing the light transmittance of the film, and reducing the light transmittance of the film.

Inactive Publication Date: 2010-11-03
SHANDONG NORMAL UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Film is a good carrier of light conversion agent. In general production, the production of light conversion film can be completed by slightly adjusting the production process and adding light conversion agent and other plastic additives to the resin masterbatch. If the addition of additives is not well dispersed, it will reduce the light transmittance of the film
In addition, in the production of ordinary agricultural film, the thermal insulation performance of the film is generally improved by adding inorganic powder to the resin as a thermal insulation agent, but the addition of the thermal insulation agent also affects the light transmittance of the film, especially if the particles of the thermal insulation agent are large, It will greatly reduce the light transmittance of the film due to poor dispersion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Take the red light conversion agent Eu 0.7 Tb 0.3 (TTA) 3 Phen0.6g, 0.6mmol was dissolved in 50ml dimethyl sulfoxide to obtain solution A; take 0.1g nano-SiO 2 (20nm-30nm), ultrasonically disperse in 50ml ethanol, adjust the pH value of the system to be weakly alkaline at 8.0-12.0, and obtain nano-dispersion system B. (2) In the state of stirring, add solution A dropwise to nano-dispersion system B, continue to stir, and gradually get white turbidity, let it stand for 30-90 minutes, and centrifuge to obtain white solid powder, that is, core-shell red light nanometer Light converting agent SiO 2 @Eu 0.7 Tb 0.3 (TTA) 3 Phen.

Embodiment 2

[0014] Take the red light conversion agent Eu 0.5 Y 0.5 (TTA) 3 Dissolve 0.6g and 0.6mmol of Phen in 50ml of acetone to obtain solution A; take 0.38nm MgO (20nm-30nm), ultrasonically disperse it in 50ml of n-propanol, adjust the pH of the system to be weakly alkaline at 8.0-12.0, and obtain nanodispersion system B . (2) In the state of stirring, add solution A dropwise to the nano-dispersion system B, continue to stir, and gradually get white turbidity, let it stand for 30-90 minutes, and centrifuge to obtain a white solid powder, which is the core-shell red light nanometer Light converting agent MgO@Eu 0.5 Y 0.5 (TTA) 3 Phen.

Embodiment 3

[0016] Take the red light conversion agent Eu 0.5 Dy 0.5 (TTA) 3 Phen 0.6g, 0.6mmol was dissolved in 50ml N,N-dimethylformamide to obtain solution A, which was subjected to oxygen removal treatment; 0.6g nanometer Cu 2 o 2 (20nm-30nm), ultrasonically disperse in 50ml n-propanol under nitrogen atmosphere, adjust the pH of the system to be weakly alkaline at 8.0-12.0, and obtain nano-dispersion system B. (2) While stirring, under nitrogen protection, add the solution A dropwise to the nano-dispersion system B, continue to stir, and gradually get white turbidity, let it stand for 30-90 minutes, and centrifuge to obtain a white solid powder, which is the core-shell type Red light nano light transfer agent Cu 2 o 2 @Eu 0.5 Dy 0.5 (TTA) 3 Phen.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanometer red-light conversion agent specifically used for agricultural films and a preparation method thereof. The light conversion agent is a core-shell-structure composite and a structure thereof can be represented by R@AxB1-xL1L2, wherein, AxB1-xL1L2 is the structure of a shell layer and R is the structure of a core layer. The preparation method comprises the following steps: the red-light conversion agent with suitable amount is taken, and dissolved in solvent S1 with suitable amount so as to obtain solution A; nano-particle R with suitable amount is taken and dispersed in proper solvent S2 by ultrasonic waves, and the pH value of the system is regulated to 8.0 to 12.0 and takes weak alkaline, thereby obtaining a nanometer dispersion system B. Under stirring, the solution A is added in the nanometer dispersion system B by dropping; stirring is continued till obtain white turbid liquid which stands for 30min to 90min, is centrifugally separated and dried so as to obtain the nanometer red-light conversion agent.

Description

technical field [0001] The invention belongs to the field of nanomaterial synthesis, and provides a core-shell structure nanometer red light conversion agent with dual functions of light conversion and heat preservation and a production method thereof. Background technique [0002] Plant growth mainly depends on photosynthesis. The demand of plants for light energy, in addition to light intensity and photoperiod, light quality is a very important factor, which not only affects the photosynthetic efficiency of crops, but also can regulate the content of nutrients in crops. Among the sunlight, red light is the most important to the photosynthesis of plants, followed by blue light; ultraviolet light is easy to promote the aging of plants, induce the occurrence of diseases and insect pests in the soil, and is harmful to plant growth. At the same time, ultraviolet light will cause the aging of plastic films and reduce the service life; other colors The light is mainly converted i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K9/10
Inventor 唐波陈德展崔官伟王茂龙石锡峰董玉明张国英
Owner SHANDONG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com